- W2357914214 endingPage "984" @default.
- W2357914214 startingPage "979" @default.
- W2357914214 abstract "The influence of surface vertical cracks in YSZ coating on the failure mechanism of thermal barrier coatings prepared by electron beam physical vapor deposition (EB-PVD) during thermal cycling was studied. The vertical cracks occurred at the initial stage of thermal cycling testing but did not directly cause the spallation of TBC. The mesh density of vertical cracks increased following thermal cycles. Calculation by finite elements analysis showed that a larger shear stress was generated by the formation of the vertical cracks just like what in the edge of the specimen. After thermal cycling testing, when the strength of equiaxial grain regions or thermally grown oxidation layer became lower than the shear stress, the spallation occurred along the vertical crack network." @default.
- W2357914214 created "2016-06-24" @default.
- W2357914214 creator A5022723755 @default.
- W2357914214 creator A5042441491 @default.
- W2357914214 creator A5082797965 @default.
- W2357914214 date "2005-09-11" @default.
- W2357914214 modified "2023-09-23" @default.
- W2357914214 title "INFLUENCE OF VERTICAL CRACKS ON FAILURE MECHANISM OF EB-PVD THERMAL BARRIER COATINGS DURING THERMAL CYCLING" @default.
- W2357914214 hasPublicationYear "2005" @default.
- W2357914214 type Work @default.
- W2357914214 sameAs 2357914214 @default.
- W2357914214 citedByCount "0" @default.
- W2357914214 crossrefType "journal-article" @default.
- W2357914214 hasAuthorship W2357914214A5022723755 @default.
- W2357914214 hasAuthorship W2357914214A5042441491 @default.
- W2357914214 hasAuthorship W2357914214A5082797965 @default.
- W2357914214 hasConcept C11608111 @default.
- W2357914214 hasConcept C121332964 @default.
- W2357914214 hasConcept C152568617 @default.
- W2357914214 hasConcept C153294291 @default.
- W2357914214 hasConcept C159985019 @default.
- W2357914214 hasConcept C166957645 @default.
- W2357914214 hasConcept C171250308 @default.
- W2357914214 hasConcept C176711861 @default.
- W2357914214 hasConcept C177564732 @default.
- W2357914214 hasConcept C192562407 @default.
- W2357914214 hasConcept C204530211 @default.
- W2357914214 hasConcept C2779227376 @default.
- W2357914214 hasConcept C2781448156 @default.
- W2357914214 hasConcept C51576277 @default.
- W2357914214 hasConcept C541528975 @default.
- W2357914214 hasConcept C57410435 @default.
- W2357914214 hasConcept C62520636 @default.
- W2357914214 hasConcept C7770020 @default.
- W2357914214 hasConcept C95457728 @default.
- W2357914214 hasConcept C96035792 @default.
- W2357914214 hasConceptScore W2357914214C11608111 @default.
- W2357914214 hasConceptScore W2357914214C121332964 @default.
- W2357914214 hasConceptScore W2357914214C152568617 @default.
- W2357914214 hasConceptScore W2357914214C153294291 @default.
- W2357914214 hasConceptScore W2357914214C159985019 @default.
- W2357914214 hasConceptScore W2357914214C166957645 @default.
- W2357914214 hasConceptScore W2357914214C171250308 @default.
- W2357914214 hasConceptScore W2357914214C176711861 @default.
- W2357914214 hasConceptScore W2357914214C177564732 @default.
- W2357914214 hasConceptScore W2357914214C192562407 @default.
- W2357914214 hasConceptScore W2357914214C204530211 @default.
- W2357914214 hasConceptScore W2357914214C2779227376 @default.
- W2357914214 hasConceptScore W2357914214C2781448156 @default.
- W2357914214 hasConceptScore W2357914214C51576277 @default.
- W2357914214 hasConceptScore W2357914214C541528975 @default.
- W2357914214 hasConceptScore W2357914214C57410435 @default.
- W2357914214 hasConceptScore W2357914214C62520636 @default.
- W2357914214 hasConceptScore W2357914214C7770020 @default.
- W2357914214 hasConceptScore W2357914214C95457728 @default.
- W2357914214 hasConceptScore W2357914214C96035792 @default.
- W2357914214 hasIssue "9" @default.
- W2357914214 hasLocation W23579142141 @default.
- W2357914214 hasOpenAccess W2357914214 @default.
- W2357914214 hasPrimaryLocation W23579142141 @default.
- W2357914214 hasRelatedWork W1607108628 @default.
- W2357914214 hasRelatedWork W1966154262 @default.
- W2357914214 hasRelatedWork W1979043150 @default.
- W2357914214 hasRelatedWork W2000303132 @default.
- W2357914214 hasRelatedWork W2020099378 @default.
- W2357914214 hasRelatedWork W2030038854 @default.
- W2357914214 hasRelatedWork W2030566566 @default.
- W2357914214 hasRelatedWork W2034315821 @default.
- W2357914214 hasRelatedWork W2038468675 @default.
- W2357914214 hasRelatedWork W2044640896 @default.
- W2357914214 hasRelatedWork W2074612411 @default.
- W2357914214 hasRelatedWork W2086505932 @default.
- W2357914214 hasRelatedWork W2105563503 @default.
- W2357914214 hasRelatedWork W2128937175 @default.
- W2357914214 hasRelatedWork W2356878545 @default.
- W2357914214 hasRelatedWork W2515933833 @default.
- W2357914214 hasRelatedWork W2980954776 @default.
- W2357914214 hasRelatedWork W642538808 @default.
- W2357914214 hasRelatedWork W2054193820 @default.
- W2357914214 hasRelatedWork W2950208131 @default.
- W2357914214 hasVolume "41" @default.
- W2357914214 isParatext "false" @default.
- W2357914214 isRetracted "false" @default.
- W2357914214 magId "2357914214" @default.
- W2357914214 workType "article" @default.