- W2364753985 abstract "U-bend immersion tests were used for studying the stress corrosion cracking behaviors for electroslag welding(ESW) Alloy 600,electroslag welding(ESW) Alloy 690 and submerged-arc welding(SAW) Alloy 690. Results showed that electroslag welding Alloy 600,electroslag welding Alloy 690 and submerged-arc welding Alloy 690 samples were immune to stress corrosion cracking in simulated primary water of pressurized water reactor(PWR) after being immersed for 1193 h,which contained 1.5×10~(-3) B,2.3×10~(-6) Li,2.5×10~(-6) H_2 at 325℃,15.8 MPa.However,stress corrosion cracks were observed in electroslag welding Alloy 600 after being immersed in 10 wt.%NaOH alkali solution for 720 h at 330℃,11 MPa.The maximum crack length was 835μm after 720 h immersion and further expanded to 1135μm after 1440 h immersion with a typical intergranular stress corrosion cracking(IGSCC) characteristic.For electroslag welding Alloy 690,microcracks were initiated with the length of 0.3μm to 1.15μm and stress corrosion crack was not observed." @default.
- W2364753985 created "2016-06-24" @default.
- W2364753985 creator A5000122950 @default.
- W2364753985 date "2011-01-01" @default.
- W2364753985 modified "2023-09-23" @default.
- W2364753985 title "STRESS CORROSION CRACKING BEHAVIORS FOR DIFFERENT NI-BASED WELDING MATERIALS IN HIGH TEMPERATURE AND HIGH PRESSURE WATER" @default.
- W2364753985 hasPublicationYear "2011" @default.
- W2364753985 type Work @default.
- W2364753985 sameAs 2364753985 @default.
- W2364753985 citedByCount "0" @default.
- W2364753985 crossrefType "journal-article" @default.
- W2364753985 hasAuthorship W2364753985A5000122950 @default.
- W2364753985 hasConcept C159985019 @default.
- W2364753985 hasConcept C184102282 @default.
- W2364753985 hasConcept C191897082 @default.
- W2364753985 hasConcept C192562407 @default.
- W2364753985 hasConcept C19474535 @default.
- W2364753985 hasConcept C20480867 @default.
- W2364753985 hasConcept C20625102 @default.
- W2364753985 hasConcept C2778760603 @default.
- W2364753985 hasConcept C2780026712 @default.
- W2364753985 hasConcept C58396970 @default.
- W2364753985 hasConceptScore W2364753985C159985019 @default.
- W2364753985 hasConceptScore W2364753985C184102282 @default.
- W2364753985 hasConceptScore W2364753985C191897082 @default.
- W2364753985 hasConceptScore W2364753985C192562407 @default.
- W2364753985 hasConceptScore W2364753985C19474535 @default.
- W2364753985 hasConceptScore W2364753985C20480867 @default.
- W2364753985 hasConceptScore W2364753985C20625102 @default.
- W2364753985 hasConceptScore W2364753985C2778760603 @default.
- W2364753985 hasConceptScore W2364753985C2780026712 @default.
- W2364753985 hasConceptScore W2364753985C58396970 @default.
- W2364753985 hasOpenAccess W2364753985 @default.
- W2364753985 hasRelatedWork W1516527585 @default.
- W2364753985 hasRelatedWork W1987657525 @default.
- W2364753985 hasRelatedWork W2012231028 @default.
- W2364753985 hasRelatedWork W2043379611 @default.
- W2364753985 hasRelatedWork W2053876108 @default.
- W2364753985 hasRelatedWork W2112470687 @default.
- W2364753985 hasRelatedWork W220857777 @default.
- W2364753985 hasRelatedWork W2324925785 @default.
- W2364753985 hasRelatedWork W2371138186 @default.
- W2364753985 hasRelatedWork W2502026166 @default.
- W2364753985 hasRelatedWork W2699199892 @default.
- W2364753985 hasRelatedWork W2734898671 @default.
- W2364753985 hasRelatedWork W2756321249 @default.
- W2364753985 hasRelatedWork W2945471105 @default.
- W2364753985 hasRelatedWork W2996311693 @default.
- W2364753985 hasRelatedWork W3131128803 @default.
- W2364753985 hasRelatedWork W425914 @default.
- W2364753985 hasRelatedWork W812584461 @default.
- W2364753985 hasRelatedWork W816960182 @default.
- W2364753985 hasRelatedWork W222915653 @default.
- W2364753985 isParatext "false" @default.
- W2364753985 isRetracted "false" @default.
- W2364753985 magId "2364753985" @default.
- W2364753985 workType "article" @default.