- W2368573762 abstract "Creep-rupture test was performed under the temperature of 500℃ and different stresses for heat treated high temperature Cr-Co-Mo-Ni gear and bearing steel.The creep-rupture strength obtained by interpolation was 1 022MPa at the state of 500℃for 500h.The microstructure of the samples,before and after creep-rupture test, was investigated by OM,SEM and TEM.The results show that the rupture time extends from 96.4hto 845.8h, the average size of carbides in the matrix increases from 0.3μm to 0.5μm and the area ratio increases from 1.65%to 3.85% with the stresses reduced from 1150MPa to 950MPa at the state of 500℃.With the reduction of stresses and the extension of rupture time,the martensite lath changes with shear deformation,fragmentation and rearranges.And the dislocation density decreases.The precipitated phase is always M6C before and after creep-rupture test." @default.
- W2368573762 created "2016-06-24" @default.
- W2368573762 creator A5065291372 @default.
- W2368573762 date "2014-01-01" @default.
- W2368573762 modified "2023-09-24" @default.
- W2368573762 title "Microstructure Evolution Research of Cr-Co-Mo-Ni Gear and Bearing Steel Under Action of Temperature and Stress Coupling" @default.
- W2368573762 hasPublicationYear "2014" @default.
- W2368573762 type Work @default.
- W2368573762 sameAs 2368573762 @default.
- W2368573762 citedByCount "0" @default.
- W2368573762 crossrefType "journal-article" @default.
- W2368573762 hasAuthorship W2368573762A5065291372 @default.
- W2368573762 hasConcept C138885662 @default.
- W2368573762 hasConcept C149912024 @default.
- W2368573762 hasConcept C159985019 @default.
- W2368573762 hasConcept C18747287 @default.
- W2368573762 hasConcept C191897082 @default.
- W2368573762 hasConcept C192562407 @default.
- W2368573762 hasConcept C199978012 @default.
- W2368573762 hasConcept C205649164 @default.
- W2368573762 hasConcept C21036866 @default.
- W2368573762 hasConcept C2780430920 @default.
- W2368573762 hasConcept C41895202 @default.
- W2368573762 hasConcept C5335593 @default.
- W2368573762 hasConcept C58640448 @default.
- W2368573762 hasConcept C87976508 @default.
- W2368573762 hasConceptScore W2368573762C138885662 @default.
- W2368573762 hasConceptScore W2368573762C149912024 @default.
- W2368573762 hasConceptScore W2368573762C159985019 @default.
- W2368573762 hasConceptScore W2368573762C18747287 @default.
- W2368573762 hasConceptScore W2368573762C191897082 @default.
- W2368573762 hasConceptScore W2368573762C192562407 @default.
- W2368573762 hasConceptScore W2368573762C199978012 @default.
- W2368573762 hasConceptScore W2368573762C205649164 @default.
- W2368573762 hasConceptScore W2368573762C21036866 @default.
- W2368573762 hasConceptScore W2368573762C2780430920 @default.
- W2368573762 hasConceptScore W2368573762C41895202 @default.
- W2368573762 hasConceptScore W2368573762C5335593 @default.
- W2368573762 hasConceptScore W2368573762C58640448 @default.
- W2368573762 hasConceptScore W2368573762C87976508 @default.
- W2368573762 hasLocation W23685737621 @default.
- W2368573762 hasOpenAccess W2368573762 @default.
- W2368573762 hasPrimaryLocation W23685737621 @default.
- W2368573762 hasRelatedWork W1481388403 @default.
- W2368573762 hasRelatedWork W1966806959 @default.
- W2368573762 hasRelatedWork W2001832428 @default.
- W2368573762 hasRelatedWork W2004019093 @default.
- W2368573762 hasRelatedWork W2009668883 @default.
- W2368573762 hasRelatedWork W2021497376 @default.
- W2368573762 hasRelatedWork W2064829449 @default.
- W2368573762 hasRelatedWork W2068615913 @default.
- W2368573762 hasRelatedWork W2074245759 @default.
- W2368573762 hasRelatedWork W2371543408 @default.
- W2368573762 hasRelatedWork W2510183592 @default.
- W2368573762 hasRelatedWork W2604189803 @default.
- W2368573762 hasRelatedWork W2607574994 @default.
- W2368573762 hasRelatedWork W2732148447 @default.
- W2368573762 hasRelatedWork W2744309296 @default.
- W2368573762 hasRelatedWork W2898606520 @default.
- W2368573762 hasRelatedWork W2970667981 @default.
- W2368573762 hasRelatedWork W388498615 @default.
- W2368573762 hasRelatedWork W851511245 @default.
- W2368573762 hasRelatedWork W3145036177 @default.
- W2368573762 isParatext "false" @default.
- W2368573762 isRetracted "false" @default.
- W2368573762 magId "2368573762" @default.
- W2368573762 workType "article" @default.