- W2360345605 abstract "The hydration properties of a synthesized water soluble phenol-formaldehyde resin, and the influences of reaction parameters on the properties of it were investigated with dynamic light scattering technology, and by means of viscosity and critical coagulating concentration(CCC) determination. The results show that the resin prepared with sodium hydroxide as catalyst at a phenol/formaldehyde mole ratio of 3∶1 can be dissolved in distilled water to form a transparent solution. The viscosity of a 10% resin solution ranges from 1.529 1 mPa·s to 6.064 7 mPa·s, and the dispersed unit in a 50 mg/L resin solution exhibits a hydrodynamics diameter between 2.1 nm and 21.1 nm and a Zeta potential varying from -54.38 mV to -10.07 mV. NaCl can weaken the resin hydration and make the resin flocculate, the CCC for different resin product solution is from 0.014 mol/L to 0.099 mol/L. The hydration properties of the resin under different reaction conditions show that along with the prepolymer mass fraction, the polymerization degree of the resin product is increased as the reaction time and reaction temperature increase, causing the viscosity of 10% resin solution and the hydrodynamics diameter of resin aggregate in dilute solution to increase. On the contrary, the CCC of the resin dilute solution and the Zeta potential of the rein aggregate are decreased. Furthermore, the change of the resin caused by the prepolymer mass fraction difference is comparatively insignificant. Otherwise, reaction time can intensively affect the product. In addition, the polycondensation below 90 ℃ is difficult to take place." @default.
- W2360345605 created "2016-06-24" @default.
- W2360345605 creator A5000597313 @default.
- W2360345605 date "2008-01-01" @default.
- W2360345605 modified "2023-09-25" @default.
- W2360345605 title "Synthesis and Hydration Properties of Water Soluble Phenol-formaldehyde Resin" @default.
- W2360345605 hasPublicationYear "2008" @default.
- W2360345605 type Work @default.
- W2360345605 sameAs 2360345605 @default.
- W2360345605 citedByCount "0" @default.
- W2360345605 crossrefType "journal-article" @default.
- W2360345605 hasAuthorship W2360345605A5000597313 @default.
- W2360345605 hasConcept C116628846 @default.
- W2360345605 hasConcept C127172972 @default.
- W2360345605 hasConcept C127413603 @default.
- W2360345605 hasConcept C155672457 @default.
- W2360345605 hasConcept C159985019 @default.
- W2360345605 hasConcept C178790620 @default.
- W2360345605 hasConcept C185592680 @default.
- W2360345605 hasConcept C188027245 @default.
- W2360345605 hasConcept C192562407 @default.
- W2360345605 hasConcept C2775930285 @default.
- W2360345605 hasConcept C2777702071 @default.
- W2360345605 hasConcept C2778562268 @default.
- W2360345605 hasConcept C2778790047 @default.
- W2360345605 hasConcept C2779429693 @default.
- W2360345605 hasConcept C2779498867 @default.
- W2360345605 hasConcept C2779578285 @default.
- W2360345605 hasConcept C42360764 @default.
- W2360345605 hasConcept C43617362 @default.
- W2360345605 hasConcept C44228677 @default.
- W2360345605 hasConcept C521977710 @default.
- W2360345605 hasConcept C86181022 @default.
- W2360345605 hasConceptScore W2360345605C116628846 @default.
- W2360345605 hasConceptScore W2360345605C127172972 @default.
- W2360345605 hasConceptScore W2360345605C127413603 @default.
- W2360345605 hasConceptScore W2360345605C155672457 @default.
- W2360345605 hasConceptScore W2360345605C159985019 @default.
- W2360345605 hasConceptScore W2360345605C178790620 @default.
- W2360345605 hasConceptScore W2360345605C185592680 @default.
- W2360345605 hasConceptScore W2360345605C188027245 @default.
- W2360345605 hasConceptScore W2360345605C192562407 @default.
- W2360345605 hasConceptScore W2360345605C2775930285 @default.
- W2360345605 hasConceptScore W2360345605C2777702071 @default.
- W2360345605 hasConceptScore W2360345605C2778562268 @default.
- W2360345605 hasConceptScore W2360345605C2778790047 @default.
- W2360345605 hasConceptScore W2360345605C2779429693 @default.
- W2360345605 hasConceptScore W2360345605C2779498867 @default.
- W2360345605 hasConceptScore W2360345605C2779578285 @default.
- W2360345605 hasConceptScore W2360345605C42360764 @default.
- W2360345605 hasConceptScore W2360345605C43617362 @default.
- W2360345605 hasConceptScore W2360345605C44228677 @default.
- W2360345605 hasConceptScore W2360345605C521977710 @default.
- W2360345605 hasConceptScore W2360345605C86181022 @default.
- W2360345605 hasLocation W23603456051 @default.
- W2360345605 hasOpenAccess W2360345605 @default.
- W2360345605 hasPrimaryLocation W23603456051 @default.
- W2360345605 hasRelatedWork W2027661298 @default.
- W2360345605 hasRelatedWork W2260726366 @default.
- W2360345605 hasRelatedWork W2332404172 @default.
- W2360345605 hasRelatedWork W2348174150 @default.
- W2360345605 hasRelatedWork W2348193682 @default.
- W2360345605 hasRelatedWork W2356161309 @default.
- W2360345605 hasRelatedWork W2357790989 @default.
- W2360345605 hasRelatedWork W2366021610 @default.
- W2360345605 hasRelatedWork W2370075092 @default.
- W2360345605 hasRelatedWork W2372409105 @default.
- W2360345605 hasRelatedWork W2390948983 @default.
- W2360345605 hasRelatedWork W2780578072 @default.
- W2360345605 hasRelatedWork W2781035288 @default.
- W2360345605 hasRelatedWork W2827225808 @default.
- W2360345605 hasRelatedWork W2827970162 @default.
- W2360345605 hasRelatedWork W2833205658 @default.
- W2360345605 hasRelatedWork W2845439654 @default.
- W2360345605 hasRelatedWork W2855090302 @default.
- W2360345605 hasRelatedWork W2926553747 @default.
- W2360345605 hasRelatedWork W3018329736 @default.
- W2360345605 isParatext "false" @default.
- W2360345605 isRetracted "false" @default.
- W2360345605 magId "2360345605" @default.
- W2360345605 workType "article" @default.