- W2378610918 abstract "Single-phase bulk Ti_(3)AlC_(2) was fabricated by mixture powders n(TiC)∶n(Ti)∶n(Al)∶n(Si)=2∶1∶ (1—1.1)∶(0.2—0.1). With soaked temperatures of 1 300 ℃ and 1 400 ℃, densities of the samples are 4.19 g/cm~(3 )and 4.22 g/cm~(3), purities of them are 98%(in mass , the same below) and 98.2%, and crystals are laminate with the dimension of 10—15 μm and 20—30 μm, respectively. Additive Si is uniformly distributed in the matrix. When the molar ratio of the additive Si was 0.2, formula of the compound is Ti_(2.76)Al_(0.78)Si_(0.22)C_(2). The Vicker′s hardness, Young′s modules, compressive strength, flexural strength, and fracture toughness are 3.3—5.0 GPa, 289 GPa, 785 MPa, 375 MPa, and 7.0 MPa·m~(1/2). Electric conductivity, heat capacity and thermal conductivity are 3.1×10~(6) S·m~(-1), 125.4 J/(mol·K) and 27.5 W/(m·K) at 25 ℃, thermal expansion coefficient is 8.8×10~(-6) K~(-1)." @default.
- W2378610918 created "2016-06-24" @default.
- W2378610918 creator A5068801158 @default.
- W2378610918 date "2004-01-01" @default.
- W2378610918 modified "2023-09-28" @default.
- W2378610918 title "FABRICATION, MICROSTRUCTURE AND PROPERTIES OF Ti_3AlC_2 SINTERED BY HOT-PRESSING" @default.
- W2378610918 hasPublicationYear "2004" @default.
- W2378610918 type Work @default.
- W2378610918 sameAs 2378610918 @default.
- W2378610918 citedByCount "0" @default.
- W2378610918 crossrefType "journal-article" @default.
- W2378610918 hasAuthorship W2378610918A5068801158 @default.
- W2378610918 hasConcept C113196181 @default.
- W2378610918 hasConcept C133392424 @default.
- W2378610918 hasConcept C136525101 @default.
- W2378610918 hasConcept C142724271 @default.
- W2378610918 hasConcept C159985019 @default.
- W2378610918 hasConcept C178405089 @default.
- W2378610918 hasConcept C178790620 @default.
- W2378610918 hasConcept C185592680 @default.
- W2378610918 hasConcept C192562407 @default.
- W2378610918 hasConcept C204787440 @default.
- W2378610918 hasConcept C2776578615 @default.
- W2378610918 hasConcept C30407753 @default.
- W2378610918 hasConcept C43617362 @default.
- W2378610918 hasConcept C44280652 @default.
- W2378610918 hasConcept C47463417 @default.
- W2378610918 hasConcept C71924100 @default.
- W2378610918 hasConcept C82455628 @default.
- W2378610918 hasConcept C87976508 @default.
- W2378610918 hasConcept C97346530 @default.
- W2378610918 hasConcept C97549433 @default.
- W2378610918 hasConceptScore W2378610918C113196181 @default.
- W2378610918 hasConceptScore W2378610918C133392424 @default.
- W2378610918 hasConceptScore W2378610918C136525101 @default.
- W2378610918 hasConceptScore W2378610918C142724271 @default.
- W2378610918 hasConceptScore W2378610918C159985019 @default.
- W2378610918 hasConceptScore W2378610918C178405089 @default.
- W2378610918 hasConceptScore W2378610918C178790620 @default.
- W2378610918 hasConceptScore W2378610918C185592680 @default.
- W2378610918 hasConceptScore W2378610918C192562407 @default.
- W2378610918 hasConceptScore W2378610918C204787440 @default.
- W2378610918 hasConceptScore W2378610918C2776578615 @default.
- W2378610918 hasConceptScore W2378610918C30407753 @default.
- W2378610918 hasConceptScore W2378610918C43617362 @default.
- W2378610918 hasConceptScore W2378610918C44280652 @default.
- W2378610918 hasConceptScore W2378610918C47463417 @default.
- W2378610918 hasConceptScore W2378610918C71924100 @default.
- W2378610918 hasConceptScore W2378610918C82455628 @default.
- W2378610918 hasConceptScore W2378610918C87976508 @default.
- W2378610918 hasConceptScore W2378610918C97346530 @default.
- W2378610918 hasConceptScore W2378610918C97549433 @default.
- W2378610918 hasLocation W23786109181 @default.
- W2378610918 hasOpenAccess W2378610918 @default.
- W2378610918 hasPrimaryLocation W23786109181 @default.
- W2378610918 hasRelatedWork W111975699 @default.
- W2378610918 hasRelatedWork W1998977190 @default.
- W2378610918 hasRelatedWork W2033896603 @default.
- W2378610918 hasRelatedWork W2108810865 @default.
- W2378610918 hasRelatedWork W2114875187 @default.
- W2378610918 hasRelatedWork W2314655863 @default.
- W2378610918 hasRelatedWork W2350962571 @default.
- W2378610918 hasRelatedWork W2367824248 @default.
- W2378610918 hasRelatedWork W2385639765 @default.
- W2378610918 hasRelatedWork W2504253302 @default.
- W2378610918 hasRelatedWork W2750940322 @default.
- W2378610918 hasRelatedWork W2800332621 @default.
- W2378610918 hasRelatedWork W2883113383 @default.
- W2378610918 hasRelatedWork W2913862769 @default.
- W2378610918 hasRelatedWork W2975569616 @default.
- W2378610918 hasRelatedWork W3015984308 @default.
- W2378610918 hasRelatedWork W3047100404 @default.
- W2378610918 hasRelatedWork W3135627132 @default.
- W2378610918 hasRelatedWork W3142782918 @default.
- W2378610918 hasRelatedWork W3201238743 @default.
- W2378610918 isParatext "false" @default.
- W2378610918 isRetracted "false" @default.
- W2378610918 magId "2378610918" @default.
- W2378610918 workType "article" @default.