- W2368779807 abstract "Cold-rolled process and annealing process were studied for Baotou Iron and steel(Group)Co.on its CSP hot-rolled sheet with four different cold-rolled(50%,62.5%,67%,80%) reduction rate and two different annealing processes in furnace.By using microscope,the pit etching textures were observed and the hardness value of the samples were measured.The result shows that the favorable texture ｛111｝ was influenced by thickness of the same sample.The amount of｛111｝ texture of samples at the quarter thickness was more than that of half thickness and its proportion was increased apparently.Under the same annealing process and the same thickness condition,the line density value of ｛111｝/｛100｝ texture was increased at first and then decreased with increasing the cold-rolling reduction rate.At the rate of 67%,the maximum as well as the regularity of change in ｛111｝ texture were picked up.The longer the isothermal time was,the bigger the value of ｛111｝/｛100｝ texture was,together with larger proportion of the favorable texture at the same cold-rolling reduction rate." @default.
- W2368779807 created "2016-06-24" @default.
- W2368779807 creator A5077361386 @default.
- W2368779807 date "2005-01-01" @default.
- W2368779807 modified "2023-09-23" @default.
- W2368779807 title "The influence of cold-rolling and annealing process on cold-rolling sheet texture evolvement for Baotou Iron and Steel(Group) Co." @default.
- W2368779807 hasPublicationYear "2005" @default.
- W2368779807 type Work @default.
- W2368779807 sameAs 2368779807 @default.
- W2368779807 citedByCount "0" @default.
- W2368779807 crossrefType "journal-article" @default.
- W2368779807 hasAuthorship W2368779807A5077361386 @default.
- W2368779807 hasConcept C159985019 @default.
- W2368779807 hasConcept C191897082 @default.
- W2368779807 hasConcept C192562407 @default.
- W2368779807 hasConcept C2777855556 @default.
- W2368779807 hasConcept C2993092055 @default.
- W2368779807 hasConceptScore W2368779807C159985019 @default.
- W2368779807 hasConceptScore W2368779807C191897082 @default.
- W2368779807 hasConceptScore W2368779807C192562407 @default.
- W2368779807 hasConceptScore W2368779807C2777855556 @default.
- W2368779807 hasConceptScore W2368779807C2993092055 @default.
- W2368779807 hasLocation W23687798071 @default.
- W2368779807 hasOpenAccess W2368779807 @default.
- W2368779807 hasPrimaryLocation W23687798071 @default.
- W2368779807 hasRelatedWork W2018508640 @default.
- W2368779807 hasRelatedWork W2049710240 @default.
- W2368779807 hasRelatedWork W2348466351 @default.
- W2368779807 hasRelatedWork W2365503730 @default.
- W2368779807 hasRelatedWork W2369869337 @default.
- W2368779807 hasRelatedWork W2382378470 @default.
- W2368779807 hasRelatedWork W2470021117 @default.
- W2368779807 hasRelatedWork W2588566970 @default.
- W2368779807 hasRelatedWork W2792690841 @default.
- W2368779807 hasRelatedWork W2808780715 @default.
- W2368779807 hasRelatedWork W2865847725 @default.
- W2368779807 hasRelatedWork W2904374028 @default.
- W2368779807 hasRelatedWork W2968369870 @default.
- W2368779807 hasRelatedWork W2996704544 @default.
- W2368779807 hasRelatedWork W3017898376 @default.
- W2368779807 hasRelatedWork W3083949332 @default.
- W2368779807 hasRelatedWork W3143474416 @default.
- W2368779807 hasRelatedWork W3188017344 @default.
- W2368779807 hasRelatedWork W3214442619 @default.
- W2368779807 hasRelatedWork W2844801686 @default.
- W2368779807 isParatext "false" @default.
- W2368779807 isRetracted "false" @default.
- W2368779807 magId "2368779807" @default.
- W2368779807 workType "article" @default.