- W2368667186 abstract "A nickel-chromizing layer was formed on the surface of Q195 steel by pulse single power plasma.The surface morphology,phase composition and Cr-Ni content of nickel-chromizing layer were analyzed by XRD,SEM and EDS.The polarization curves of nickel-chromizing layer in 3.5% NaCl solution and 1 mol/L HNO3 solution were measured by electrochemical tests.The corrosion morphology was investigated and compared that of unprocessed samples of Q195 steel.The results show that the main phase composition of nickel-chromizing layer was Fe-Cr-Ni solid solution.The surface convex cellular organizations of nickel-chromizing layer were dense.The composition of the surface was Cr 16.9%,Ni 48.16%,and iron remaining.In NaCl solution,the surface of unprocessed sample of Q195 steel was corroded seriously resulted in holes,but the surface of nickel-chromizing layer only showed minor localized corrosion and produced some plaques.In HNO3 solution,the unprocessed sample of Q195 steel showed serious surface corrosion,but it was almost not corrode in the nickel-chromizing layer,i,e.,the corrosion resistance of the latter was much higher than that of the former." @default.
- W2368667186 created "2016-06-24" @default.
- W2368667186 creator A5072415978 @default.
- W2368667186 date "2012-01-01" @default.
- W2368667186 modified "2023-09-23" @default.
- W2368667186 title "Corrosion Resistance of Nickel-chromizing Layer Prepared by Pulse Single Power Plasma" @default.
- W2368667186 hasPublicationYear "2012" @default.
- W2368667186 type Work @default.
- W2368667186 sameAs 2368667186 @default.
- W2368667186 citedByCount "0" @default.
- W2368667186 crossrefType "journal-article" @default.
- W2368667186 hasAuthorship W2368667186A5072415978 @default.
- W2368667186 hasConcept C159985019 @default.
- W2368667186 hasConcept C191897082 @default.
- W2368667186 hasConcept C192562407 @default.
- W2368667186 hasConcept C197751951 @default.
- W2368667186 hasConcept C20625102 @default.
- W2368667186 hasConcept C2779227376 @default.
- W2368667186 hasConcept C504270822 @default.
- W2368667186 hasConcept C87976508 @default.
- W2368667186 hasConceptScore W2368667186C159985019 @default.
- W2368667186 hasConceptScore W2368667186C191897082 @default.
- W2368667186 hasConceptScore W2368667186C192562407 @default.
- W2368667186 hasConceptScore W2368667186C197751951 @default.
- W2368667186 hasConceptScore W2368667186C20625102 @default.
- W2368667186 hasConceptScore W2368667186C2779227376 @default.
- W2368667186 hasConceptScore W2368667186C504270822 @default.
- W2368667186 hasConceptScore W2368667186C87976508 @default.
- W2368667186 hasLocation W23686671861 @default.
- W2368667186 hasOpenAccess W2368667186 @default.
- W2368667186 hasPrimaryLocation W23686671861 @default.
- W2368667186 hasRelatedWork W10703937 @default.
- W2368667186 hasRelatedWork W1971653547 @default.
- W2368667186 hasRelatedWork W1985403289 @default.
- W2368667186 hasRelatedWork W1995799092 @default.
- W2368667186 hasRelatedWork W1996226241 @default.
- W2368667186 hasRelatedWork W2002077429 @default.
- W2368667186 hasRelatedWork W2031866762 @default.
- W2368667186 hasRelatedWork W2048747371 @default.
- W2368667186 hasRelatedWork W2079032841 @default.
- W2368667186 hasRelatedWork W2104591924 @default.
- W2368667186 hasRelatedWork W2349657870 @default.
- W2368667186 hasRelatedWork W2352319023 @default.
- W2368667186 hasRelatedWork W2365069989 @default.
- W2368667186 hasRelatedWork W2373142039 @default.
- W2368667186 hasRelatedWork W2374927127 @default.
- W2368667186 hasRelatedWork W2389373923 @default.
- W2368667186 hasRelatedWork W2419417762 @default.
- W2368667186 hasRelatedWork W2793986095 @default.
- W2368667186 hasRelatedWork W2803303453 @default.
- W2368667186 hasRelatedWork W2490781905 @default.
- W2368667186 isParatext "false" @default.
- W2368667186 isRetracted "false" @default.
- W2368667186 magId "2368667186" @default.
- W2368667186 workType "article" @default.