- W2362967658 abstract "The bulk glassy Cu 60 Zr 30 Ti 10 alloy with a diameter up to 4 mm and a length of 70 mm containing nanocrystalline phase was successfully developed by using copper mold casting method. The temperature interval of the supercooled liquid region before crystallization is above 37 K. The glass transition temperature ( T g) and the reduced glass transition temperature ( T g/ T l) of the cast bulk glassy Cu 60 Zr 30 Ti 10 alloy are 713 K and 0.62. The cast bulk glassy alloy, which has high glassy forming ability, shows expected mechanical properties. The elastic modulus, yield strength, fracture strength and elongation including elastic elongation are 114 GPa, 1 785 MPa, 2 150 MPa and 3.3% respectively in compressive deformation, and 112 GPa, 1 780 MPa, 2 000 MPa and 1.9% respectively in tensile deformation. High resolution transmission electron microscope (HRTEM) and nano beam electron diffraction (NBED) studies indicate that the cast metallic bulk glassy Cu 60 Zr 30 Ti 10 alloy consists of nanocrystals with a size of 4 nm embedded in glassy matrix. The nanoparticle is identified as CuZr and has point space group symmetry of pm3m and its lattice parameter is a =0.3 262 nm . The nanocrystalline phase grew up to 10 nm upon annealing at 430 ℃ for 10 min and caused the alloy brittle." @default.
- W2362967658 created "2016-06-24" @default.
- W2362967658 creator A5037458498 @default.
- W2362967658 date "2003-01-01" @default.
- W2362967658 modified "2023-09-25" @default.
- W2362967658 title "Nanostructured bulk glassy Cu_(60)Zr_(30)Ti_(10) alloy with high strength and good ductility in cast state" @default.
- W2362967658 hasPublicationYear "2003" @default.
- W2362967658 type Work @default.
- W2362967658 sameAs 2362967658 @default.
- W2362967658 citedByCount "0" @default.
- W2362967658 crossrefType "journal-article" @default.
- W2362967658 hasAuthorship W2362967658A5037458498 @default.
- W2362967658 hasConcept C112950240 @default.
- W2362967658 hasConcept C112964491 @default.
- W2362967658 hasConcept C121332964 @default.
- W2362967658 hasConcept C122865956 @default.
- W2362967658 hasConcept C123266363 @default.
- W2362967658 hasConcept C127413603 @default.
- W2362967658 hasConcept C140676511 @default.
- W2362967658 hasConcept C146088050 @default.
- W2362967658 hasConcept C159985019 @default.
- W2362967658 hasConcept C161368742 @default.
- W2362967658 hasConcept C171250308 @default.
- W2362967658 hasConcept C191897082 @default.
- W2362967658 hasConcept C192562407 @default.
- W2362967658 hasConcept C203036418 @default.
- W2362967658 hasConcept C2777855556 @default.
- W2362967658 hasConcept C2780026712 @default.
- W2362967658 hasConcept C42360764 @default.
- W2362967658 hasConcept C521977710 @default.
- W2362967658 hasConcept C97355855 @default.
- W2362967658 hasConceptScore W2362967658C112950240 @default.
- W2362967658 hasConceptScore W2362967658C112964491 @default.
- W2362967658 hasConceptScore W2362967658C121332964 @default.
- W2362967658 hasConceptScore W2362967658C122865956 @default.
- W2362967658 hasConceptScore W2362967658C123266363 @default.
- W2362967658 hasConceptScore W2362967658C127413603 @default.
- W2362967658 hasConceptScore W2362967658C140676511 @default.
- W2362967658 hasConceptScore W2362967658C146088050 @default.
- W2362967658 hasConceptScore W2362967658C159985019 @default.
- W2362967658 hasConceptScore W2362967658C161368742 @default.
- W2362967658 hasConceptScore W2362967658C171250308 @default.
- W2362967658 hasConceptScore W2362967658C191897082 @default.
- W2362967658 hasConceptScore W2362967658C192562407 @default.
- W2362967658 hasConceptScore W2362967658C203036418 @default.
- W2362967658 hasConceptScore W2362967658C2777855556 @default.
- W2362967658 hasConceptScore W2362967658C2780026712 @default.
- W2362967658 hasConceptScore W2362967658C42360764 @default.
- W2362967658 hasConceptScore W2362967658C521977710 @default.
- W2362967658 hasConceptScore W2362967658C97355855 @default.
- W2362967658 hasLocation W23629676581 @default.
- W2362967658 hasOpenAccess W2362967658 @default.
- W2362967658 hasPrimaryLocation W23629676581 @default.
- W2362967658 hasRelatedWork W1970802509 @default.
- W2362967658 hasRelatedWork W1990970981 @default.
- W2362967658 hasRelatedWork W1998693500 @default.
- W2362967658 hasRelatedWork W2002700964 @default.
- W2362967658 hasRelatedWork W2002862712 @default.
- W2362967658 hasRelatedWork W2007562443 @default.
- W2362967658 hasRelatedWork W2007618848 @default.
- W2362967658 hasRelatedWork W2023062340 @default.
- W2362967658 hasRelatedWork W2057472266 @default.
- W2362967658 hasRelatedWork W2058221811 @default.
- W2362967658 hasRelatedWork W2083440658 @default.
- W2362967658 hasRelatedWork W2088565476 @default.
- W2362967658 hasRelatedWork W2103481675 @default.
- W2362967658 hasRelatedWork W2158119405 @default.
- W2362967658 hasRelatedWork W2349235398 @default.
- W2362967658 hasRelatedWork W2349904013 @default.
- W2362967658 hasRelatedWork W2365614139 @default.
- W2362967658 hasRelatedWork W2372976802 @default.
- W2362967658 hasRelatedWork W2527712782 @default.
- W2362967658 hasRelatedWork W2471696900 @default.
- W2362967658 isParatext "false" @default.
- W2362967658 isRetracted "false" @default.
- W2362967658 magId "2362967658" @default.
- W2362967658 workType "article" @default.