- W2366253002 abstract "High hardness composite chromium carbide was successfully produced by in situ synthesis technology,which make it possible to prepare high temperature wear resistance alloy.Chemical reaction among Cr,Fe and C powder which were mixed and laid on the metal surface occurred through vacuum electron beam rotary scanning heating.The resultant of reaction at the metal was identified as Cr7C3 composite by X-ray diffraction.And microstructure of composite shows that there is chromium carbide congregated at the metal surface.The mechanical properties show that surface hardness is higher than that of base metal because of chromium carbide.In situ synthesis technology was proved to be a good way to realize metal surface modification." @default.
- W2366253002 created "2016-06-24" @default.
- W2366253002 creator A5020139374 @default.
- W2366253002 date "2007-01-01" @default.
- W2366253002 modified "2023-09-26" @default.
- W2366253002 title "Chromium Carbide in situ synthesis by vacuum electron beam" @default.
- W2366253002 hasPublicationYear "2007" @default.
- W2366253002 type Work @default.
- W2366253002 sameAs 2366253002 @default.
- W2366253002 citedByCount "0" @default.
- W2366253002 crossrefType "journal-article" @default.
- W2366253002 hasAuthorship W2366253002A5020139374 @default.
- W2366253002 hasConcept C104779481 @default.
- W2366253002 hasConcept C159985019 @default.
- W2366253002 hasConcept C191897082 @default.
- W2366253002 hasConcept C192562407 @default.
- W2366253002 hasConcept C2776776789 @default.
- W2366253002 hasConcept C2780026712 @default.
- W2366253002 hasConcept C511782168 @default.
- W2366253002 hasConcept C5335593 @default.
- W2366253002 hasConcept C544153396 @default.
- W2366253002 hasConcept C87976508 @default.
- W2366253002 hasConceptScore W2366253002C104779481 @default.
- W2366253002 hasConceptScore W2366253002C159985019 @default.
- W2366253002 hasConceptScore W2366253002C191897082 @default.
- W2366253002 hasConceptScore W2366253002C192562407 @default.
- W2366253002 hasConceptScore W2366253002C2776776789 @default.
- W2366253002 hasConceptScore W2366253002C2780026712 @default.
- W2366253002 hasConceptScore W2366253002C511782168 @default.
- W2366253002 hasConceptScore W2366253002C5335593 @default.
- W2366253002 hasConceptScore W2366253002C544153396 @default.
- W2366253002 hasConceptScore W2366253002C87976508 @default.
- W2366253002 hasLocation W23662530021 @default.
- W2366253002 hasOpenAccess W2366253002 @default.
- W2366253002 hasPrimaryLocation W23662530021 @default.
- W2366253002 hasRelatedWork W1967987009 @default.
- W2366253002 hasRelatedWork W2013658752 @default.
- W2366253002 hasRelatedWork W2052107960 @default.
- W2366253002 hasRelatedWork W2067781194 @default.
- W2366253002 hasRelatedWork W2084430426 @default.
- W2366253002 hasRelatedWork W2110500021 @default.
- W2366253002 hasRelatedWork W2317188225 @default.
- W2366253002 hasRelatedWork W2550481525 @default.
- W2366253002 hasRelatedWork W2752845104 @default.
- W2366253002 hasRelatedWork W2884456879 @default.
- W2366253002 hasRelatedWork W2903869362 @default.
- W2366253002 hasRelatedWork W2916225750 @default.
- W2366253002 hasRelatedWork W2973997514 @default.
- W2366253002 hasRelatedWork W3021144989 @default.
- W2366253002 hasRelatedWork W3025079273 @default.
- W2366253002 hasRelatedWork W3028892527 @default.
- W2366253002 hasRelatedWork W3039444625 @default.
- W2366253002 hasRelatedWork W2828883461 @default.
- W2366253002 hasRelatedWork W2830673987 @default.
- W2366253002 hasRelatedWork W2934806471 @default.
- W2366253002 isParatext "false" @default.
- W2366253002 isRetracted "false" @default.
- W2366253002 magId "2366253002" @default.
- W2366253002 workType "article" @default.