- W2380350683 abstract "Compared to fusion welding processes used in joining structural aluminum alloy, the friction stir welding(FSW)is an emerging solid state welding process which can lead to less distortion and residual stress owing to low heat input characteristic.In order to apply FSW in the aerospace field,the 2219 aluminum alloy in Al Cu series,which has high-strength-weight ratio,resistance to stress corrosion cracking and superior cryogenic properties,and is an ideal material in the construction of liquid cryogenic rocket fuel tanks,has been welded in O condition(full annealing). Microstructures of weld nugget zones and mechanical properties of the slices in the three kinds of thick plate FSW joints,which are the flaw-free joint,the joint with flaw and the flaw-free joint after post weld heat treatment(PWHT),were studied.The tensile testing shows that the tensile strengthσ_b and yield strengthσ_(0.2)decrease from 160.8 and 96.8 MPa of the top part of the flaw free joint to 146 and 86 MPa of the bottom part,respectively,σ_b andσ_(0.2)decrease from 132.9 and 94 MPa of the top part of the joint with flaw to 126 and 78.8 MPa of the bottom part,respectively.σ_b of the middle of the flaw-free joint after PWHT is 243.8 MPa andσ_(0.2)of the top of the flaw-free joint after PWHT is 123.3 MPa,they are higher than those of the other parts.δincreases from 6.7%,4.8%and 7.5%of the top parts of the flaw free joint,joint with flaw and flaw-free joint after PWHT to 10.1%,8.5%and 14%of the bottom parts of the joints,respectively.For the PWHT (500℃/50 min+160℃/20 h)flaw free joint,grains are more uniform and finer along the thickness direction in weld nugget zone,fractographs present deep dimples,most of the failure is ductile fracture,and the microhardness distribution has no obvious fluctuation.For the joint with flaw the mechanical properties decrease sharply,fractograph exhibits a ductile-brittle fracture morphology and the microhardnesses in slices are lower than those of the flaw-free joints." @default.
- W2380350683 created "2016-06-24" @default.
- W2380350683 creator A5000601777 @default.
- W2380350683 creator A5051557097 @default.
- W2380350683 creator A5052054327 @default.
- W2380350683 creator A5062590441 @default.
- W2380350683 date "2009-04-11" @default.
- W2380350683 modified "2023-09-23" @default.
- W2380350683 title "MICROSTRUCTURES AND MECHANICAL PROPERTIES OF FRICTION STIR WELDED JOINTS OF ALUMINIUM ALLOY THICK PLATE WITH DIFFERENT WELDING STATES" @default.
- W2380350683 hasPublicationYear "2009" @default.
- W2380350683 type Work @default.
- W2380350683 sameAs 2380350683 @default.
- W2380350683 citedByCount "1" @default.
- W2380350683 countsByYear W23803506832014 @default.
- W2380350683 crossrefType "journal-article" @default.
- W2380350683 hasAuthorship W2380350683A5000601777 @default.
- W2380350683 hasAuthorship W2380350683A5051557097 @default.
- W2380350683 hasAuthorship W2380350683A5052054327 @default.
- W2380350683 hasAuthorship W2380350683A5062590441 @default.
- W2380350683 hasConcept C112950240 @default.
- W2380350683 hasConcept C127413603 @default.
- W2380350683 hasConcept C159985019 @default.
- W2380350683 hasConcept C169312260 @default.
- W2380350683 hasConcept C18555067 @default.
- W2380350683 hasConcept C191897082 @default.
- W2380350683 hasConcept C192562407 @default.
- W2380350683 hasConcept C19474535 @default.
- W2380350683 hasConcept C2777855556 @default.
- W2380350683 hasConcept C2780026712 @default.
- W2380350683 hasConcept C37292000 @default.
- W2380350683 hasConcept C40367268 @default.
- W2380350683 hasConcept C66938386 @default.
- W2380350683 hasConcept C87976508 @default.
- W2380350683 hasConceptScore W2380350683C112950240 @default.
- W2380350683 hasConceptScore W2380350683C127413603 @default.
- W2380350683 hasConceptScore W2380350683C159985019 @default.
- W2380350683 hasConceptScore W2380350683C169312260 @default.
- W2380350683 hasConceptScore W2380350683C18555067 @default.
- W2380350683 hasConceptScore W2380350683C191897082 @default.
- W2380350683 hasConceptScore W2380350683C192562407 @default.
- W2380350683 hasConceptScore W2380350683C19474535 @default.
- W2380350683 hasConceptScore W2380350683C2777855556 @default.
- W2380350683 hasConceptScore W2380350683C2780026712 @default.
- W2380350683 hasConceptScore W2380350683C37292000 @default.
- W2380350683 hasConceptScore W2380350683C40367268 @default.
- W2380350683 hasConceptScore W2380350683C66938386 @default.
- W2380350683 hasConceptScore W2380350683C87976508 @default.
- W2380350683 hasIssue "4" @default.
- W2380350683 hasLocation W23803506831 @default.
- W2380350683 hasOpenAccess W2380350683 @default.
- W2380350683 hasPrimaryLocation W23803506831 @default.
- W2380350683 hasRelatedWork W2005718494 @default.
- W2380350683 hasRelatedWork W2034053233 @default.
- W2380350683 hasRelatedWork W2061904125 @default.
- W2380350683 hasRelatedWork W2094517300 @default.
- W2380350683 hasRelatedWork W2349396062 @default.
- W2380350683 hasRelatedWork W2350142523 @default.
- W2380350683 hasRelatedWork W2351941662 @default.
- W2380350683 hasRelatedWork W2357688449 @default.
- W2380350683 hasRelatedWork W2363919240 @default.
- W2380350683 hasRelatedWork W2364276760 @default.
- W2380350683 hasRelatedWork W2367384807 @default.
- W2380350683 hasRelatedWork W2375759498 @default.
- W2380350683 hasRelatedWork W2380313146 @default.
- W2380350683 hasRelatedWork W2380531737 @default.
- W2380350683 hasRelatedWork W2383750994 @default.
- W2380350683 hasRelatedWork W2397204296 @default.
- W2380350683 hasRelatedWork W2996393664 @default.
- W2380350683 hasRelatedWork W3010708663 @default.
- W2380350683 hasRelatedWork W3116839376 @default.
- W2380350683 hasRelatedWork W3206861315 @default.
- W2380350683 hasVolume "45" @default.
- W2380350683 isParatext "false" @default.
- W2380350683 isRetracted "false" @default.
- W2380350683 magId "2380350683" @default.
- W2380350683 workType "article" @default.