• W2379131330 abstract "The laser glazing rapid solidification can make the dendrite refined and reduce the segregation of alloying elements,so it is very favorable to mechanical properties of alloys,e.g.,the fatigue life of Ni-based superalloy can be prolonged by laser surface melting process due to improved resistance to stress corrosion cleavage.The laser surface melting process can be used for modification of surface or repair of casting defects(such as surface porosity,surface stray grains) in single crystal components.Recently,this technique has become an attractive research subject with latent application. A successful laser glazing rapid solidification to single-crystal should ensure the preservation of the single-crystal nature,i.e.,the re-solidified surface layer needs to be epitactic with the substrate.The microstructure after laser re-solidification is closely related to the processing parameters,however, the relationship between microstructure and re-solidification conditions or processing parameters is not well understood and needs further study.In the present work,the microstructure of laser glazing solidified Ni-based single crystal DD8 was investigated by OM,SEM as well as TEM.The results show that the surface width of the melted pool becomes narrow with an increase of scanning rate, so the melted pool has a relatively high interface/volume ratio which leads to a higher cooling rate. The primary dendrite arm spacing decreases with an increase of cooling rate,and gradually reaches a minimum about only 3μm,which is two orders of magnitude smaller than that of the untreated part of alloy.EDXA shows that the dendritic segregation is not obvious and the chemical compositions tend to be homogeneous after re-solidification,which is caused by the higher solidification rate and related partition coefficients of alloying elements.The solidified structures are composed of the quasiplane front,cellular and fine dendrites from substrate to surface of melted pool.The structures in the regions of the quasi-plane front and cellular consist ofγ-solid solution and dispersiveγ' precipitates with about 20 nm in size.In the regions of the cellular-dendrite and the dendrite,however,there is a eutectic structure with a higher Ti content in the interdendrites.These eutectic structures are small in size and look like leaves.In the transition region,bothγandγ'-phases are not completely melted,and there are some dislocations distributed on the interfaces of theγ'-phase particles induced by thermal stress betweenγandγ' phases at higher cooling rate.The unmeltedγ' particles can act as nuclei of the second precipitatedγ' phases which have a size of about 10 nm and a pile-up-like morphology." @default.
• W2379131330 created "2016-06-24" @default.
• W2379131330 creator A5025050421 @default.
• W2379131330 creator A5056465813 @default.
• W2379131330 creator A5073158271 @default.
• W2379131330 creator A5073275285 @default.
• W2379131330 creator A5079442679 @default.
• W2379131330 date "2009-10-10" @default.
• W2379131330 modified "2023-09-28" @default.
• W2379131330 title "LASER GLAZING RAPIDLY SOLIDIFIED MICROSTRUCTURE OF DD8 SINGLE CRYSTAL Ni--BASED SUPERALLOY" @default.
• W2379131330 hasPublicationYear "2009" @default.
• W2379131330 type Work @default.
• W2379131330 sameAs 2379131330 @default.
• W2379131330 citedByCount "0" @default.
• W2379131330 crossrefType "journal-article" @default.
• W2379131330 hasAuthorship W2379131330A5025050421 @default.
• W2379131330 hasAuthorship W2379131330A5056465813 @default.
• W2379131330 hasAuthorship W2379131330A5073158271 @default.
• W2379131330 hasAuthorship W2379131330A5073275285 @default.
• W2379131330 hasAuthorship W2379131330A5079442679 @default.
• W2379131330 hasConcept C120665830 @default.
• W2379131330 hasConcept C121332964 @default.
• W2379131330 hasConcept C159985019 @default.
• W2379131330 hasConcept C16635281 @default.
• W2379131330 hasConcept C185592680 @default.
• W2379131330 hasConcept C191897082 @default.
• W2379131330 hasConcept C192562407 @default.
• W2379131330 hasConcept C199360897 @default.
• W2379131330 hasConcept C207055975 @default.
• W2379131330 hasConcept C2524010 @default.
• W2379131330 hasConcept C2780026712 @default.
• W2379131330 hasConcept C2781285689 @default.
• W2379131330 hasConcept C33923547 @default.
• W2379131330 hasConcept C41008148 @default.
• W2379131330 hasConcept C520434653 @default.
• W2379131330 hasConcept C53559285 @default.
• W2379131330 hasConcept C73922627 @default.
• W2379131330 hasConcept C8010536 @default.
• W2379131330 hasConcept C84248122 @default.
• W2379131330 hasConcept C87976508 @default.
• W2379131330 hasConceptScore W2379131330C120665830 @default.
• W2379131330 hasConceptScore W2379131330C121332964 @default.
• W2379131330 hasConceptScore W2379131330C159985019 @default.
• W2379131330 hasConceptScore W2379131330C16635281 @default.
• W2379131330 hasConceptScore W2379131330C185592680 @default.
• W2379131330 hasConceptScore W2379131330C191897082 @default.
• W2379131330 hasConceptScore W2379131330C192562407 @default.
• W2379131330 hasConceptScore W2379131330C199360897 @default.
• W2379131330 hasConceptScore W2379131330C207055975 @default.
• W2379131330 hasConceptScore W2379131330C2524010 @default.
• W2379131330 hasConceptScore W2379131330C2780026712 @default.
• W2379131330 hasConceptScore W2379131330C2781285689 @default.
• W2379131330 hasConceptScore W2379131330C33923547 @default.
• W2379131330 hasConceptScore W2379131330C41008148 @default.
• W2379131330 hasConceptScore W2379131330C520434653 @default.
• W2379131330 hasConceptScore W2379131330C53559285 @default.
• W2379131330 hasConceptScore W2379131330C73922627 @default.
• W2379131330 hasConceptScore W2379131330C8010536 @default.
• W2379131330 hasConceptScore W2379131330C84248122 @default.
• W2379131330 hasConceptScore W2379131330C87976508 @default.
• W2379131330 hasIssue "6" @default.
• W2379131330 hasOpenAccess W2379131330 @default.
• W2379131330 hasRelatedWork W1537417226 @default.
• W2379131330 hasRelatedWork W1996103019 @default.
• W2379131330 hasRelatedWork W2029884270 @default.
• W2379131330 hasRelatedWork W2050138751 @default.
• W2379131330 hasRelatedWork W2055375754 @default.
• W2379131330 hasRelatedWork W2071058634 @default.
• W2379131330 hasRelatedWork W2071985090 @default.
• W2379131330 hasRelatedWork W2300653410 @default.
• W2379131330 hasRelatedWork W2316182172 @default.
• W2379131330 hasRelatedWork W2381546724 @default.
• W2379131330 hasRelatedWork W2462951131 @default.
• W2379131330 hasRelatedWork W2554428490 @default.
• W2379131330 hasRelatedWork W2759175412 @default.
• W2379131330 hasRelatedWork W2790045953 @default.
• W2379131330 hasRelatedWork W2792934949 @default.
• W2379131330 hasRelatedWork W3025048475 @default.
• W2379131330 hasRelatedWork W3088910325 @default.
• W2379131330 hasRelatedWork W3129973602 @default.
• W2379131330 hasRelatedWork W3134916386 @default.
• W2379131330 hasRelatedWork W3151282743 @default.
• W2379131330 hasVolume "45" @default.
• W2379131330 isParatext "false" @default.
• W2379131330 isRetracted "false" @default.
• W2379131330 magId "2379131330" @default.
• W2379131330 workType "article" @default.