- W2362589937 abstract "Effect of chemically strengthening on glass wear resistance was investigated.The chemically strengthening process was carried out in molten KNO3 at 430~500 ℃ for 2~8 h.The glass samples were tested by JM-I type abrasion tester at different loads.The wear mass loss was weighed by electronic balance,by which the wear properties of glass surface were estimated.The grinding crack morphologies of glass samples were observed by optical microscope,and the flexural strength of glass samples before and after wear process were measured by CMT5204 type electronic multi-function testing machine.With the same wear process(2.5 N,80 s),the number of grinding cracks on the surface of as-received glass was more and deeper than that of chemically strengthened glass.The wear mass loss of chemically strengthened glass(450 ℃,8 h) was only 1/10 than that of as-received one.The flexural strength of as-received glass decreased about 50% after wear process,whereas the flexural strength of chemically strengthened glass decreased only about 11% than that of unworn samples.It indicates that chemically strengthening can improve wear resistance of glass sample." @default.
- W2362589937 created "2016-06-24" @default.
- W2362589937 creator A5012902683 @default.
- W2362589937 date "2007-01-01" @default.
- W2362589937 modified "2023-09-26" @default.
- W2362589937 title "Surface Wear Resistance of Chemically Strengthened Glass" @default.
- W2362589937 hasPublicationYear "2007" @default.
- W2362589937 type Work @default.
- W2362589937 sameAs 2362589937 @default.
- W2362589937 citedByCount "0" @default.
- W2362589937 crossrefType "journal-article" @default.
- W2362589937 hasAuthorship W2362589937A5012902683 @default.
- W2362589937 hasConcept C118231568 @default.
- W2362589937 hasConcept C159985019 @default.
- W2362589937 hasConcept C178405089 @default.
- W2362589937 hasConcept C192562407 @default.
- W2362589937 hasConcept C2777571299 @default.
- W2362589937 hasConcept C2983445633 @default.
- W2362589937 hasConcept C35288751 @default.
- W2362589937 hasConceptScore W2362589937C118231568 @default.
- W2362589937 hasConceptScore W2362589937C159985019 @default.
- W2362589937 hasConceptScore W2362589937C178405089 @default.
- W2362589937 hasConceptScore W2362589937C192562407 @default.
- W2362589937 hasConceptScore W2362589937C2777571299 @default.
- W2362589937 hasConceptScore W2362589937C2983445633 @default.
- W2362589937 hasConceptScore W2362589937C35288751 @default.
- W2362589937 hasLocation W23625899371 @default.
- W2362589937 hasOpenAccess W2362589937 @default.
- W2362589937 hasPrimaryLocation W23625899371 @default.
- W2362589937 hasRelatedWork W1605177717 @default.
- W2362589937 hasRelatedWork W1989201450 @default.
- W2362589937 hasRelatedWork W1992090766 @default.
- W2362589937 hasRelatedWork W2009072427 @default.
- W2362589937 hasRelatedWork W2009613125 @default.
- W2362589937 hasRelatedWork W2037232286 @default.
- W2362589937 hasRelatedWork W2043370225 @default.
- W2362589937 hasRelatedWork W2067693703 @default.
- W2362589937 hasRelatedWork W2073919641 @default.
- W2362589937 hasRelatedWork W2089027900 @default.
- W2362589937 hasRelatedWork W2349421146 @default.
- W2362589937 hasRelatedWork W2352717576 @default.
- W2362589937 hasRelatedWork W2355766349 @default.
- W2362589937 hasRelatedWork W2360955807 @default.
- W2362589937 hasRelatedWork W2369293390 @default.
- W2362589937 hasRelatedWork W2382697153 @default.
- W2362589937 hasRelatedWork W3004672234 @default.
- W2362589937 hasRelatedWork W3014748863 @default.
- W2362589937 hasRelatedWork W3170662447 @default.
- W2362589937 hasRelatedWork W2186050640 @default.
- W2362589937 isParatext "false" @default.
- W2362589937 isRetracted "false" @default.
- W2362589937 magId "2362589937" @default.
- W2362589937 workType "article" @default.