- W2352006323 abstract "The epoxy/polyurethane (EP/PU) mixed two component grouting material was prepared using combination of the interpenetrating polymer network (IPN) technology and the polyurethane foaming technology.The mechanical properties of the cured EP/PU based IPN product were tested.The result showed that the variation of tensile shear strength of the cured IPN product with time was similar with that of the cured epoxy resin,and the tensile shear strength of cured IPN product was superior to that of cured PU or epoxy resin.The comparison of infrared spectra of the IPN at 2 min -1 and 7 days during curing indicated that the epoxy group absorption peak at 914cm -1 was significantly weakened and the isocyanate group absorption peak at 2 220cm disappeared at 7 days during curing,which proved the formation of EP/PU based IPN structure.The morphology obtained by SEM analysis showed that when EP/PU=40/100,the compatibility between the two phases of the grout concretion body was the best." @default.
- W2352006323 created "2016-06-24" @default.
- W2352006323 creator A5051292006 @default.
- W2352006323 date "2012-01-01" @default.
- W2352006323 modified "2023-09-26" @default.
- W2352006323 title "Preparation and performance of epoxy/polyurethane mixed grouting material" @default.
- W2352006323 hasPublicationYear "2012" @default.
- W2352006323 type Work @default.
- W2352006323 sameAs 2352006323 @default.
- W2352006323 citedByCount "0" @default.
- W2352006323 crossrefType "journal-article" @default.
- W2352006323 hasAuthorship W2352006323A5051292006 @default.
- W2352006323 hasConcept C112950240 @default.
- W2352006323 hasConcept C132976073 @default.
- W2352006323 hasConcept C159985019 @default.
- W2352006323 hasConcept C166595027 @default.
- W2352006323 hasConcept C192562407 @default.
- W2352006323 hasConcept C2779310008 @default.
- W2352006323 hasConcept C2779578285 @default.
- W2352006323 hasConcept C2780534471 @default.
- W2352006323 hasConcept C521977710 @default.
- W2352006323 hasConceptScore W2352006323C112950240 @default.
- W2352006323 hasConceptScore W2352006323C132976073 @default.
- W2352006323 hasConceptScore W2352006323C159985019 @default.
- W2352006323 hasConceptScore W2352006323C166595027 @default.
- W2352006323 hasConceptScore W2352006323C192562407 @default.
- W2352006323 hasConceptScore W2352006323C2779310008 @default.
- W2352006323 hasConceptScore W2352006323C2779578285 @default.
- W2352006323 hasConceptScore W2352006323C2780534471 @default.
- W2352006323 hasConceptScore W2352006323C521977710 @default.
- W2352006323 hasLocation W23520063231 @default.
- W2352006323 hasOpenAccess W2352006323 @default.
- W2352006323 hasPrimaryLocation W23520063231 @default.
- W2352006323 hasRelatedWork W2029813515 @default.
- W2352006323 hasRelatedWork W2045090887 @default.
- W2352006323 hasRelatedWork W2054111494 @default.
- W2352006323 hasRelatedWork W2058007318 @default.
- W2352006323 hasRelatedWork W2071079599 @default.
- W2352006323 hasRelatedWork W2330776854 @default.
- W2352006323 hasRelatedWork W2348154353 @default.
- W2352006323 hasRelatedWork W2352781917 @default.
- W2352006323 hasRelatedWork W2360395536 @default.
- W2352006323 hasRelatedWork W2360470111 @default.
- W2352006323 hasRelatedWork W2372488449 @default.
- W2352006323 hasRelatedWork W2377050948 @default.
- W2352006323 hasRelatedWork W2377220965 @default.
- W2352006323 hasRelatedWork W2378252217 @default.
- W2352006323 hasRelatedWork W2378531130 @default.
- W2352006323 hasRelatedWork W2384497514 @default.
- W2352006323 hasRelatedWork W2386373916 @default.
- W2352006323 hasRelatedWork W2574008347 @default.
- W2352006323 hasRelatedWork W3200110141 @default.
- W2352006323 hasRelatedWork W2408552319 @default.
- W2352006323 isParatext "false" @default.
- W2352006323 isRetracted "false" @default.
- W2352006323 magId "2352006323" @default.
- W2352006323 workType "article" @default.