- W2355290864 abstract "The RJ16-1000BI expansion joint made of stainless steel in heating system experienced cracking after being put into use for four years.Thus the state of the expansion joint in field application was investigated.The chemical composition of the parent metal and corrosion products was analyzed.The fractured surface of the failed parts were examined using a scanning electron microscope,aiming at revealing the causes leading to the cracking of the expansion joint.It was found that the failure of the expansion joint was attributed to severe chloride stress corrosion cracking and partial corrosion." @default.
- W2355290864 created "2016-06-24" @default.
- W2355290864 creator A5067592503 @default.
- W2355290864 date "2007-01-01" @default.
- W2355290864 modified "2023-09-26" @default.
- W2355290864 title "Analysis of the Causes Leading to Cracking of RJ16-1000BI Stainless Steel Expansion Joint of a Hot-Water Transporting Pipe" @default.
- W2355290864 hasPublicationYear "2007" @default.
- W2355290864 type Work @default.
- W2355290864 sameAs 2355290864 @default.
- W2355290864 citedByCount "0" @default.
- W2355290864 crossrefType "journal-article" @default.
- W2355290864 hasAuthorship W2355290864A5067592503 @default.
- W2355290864 hasConcept C113024971 @default.
- W2355290864 hasConcept C127413603 @default.
- W2355290864 hasConcept C159985019 @default.
- W2355290864 hasConcept C18555067 @default.
- W2355290864 hasConcept C191897082 @default.
- W2355290864 hasConcept C192562407 @default.
- W2355290864 hasConcept C20625102 @default.
- W2355290864 hasConcept C26771246 @default.
- W2355290864 hasConcept C2778695967 @default.
- W2355290864 hasConcept C2778760603 @default.
- W2355290864 hasConcept C58396970 @default.
- W2355290864 hasConcept C66938386 @default.
- W2355290864 hasConceptScore W2355290864C113024971 @default.
- W2355290864 hasConceptScore W2355290864C127413603 @default.
- W2355290864 hasConceptScore W2355290864C159985019 @default.
- W2355290864 hasConceptScore W2355290864C18555067 @default.
- W2355290864 hasConceptScore W2355290864C191897082 @default.
- W2355290864 hasConceptScore W2355290864C192562407 @default.
- W2355290864 hasConceptScore W2355290864C20625102 @default.
- W2355290864 hasConceptScore W2355290864C26771246 @default.
- W2355290864 hasConceptScore W2355290864C2778695967 @default.
- W2355290864 hasConceptScore W2355290864C2778760603 @default.
- W2355290864 hasConceptScore W2355290864C58396970 @default.
- W2355290864 hasConceptScore W2355290864C66938386 @default.
- W2355290864 hasLocation W23552908641 @default.
- W2355290864 hasOpenAccess W2355290864 @default.
- W2355290864 hasPrimaryLocation W23552908641 @default.
- W2355290864 hasRelatedWork W1971280843 @default.
- W2355290864 hasRelatedWork W1990586903 @default.
- W2355290864 hasRelatedWork W2000524706 @default.
- W2355290864 hasRelatedWork W2011757797 @default.
- W2355290864 hasRelatedWork W2033769450 @default.
- W2355290864 hasRelatedWork W2087624742 @default.
- W2355290864 hasRelatedWork W2248581911 @default.
- W2355290864 hasRelatedWork W2356448484 @default.
- W2355290864 hasRelatedWork W2358280275 @default.
- W2355290864 hasRelatedWork W2358421742 @default.
- W2355290864 hasRelatedWork W2360969393 @default.
- W2355290864 hasRelatedWork W2363767341 @default.
- W2355290864 hasRelatedWork W2369170480 @default.
- W2355290864 hasRelatedWork W2370047518 @default.
- W2355290864 hasRelatedWork W2373996636 @default.
- W2355290864 hasRelatedWork W2376571558 @default.
- W2355290864 hasRelatedWork W2383116872 @default.
- W2355290864 hasRelatedWork W2391642656 @default.
- W2355290864 hasRelatedWork W628791409 @default.
- W2355290864 hasRelatedWork W1986086804 @default.
- W2355290864 isParatext "false" @default.
- W2355290864 isRetracted "false" @default.
- W2355290864 magId "2355290864" @default.
- W2355290864 workType "article" @default.