- W2371495552 abstract "Tensile strength and elongation of Zn20SnxCu solder alloys melted by antivacuum furnace were measured.The results showed that tensile strength of Zn20SnxCu solder alloys was improved obviously by adding Cu into Zn20Sn solder and its elongation was decreased with the increasing of the Cu content(less than 8%).When Cu content was 8%,tensile strength of Zn20Sn8Cu solder alloy was 229.9 MPa which was about 1.86 times than that of the matrix solder.It was mainly related to the quantity and shape of the new CuZn5 metal intermetallic compound.The way of fracture was changed from plastic fracture to brittle fracture." @default.
- W2371495552 created "2016-06-24" @default.
- W2371495552 creator A5028835708 @default.
- W2371495552 date "2011-01-01" @default.
- W2371495552 modified "2023-09-24" @default.
- W2371495552 title "Impact of Cu content on mechanical properties of Zn20Sn solder" @default.
- W2371495552 hasPublicationYear "2011" @default.
- W2371495552 type Work @default.
- W2371495552 sameAs 2371495552 @default.
- W2371495552 citedByCount "0" @default.
- W2371495552 crossrefType "journal-article" @default.
- W2371495552 hasAuthorship W2371495552A5028835708 @default.
- W2371495552 hasConcept C112950240 @default.
- W2371495552 hasConcept C136478896 @default.
- W2371495552 hasConcept C159985019 @default.
- W2371495552 hasConcept C191897082 @default.
- W2371495552 hasConcept C192562407 @default.
- W2371495552 hasConcept C27501479 @default.
- W2371495552 hasConcept C2780026712 @default.
- W2371495552 hasConcept C2988439775 @default.
- W2371495552 hasConcept C33947775 @default.
- W2371495552 hasConcept C43369102 @default.
- W2371495552 hasConcept C50296614 @default.
- W2371495552 hasConceptScore W2371495552C112950240 @default.
- W2371495552 hasConceptScore W2371495552C136478896 @default.
- W2371495552 hasConceptScore W2371495552C159985019 @default.
- W2371495552 hasConceptScore W2371495552C191897082 @default.
- W2371495552 hasConceptScore W2371495552C192562407 @default.
- W2371495552 hasConceptScore W2371495552C27501479 @default.
- W2371495552 hasConceptScore W2371495552C2780026712 @default.
- W2371495552 hasConceptScore W2371495552C2988439775 @default.
- W2371495552 hasConceptScore W2371495552C33947775 @default.
- W2371495552 hasConceptScore W2371495552C43369102 @default.
- W2371495552 hasConceptScore W2371495552C50296614 @default.
- W2371495552 hasOpenAccess W2371495552 @default.
- W2371495552 hasRelatedWork W1980289453 @default.
- W2371495552 hasRelatedWork W2000211446 @default.
- W2371495552 hasRelatedWork W2026631297 @default.
- W2371495552 hasRelatedWork W2056907045 @default.
- W2371495552 hasRelatedWork W2069180894 @default.
- W2371495552 hasRelatedWork W2075525938 @default.
- W2371495552 hasRelatedWork W2140398932 @default.
- W2371495552 hasRelatedWork W2188595241 @default.
- W2371495552 hasRelatedWork W2307539054 @default.
- W2371495552 hasRelatedWork W2349212287 @default.
- W2371495552 hasRelatedWork W2616510073 @default.
- W2371495552 hasRelatedWork W2765844472 @default.
- W2371495552 hasRelatedWork W2808831092 @default.
- W2371495552 hasRelatedWork W2889866640 @default.
- W2371495552 hasRelatedWork W2901216416 @default.
- W2371495552 hasRelatedWork W2901667743 @default.
- W2371495552 hasRelatedWork W2951296256 @default.
- W2371495552 hasRelatedWork W3159826709 @default.
- W2371495552 hasRelatedWork W812545039 @default.
- W2371495552 hasRelatedWork W2527284769 @default.
- W2371495552 isParatext "false" @default.
- W2371495552 isRetracted "false" @default.
- W2371495552 magId "2371495552" @default.
- W2371495552 workType "article" @default.