- W2356236102 abstract "W-1wt%TiC nanocomposite was prepared by high energy ball milling and vacuum hot-pressing(VHP).The microstructure,room temperature mechanical properties of the composite were investigated in detail.The results show that the particle size of powders decreases to 300 nm,the crystalline size of W decreases and the crystalline distortion increases after milling.High energy ball milling is beneficial to further sintering densification.Nano-TiCp is homogeneously distributed in W matrix due to high energy ball milling and its size is about 100 nm after sintering.No voids or precipitation can be detected at TiC/W interface,indicating excellent interfacial bonding.The relative density,vickers microhardness,elastic modulus and fracture strength of W-1wt%TiC nanocomposite is 98.4%,4.33 GPa,396 GPa,1065 MPa respectively while the monolithic W is 95.6%,3.32 GPa,345 GPa,730 MPa respectively.The improved mechanical properties may be mainly attributed to grain size strengthening and grain boundary strengthening." @default.
- W2356236102 created "2016-06-24" @default.
- W2356236102 creator A5022199302 @default.
- W2356236102 date "2008-01-01" @default.
- W2356236102 modified "2023-09-24" @default.
- W2356236102 title "Microstructure and mechanical properties of W-1wt%TiC nanocomposite" @default.
- W2356236102 hasPublicationYear "2008" @default.
- W2356236102 type Work @default.
- W2356236102 sameAs 2356236102 @default.
- W2356236102 citedByCount "0" @default.
- W2356236102 crossrefType "journal-article" @default.
- W2356236102 hasAuthorship W2356236102A5022199302 @default.
- W2356236102 hasConcept C104779481 @default.
- W2356236102 hasConcept C132186339 @default.
- W2356236102 hasConcept C133392424 @default.
- W2356236102 hasConcept C159985019 @default.
- W2356236102 hasConcept C165720898 @default.
- W2356236102 hasConcept C192191005 @default.
- W2356236102 hasConcept C192562407 @default.
- W2356236102 hasConcept C2776578615 @default.
- W2356236102 hasConcept C2777581544 @default.
- W2356236102 hasConcept C79148161 @default.
- W2356236102 hasConcept C82455628 @default.
- W2356236102 hasConcept C87976508 @default.
- W2356236102 hasConcept C92880739 @default.
- W2356236102 hasConceptScore W2356236102C104779481 @default.
- W2356236102 hasConceptScore W2356236102C132186339 @default.
- W2356236102 hasConceptScore W2356236102C133392424 @default.
- W2356236102 hasConceptScore W2356236102C159985019 @default.
- W2356236102 hasConceptScore W2356236102C165720898 @default.
- W2356236102 hasConceptScore W2356236102C192191005 @default.
- W2356236102 hasConceptScore W2356236102C192562407 @default.
- W2356236102 hasConceptScore W2356236102C2776578615 @default.
- W2356236102 hasConceptScore W2356236102C2777581544 @default.
- W2356236102 hasConceptScore W2356236102C79148161 @default.
- W2356236102 hasConceptScore W2356236102C82455628 @default.
- W2356236102 hasConceptScore W2356236102C87976508 @default.
- W2356236102 hasConceptScore W2356236102C92880739 @default.
- W2356236102 hasLocation W23562361021 @default.
- W2356236102 hasOpenAccess W2356236102 @default.
- W2356236102 hasPrimaryLocation W23562361021 @default.
- W2356236102 hasRelatedWork W1996872831 @default.
- W2356236102 hasRelatedWork W2046327043 @default.
- W2356236102 hasRelatedWork W2047985081 @default.
- W2356236102 hasRelatedWork W2166272769 @default.
- W2356236102 hasRelatedWork W2240254047 @default.
- W2356236102 hasRelatedWork W2366756360 @default.
- W2356236102 hasRelatedWork W2375373260 @default.
- W2356236102 hasRelatedWork W2495997755 @default.
- W2356236102 hasRelatedWork W2774091496 @default.
- W2356236102 hasRelatedWork W2791539246 @default.
- W2356236102 hasRelatedWork W2800239945 @default.
- W2356236102 hasRelatedWork W2885560227 @default.
- W2356236102 hasRelatedWork W2892539225 @default.
- W2356236102 hasRelatedWork W2909079102 @default.
- W2356236102 hasRelatedWork W2915041522 @default.
- W2356236102 hasRelatedWork W2917975168 @default.
- W2356236102 hasRelatedWork W3020500756 @default.
- W2356236102 hasRelatedWork W3110862376 @default.
- W2356236102 hasRelatedWork W3121091345 @default.
- W2356236102 hasRelatedWork W3171310147 @default.
- W2356236102 isParatext "false" @default.
- W2356236102 isRetracted "false" @default.
- W2356236102 magId "2356236102" @default.
- W2356236102 workType "article" @default.