• W2369890813 abstract "By hotpressing method, TiB2TiC multiphase ceramics were fabricated from TiB2TiC composites powders under the following sintering conditions: sintering temperature: 1700 ℃ and 1800 ℃, pressure: 30 MPa, sintering time: 60 min. The relative density, the hardness and fracture toughness of TiB2TiC multiphase ceramic at room temperature were 99.8 %, 93.2 HRA and 5.53 MPa·m1/2 respectively. The residual porosities and dislocation in sintered ceramics went against the performance. The microstructure of TiB2TiC multiphase ceramics from composite powders had smaller and more symmetrical grains than the TiB2TiC ceramics sintered from the mixtures of TiB2 and TiC powders. The elements of B, C and Ti at the interface of TiB2 and TiC were distributed gradually. There were no impurities at the interface and the bonds between phases were strong, which probably has relation to the higher properties of TiB2TiC multiphase ceramics. The growth of TiB2 in different crystal directions was different in TiB2TiC multiphase ceramics." @default.
• W2369890813 created "2016-06-24" @default.
• W2369890813 creator A5036665244 @default.
• W2369890813 date "2003-01-01" @default.
• W2369890813 modified "2023-09-23" @default.
• W2369890813 title "STUDY ON THE STRUCTURE AND PROPERTIES OF TiB_2-TiC MULTIPHASE CERAMICS" @default.
• W2369890813 hasPublicationYear "2003" @default.
• W2369890813 type Work @default.
• W2369890813 sameAs 2369890813 @default.
• W2369890813 citedByCount "0" @default.
• W2369890813 crossrefType "journal-article" @default.
• W2369890813 hasAuthorship W2369890813A5036665244 @default.
• W2369890813 hasConcept C104779481 @default.
• W2369890813 hasConcept C134132462 @default.
• W2369890813 hasConcept C159985019 @default.
• W2369890813 hasConcept C191897082 @default.
• W2369890813 hasConcept C192562407 @default.
• W2369890813 hasConcept C2776578615 @default.
• W2369890813 hasConcept C2777581544 @default.
• W2369890813 hasConcept C82455628 @default.
• W2369890813 hasConcept C87976508 @default.
• W2369890813 hasConcept C97549433 @default.
• W2369890813 hasConceptScore W2369890813C104779481 @default.
• W2369890813 hasConceptScore W2369890813C134132462 @default.
• W2369890813 hasConceptScore W2369890813C159985019 @default.
• W2369890813 hasConceptScore W2369890813C191897082 @default.
• W2369890813 hasConceptScore W2369890813C192562407 @default.
• W2369890813 hasConceptScore W2369890813C2776578615 @default.
• W2369890813 hasConceptScore W2369890813C2777581544 @default.
• W2369890813 hasConceptScore W2369890813C82455628 @default.
• W2369890813 hasConceptScore W2369890813C87976508 @default.
• W2369890813 hasConceptScore W2369890813C97549433 @default.
• W2369890813 hasOpenAccess W2369890813 @default.
• W2369890813 hasRelatedWork W150163303 @default.
• W2369890813 hasRelatedWork W1974721409 @default.
• W2369890813 hasRelatedWork W1980277350 @default.
• W2369890813 hasRelatedWork W1991085315 @default.
• W2369890813 hasRelatedWork W2007914699 @default.
• W2369890813 hasRelatedWork W2037940676 @default.
• W2369890813 hasRelatedWork W2055288015 @default.
• W2369890813 hasRelatedWork W2068895261 @default.
• W2369890813 hasRelatedWork W2094764131 @default.
• W2369890813 hasRelatedWork W2315074034 @default.
• W2369890813 hasRelatedWork W2387485723 @default.
• W2369890813 hasRelatedWork W2512479025 @default.
• W2369890813 hasRelatedWork W3027861265 @default.
• W2369890813 hasRelatedWork W3037203274 @default.
• W2369890813 hasRelatedWork W3038229375 @default.
• W2369890813 hasRelatedWork W3086266435 @default.
• W2369890813 hasRelatedWork W3146778400 @default.
• W2369890813 hasRelatedWork W3165977859 @default.
• W2369890813 hasRelatedWork W3171724797 @default.
• W2369890813 hasRelatedWork W3198981834 @default.
• W2369890813 isParatext "false" @default.
• W2369890813 isRetracted "false" @default.
• W2369890813 magId "2369890813" @default.
• W2369890813 workType "article" @default.