- W2367346110 abstract "Aiming at developing novel microwave-transparent ceramics with low dielectric loss,high thermal conductivity and high strength,Si3N4-AlN(30%,mass fraction) composite ceramics with La2O3 as sintering additive were prepared by hot-pressing at 1 800 °C and subsequently annealed at 1 450 °C and 1 850 °C for 2 h and 4 h,respectively.The materials were characterized by XRD and SEM.The effect of annealing process on the phase composition,sintering performance,microstructure,bending strength,dielectric loss and thermal conductivity of the materials was investigated.The results showed that both annealing at 1 850 °C and 1 450 °C promoted the phase transformation of α-Si3N4 to β-Si3N4.After annealing at 1 850 °C,grain growth to a certain extent occurred in the materials.Especially,the elongated β-Si3N4 grains showed a slight increase in diameter from 0.2 μm to 0.6 μm approximately and a decrease in aspect ratio.As a result,as the annealing time increased to 4 h,the bending strength declined from 456 MPa to 390 MPa,whereas the dielectric loss decreased to 2.15×10-3 and the thermal conductivity increased to 16.3 W/(m·K) gradually.When annealed at 1 450 °C,increasing the annealing time to 4 h significantly promoted the crystallization of glassy phase to La2Si6N8O3 phase in the materials,which led to the increase in bending strength to 619 MPa and thermal conductivity to 15.9 W/(m·K),respectively,and simultaneously the decrease in dielectric loss to 1.53×10-3." @default.
- W2367346110 created "2016-06-24" @default.
- W2367346110 creator A5012997112 @default.
- W2367346110 date "2011-01-01" @default.
- W2367346110 modified "2023-09-23" @default.
- W2367346110 title "Effect of annealing on microstructure and properties of Si_3N_4-AlN composite ceramics" @default.
- W2367346110 hasPublicationYear "2011" @default.
- W2367346110 type Work @default.
- W2367346110 sameAs 2367346110 @default.
- W2367346110 citedByCount "0" @default.
- W2367346110 crossrefType "journal-article" @default.
- W2367346110 hasAuthorship W2367346110A5012997112 @default.
- W2367346110 hasConcept C104779481 @default.
- W2367346110 hasConcept C127413603 @default.
- W2367346110 hasConcept C131540310 @default.
- W2367346110 hasConcept C133386390 @default.
- W2367346110 hasConcept C134132462 @default.
- W2367346110 hasConcept C147789679 @default.
- W2367346110 hasConcept C159985019 @default.
- W2367346110 hasConcept C185592680 @default.
- W2367346110 hasConcept C192191005 @default.
- W2367346110 hasConcept C192562407 @default.
- W2367346110 hasConcept C199289684 @default.
- W2367346110 hasConcept C203036418 @default.
- W2367346110 hasConcept C2777581544 @default.
- W2367346110 hasConcept C2777855556 @default.
- W2367346110 hasConcept C42360764 @default.
- W2367346110 hasConcept C49040817 @default.
- W2367346110 hasConcept C87976508 @default.
- W2367346110 hasConcept C91066073 @default.
- W2367346110 hasConcept C97346530 @default.
- W2367346110 hasConcept C98390173 @default.
- W2367346110 hasConceptScore W2367346110C104779481 @default.
- W2367346110 hasConceptScore W2367346110C127413603 @default.
- W2367346110 hasConceptScore W2367346110C131540310 @default.
- W2367346110 hasConceptScore W2367346110C133386390 @default.
- W2367346110 hasConceptScore W2367346110C134132462 @default.
- W2367346110 hasConceptScore W2367346110C147789679 @default.
- W2367346110 hasConceptScore W2367346110C159985019 @default.
- W2367346110 hasConceptScore W2367346110C185592680 @default.
- W2367346110 hasConceptScore W2367346110C192191005 @default.
- W2367346110 hasConceptScore W2367346110C192562407 @default.
- W2367346110 hasConceptScore W2367346110C199289684 @default.
- W2367346110 hasConceptScore W2367346110C203036418 @default.
- W2367346110 hasConceptScore W2367346110C2777581544 @default.
- W2367346110 hasConceptScore W2367346110C2777855556 @default.
- W2367346110 hasConceptScore W2367346110C42360764 @default.
- W2367346110 hasConceptScore W2367346110C49040817 @default.
- W2367346110 hasConceptScore W2367346110C87976508 @default.
- W2367346110 hasConceptScore W2367346110C91066073 @default.
- W2367346110 hasConceptScore W2367346110C97346530 @default.
- W2367346110 hasConceptScore W2367346110C98390173 @default.
- W2367346110 hasLocation W23673461101 @default.
- W2367346110 hasOpenAccess W2367346110 @default.
- W2367346110 hasPrimaryLocation W23673461101 @default.
- W2367346110 hasRelatedWork W2013845406 @default.
- W2367346110 hasRelatedWork W2020325523 @default.
- W2367346110 hasRelatedWork W2020949333 @default.
- W2367346110 hasRelatedWork W2040268217 @default.
- W2367346110 hasRelatedWork W2080095493 @default.
- W2367346110 hasRelatedWork W2298692926 @default.
- W2367346110 hasRelatedWork W2339074179 @default.
- W2367346110 hasRelatedWork W2379221907 @default.
- W2367346110 hasRelatedWork W2384287694 @default.
- W2367346110 hasRelatedWork W2386830101 @default.
- W2367346110 hasRelatedWork W2692136365 @default.
- W2367346110 hasRelatedWork W2972258659 @default.
- W2367346110 hasRelatedWork W2977467196 @default.
- W2367346110 hasRelatedWork W2990325402 @default.
- W2367346110 hasRelatedWork W3011985841 @default.
- W2367346110 hasRelatedWork W3057934319 @default.
- W2367346110 hasRelatedWork W3164908100 @default.
- W2367346110 hasRelatedWork W3171319141 @default.
- W2367346110 hasRelatedWork W3184076136 @default.
- W2367346110 hasRelatedWork W2338720222 @default.
- W2367346110 isParatext "false" @default.
- W2367346110 isRetracted "false" @default.
- W2367346110 magId "2367346110" @default.
- W2367346110 workType "article" @default.