- W2380771841 abstract "Attempts are made on revealing the very-high cycle fatigue behavior and fatigue mechanism of high strength steels. GCr15 steel was used as testing material and rotating bending fatigue test was adopted. The fractography of fatigue failure was observed by optical microscopy and scanning electron microscopy. The observations shows that, for the number of cycles to fatigue failure between 10~6 and 4×10~8 cycles, fatigue cracks mostly initiated in the interior of specimen and originated at non-metallic inclusions. The results indicate that the fatigue life of specimens with crack origin at the interior of specimen is longer than that with crack origin at specimen surface. The experimental results and the fatigue mechanism were further analyzed in terms of fracture mechanics and fracture physics." @default.
- W2380771841 created "2016-06-24" @default.
- W2380771841 creator A5081832121 @default.
- W2380771841 date "2004-01-01" @default.
- W2380771841 modified "2023-09-25" @default.
- W2380771841 title "EXPERIMENTAL INVESTIGATION ON VERY-HIGH-CYCLE FATIGUE OF GCr15 STEEL" @default.
- W2380771841 hasPublicationYear "2004" @default.
- W2380771841 type Work @default.
- W2380771841 sameAs 2380771841 @default.
- W2380771841 citedByCount "0" @default.
- W2380771841 crossrefType "journal-article" @default.
- W2380771841 hasAuthorship W2380771841A5081832121 @default.
- W2380771841 hasConcept C131850400 @default.
- W2380771841 hasConcept C159985019 @default.
- W2380771841 hasConcept C191897082 @default.
- W2380771841 hasConcept C192562407 @default.
- W2380771841 hasConcept C26771246 @default.
- W2380771841 hasConcept C2985278600 @default.
- W2380771841 hasConcept C3018344627 @default.
- W2380771841 hasConcept C43369102 @default.
- W2380771841 hasConcept C45780264 @default.
- W2380771841 hasConcept C59085676 @default.
- W2380771841 hasConceptScore W2380771841C131850400 @default.
- W2380771841 hasConceptScore W2380771841C159985019 @default.
- W2380771841 hasConceptScore W2380771841C191897082 @default.
- W2380771841 hasConceptScore W2380771841C192562407 @default.
- W2380771841 hasConceptScore W2380771841C26771246 @default.
- W2380771841 hasConceptScore W2380771841C2985278600 @default.
- W2380771841 hasConceptScore W2380771841C3018344627 @default.
- W2380771841 hasConceptScore W2380771841C43369102 @default.
- W2380771841 hasConceptScore W2380771841C45780264 @default.
- W2380771841 hasConceptScore W2380771841C59085676 @default.
- W2380771841 hasLocation W23807718411 @default.
- W2380771841 hasOpenAccess W2380771841 @default.
- W2380771841 hasPrimaryLocation W23807718411 @default.
- W2380771841 hasRelatedWork W1584456716 @default.
- W2380771841 hasRelatedWork W1975677581 @default.
- W2380771841 hasRelatedWork W1984145311 @default.
- W2380771841 hasRelatedWork W1984164438 @default.
- W2380771841 hasRelatedWork W1984584006 @default.
- W2380771841 hasRelatedWork W1994432133 @default.
- W2380771841 hasRelatedWork W1997766939 @default.
- W2380771841 hasRelatedWork W2001368480 @default.
- W2380771841 hasRelatedWork W2057146555 @default.
- W2380771841 hasRelatedWork W2078106579 @default.
- W2380771841 hasRelatedWork W2152114482 @default.
- W2380771841 hasRelatedWork W2317501757 @default.
- W2380771841 hasRelatedWork W2348313199 @default.
- W2380771841 hasRelatedWork W2364594002 @default.
- W2380771841 hasRelatedWork W2380495834 @default.
- W2380771841 hasRelatedWork W2381397928 @default.
- W2380771841 hasRelatedWork W2387519411 @default.
- W2380771841 hasRelatedWork W2489846950 @default.
- W2380771841 hasRelatedWork W2889215482 @default.
- W2380771841 hasRelatedWork W3206087596 @default.
- W2380771841 isParatext "false" @default.
- W2380771841 isRetracted "false" @default.
- W2380771841 magId "2380771841" @default.
- W2380771841 workType "article" @default.