- W2379551451 abstract "Regenerated MgO-CaO brick samples with MgO contents of 75%were prepared using spent MgO-CaO bricks from AOD furnace and fused magnesite as raw materials.Their room temperature flexural strength and microstructure before and after thermal shock experiments were investigated,and the thermal shock resistance of regenerated MgO-CaO brick was evaluated subsequently.The results showed that there was no obvious change before and after thermal shock experiments for the bulk morphology of regenerated samples.The flexural strength of regenerated samples at room temperature was 35.80 MPa after 20 times thermal shock cycle,which was shown its higher mechanical property at room temperature,however,along with increased the times of thermal shock cycle,the flexural strengdi at room temperature was lightly decreased,the flexural strength loss ratio was increased,and furthermore lead to the decrease of the thermal shock resistance coefficient,and the linear relationship between the flexural strength and the times of thermal shock cycle were found.Because the internal cracks was generated in the regenerated samples and extended while shocked by the diermal stress,so diat the flexural strength at room temperature was gradually decreased." @default.
- W2379551451 created "2016-06-24" @default.
- W2379551451 creator A5045011785 @default.
- W2379551451 date "2014-01-01" @default.
- W2379551451 modified "2023-09-23" @default.
- W2379551451 title "Study on Thermal Shock Resistance of Regenerated MgO-CaO Brick" @default.
- W2379551451 hasPublicationYear "2014" @default.
- W2379551451 type Work @default.
- W2379551451 sameAs 2379551451 @default.
- W2379551451 citedByCount "0" @default.
- W2379551451 crossrefType "journal-article" @default.
- W2379551451 hasAuthorship W2379551451A5045011785 @default.
- W2379551451 hasConcept C154226666 @default.
- W2379551451 hasConcept C159985019 @default.
- W2379551451 hasConcept C176177977 @default.
- W2379551451 hasConcept C178405089 @default.
- W2379551451 hasConcept C192562407 @default.
- W2379551451 hasConcept C47463417 @default.
- W2379551451 hasConcept C87976508 @default.
- W2379551451 hasConceptScore W2379551451C154226666 @default.
- W2379551451 hasConceptScore W2379551451C159985019 @default.
- W2379551451 hasConceptScore W2379551451C176177977 @default.
- W2379551451 hasConceptScore W2379551451C178405089 @default.
- W2379551451 hasConceptScore W2379551451C192562407 @default.
- W2379551451 hasConceptScore W2379551451C47463417 @default.
- W2379551451 hasConceptScore W2379551451C87976508 @default.
- W2379551451 hasLocation W23795514511 @default.
- W2379551451 hasOpenAccess W2379551451 @default.
- W2379551451 hasPrimaryLocation W23795514511 @default.
- W2379551451 hasRelatedWork W1493265654 @default.
- W2379551451 hasRelatedWork W1979102327 @default.
- W2379551451 hasRelatedWork W2003148989 @default.
- W2379551451 hasRelatedWork W2007698206 @default.
- W2379551451 hasRelatedWork W2032911810 @default.
- W2379551451 hasRelatedWork W2051886638 @default.
- W2379551451 hasRelatedWork W2072628667 @default.
- W2379551451 hasRelatedWork W2113953794 @default.
- W2379551451 hasRelatedWork W2132931036 @default.
- W2379551451 hasRelatedWork W2318545402 @default.
- W2379551451 hasRelatedWork W2327502503 @default.
- W2379551451 hasRelatedWork W2356386564 @default.
- W2379551451 hasRelatedWork W2369194103 @default.
- W2379551451 hasRelatedWork W2373580295 @default.
- W2379551451 hasRelatedWork W2734692882 @default.
- W2379551451 hasRelatedWork W2908341647 @default.
- W2379551451 hasRelatedWork W2983553837 @default.
- W2379551451 hasRelatedWork W3188679686 @default.
- W2379551451 hasRelatedWork W571014939 @default.
- W2379551451 hasRelatedWork W1814216294 @default.
- W2379551451 isParatext "false" @default.
- W2379551451 isRetracted "false" @default.
- W2379551451 magId "2379551451" @default.
- W2379551451 workType "article" @default.