- W2372187515 abstract "A turning of the slope at about 660 ℃ was found on the dilation-temperature curve of 9Cr martensitic heat resistant steel during heating process before α→γ phase transformation.In the present work,the steel samples were heated at the same heating rate from room temperature to 600,660 and 750 ℃,respectively,held for 15 min and then water-quenched.Optical microscope and scanning electron microscope were used to examine the microstructure difference of the three samples.The results show that there are much more precipitations in the samples heated to 660 and 750 ℃ than that heated to 600 ℃.Therefore,it could be concluded that the large amount of carbonitride precipitations in the steel at the turning point lead to the slope change on the dilation-temperature curve." @default.
- W2372187515 created "2016-06-24" @default.
- W2372187515 creator A5021572005 @default.
- W2372187515 date "2009-01-01" @default.
- W2372187515 modified "2023-09-28" @default.
- W2372187515 title "Slope change on dilation-temperature curve of 9Cr martensitic heat resistant steel" @default.
- W2372187515 hasPublicationYear "2009" @default.
- W2372187515 type Work @default.
- W2372187515 sameAs 2372187515 @default.
- W2372187515 citedByCount "0" @default.
- W2372187515 crossrefType "journal-article" @default.
- W2372187515 hasAuthorship W2372187515A5021572005 @default.
- W2372187515 hasConcept C114614502 @default.
- W2372187515 hasConcept C159985019 @default.
- W2372187515 hasConcept C18747287 @default.
- W2372187515 hasConcept C191897082 @default.
- W2372187515 hasConcept C192562407 @default.
- W2372187515 hasConcept C26771246 @default.
- W2372187515 hasConcept C2780757906 @default.
- W2372187515 hasConcept C33923547 @default.
- W2372187515 hasConcept C73170135 @default.
- W2372187515 hasConcept C77017923 @default.
- W2372187515 hasConcept C87976508 @default.
- W2372187515 hasConcept C90086362 @default.
- W2372187515 hasConceptScore W2372187515C114614502 @default.
- W2372187515 hasConceptScore W2372187515C159985019 @default.
- W2372187515 hasConceptScore W2372187515C18747287 @default.
- W2372187515 hasConceptScore W2372187515C191897082 @default.
- W2372187515 hasConceptScore W2372187515C192562407 @default.
- W2372187515 hasConceptScore W2372187515C26771246 @default.
- W2372187515 hasConceptScore W2372187515C2780757906 @default.
- W2372187515 hasConceptScore W2372187515C33923547 @default.
- W2372187515 hasConceptScore W2372187515C73170135 @default.
- W2372187515 hasConceptScore W2372187515C77017923 @default.
- W2372187515 hasConceptScore W2372187515C87976508 @default.
- W2372187515 hasConceptScore W2372187515C90086362 @default.
- W2372187515 hasOpenAccess W2372187515 @default.
- W2372187515 hasRelatedWork W153679767 @default.
- W2372187515 hasRelatedWork W1976443931 @default.
- W2372187515 hasRelatedWork W1989628550 @default.
- W2372187515 hasRelatedWork W2022040653 @default.
- W2372187515 hasRelatedWork W2209662481 @default.
- W2372187515 hasRelatedWork W2287316437 @default.
- W2372187515 hasRelatedWork W2348411994 @default.
- W2372187515 hasRelatedWork W2352268431 @default.
- W2372187515 hasRelatedWork W2353626362 @default.
- W2372187515 hasRelatedWork W2355113871 @default.
- W2372187515 hasRelatedWork W2357708597 @default.
- W2372187515 hasRelatedWork W2362453195 @default.
- W2372187515 hasRelatedWork W2370636422 @default.
- W2372187515 hasRelatedWork W2372789626 @default.
- W2372187515 hasRelatedWork W2374346074 @default.
- W2372187515 hasRelatedWork W2374489886 @default.
- W2372187515 hasRelatedWork W2378683733 @default.
- W2372187515 hasRelatedWork W2385742730 @default.
- W2372187515 hasRelatedWork W2392978621 @default.
- W2372187515 hasRelatedWork W2978854982 @default.
- W2372187515 isParatext "false" @default.
- W2372187515 isRetracted "false" @default.
- W2372187515 magId "2372187515" @default.
- W2372187515 workType "article" @default.