- W2381831025 abstract "The poly(cyanoarylether) was a new thermoplast being used as the basis of resin and engineering material in high property composite material.It exhibited high temperature stability,and resistance to radiation and to solvent attack.Crystalline ploy(cyanoarylether) could be prepared by the polycondensation of 2,6 difluorobenzonitrile with resorcinol at 200℃ in N methylpyrrolidone (with less water) in the presence of sodium carbonate.The reaction was affected by some conditions like temperature,polymer concentration and reaction time.A reaction temperature of at least 200℃ was necessary to attain high molecular weight polymer.Less water that was added in reaction mixture could improve reaction rate,and enhance molecular weight of the polymer.Spectral data indicated that the polymer had the structure of a poly(meta phenylene ether) with pendent nitrile.The glass transition temperature and the melting temperature of the polymer were examined to be 148℃ and 335℃ by turn.A cool crystalline exothermal peak appeared at 214 4℃.The decomposition temperature (loss weight 5%) and all weight loss by 900℃ of polymer were speculated from TG curve.The results showed the polymer had a fire resistance and aging resistance properties.The glass temperature and the melting temperature of the polymer were almost the same as the poly(ether ether ketone)(PEEK).The crystalline behaviour of the polymer was studied by X ray diffraction method.The degree of crystallization was 30 7%.The polymer had five evident diffraction peak,which indicated the polymer had better crystalline behaviour.The poly(cyanoarylether) exhibited also excellent solvent resistance compared with the corresponding phenolphthalein polymer.This showed the molecular structure would affect on the solubility of the polymers.The crystal structune of the polymer was discussed by comparing with that of the poly(ether ether ketone).The poly(cyanoarylether) was the same as poly(ether ether ketone) to be attributed to orthorhombic system.The space unit parameter were computed." @default.
- W2381831025 created "2016-06-24" @default.
- W2381831025 creator A5036097394 @default.
- W2381831025 date "1998-01-01" @default.
- W2381831025 modified "2023-09-23" @default.
- W2381831025 title "STUDIES ON THE STRUCTURE AND PROPERTIES OF POLY(CYANOARYLETHER)" @default.
- W2381831025 hasPublicationYear "1998" @default.
- W2381831025 type Work @default.
- W2381831025 sameAs 2381831025 @default.
- W2381831025 citedByCount "0" @default.
- W2381831025 crossrefType "journal-article" @default.
- W2381831025 hasAuthorship W2381831025A5036097394 @default.
- W2381831025 hasConcept C122865956 @default.
- W2381831025 hasConcept C127413603 @default.
- W2381831025 hasConcept C159985019 @default.
- W2381831025 hasConcept C178790620 @default.
- W2381831025 hasConcept C185592680 @default.
- W2381831025 hasConcept C188027245 @default.
- W2381831025 hasConcept C192562407 @default.
- W2381831025 hasConcept C203036418 @default.
- W2381831025 hasConcept C2780407432 @default.
- W2381831025 hasConcept C2780471494 @default.
- W2381831025 hasConcept C42360764 @default.
- W2381831025 hasConcept C521977710 @default.
- W2381831025 hasConcept C53033327 @default.
- W2381831025 hasConcept C7660682 @default.
- W2381831025 hasConceptScore W2381831025C122865956 @default.
- W2381831025 hasConceptScore W2381831025C127413603 @default.
- W2381831025 hasConceptScore W2381831025C159985019 @default.
- W2381831025 hasConceptScore W2381831025C178790620 @default.
- W2381831025 hasConceptScore W2381831025C185592680 @default.
- W2381831025 hasConceptScore W2381831025C188027245 @default.
- W2381831025 hasConceptScore W2381831025C192562407 @default.
- W2381831025 hasConceptScore W2381831025C203036418 @default.
- W2381831025 hasConceptScore W2381831025C2780407432 @default.
- W2381831025 hasConceptScore W2381831025C2780471494 @default.
- W2381831025 hasConceptScore W2381831025C42360764 @default.
- W2381831025 hasConceptScore W2381831025C521977710 @default.
- W2381831025 hasConceptScore W2381831025C53033327 @default.
- W2381831025 hasConceptScore W2381831025C7660682 @default.
- W2381831025 hasLocation W23818310251 @default.
- W2381831025 hasOpenAccess W2381831025 @default.
- W2381831025 hasPrimaryLocation W23818310251 @default.
- W2381831025 hasRelatedWork W137041975 @default.
- W2381831025 hasRelatedWork W1978074210 @default.
- W2381831025 hasRelatedWork W2018420105 @default.
- W2381831025 hasRelatedWork W2020702035 @default.
- W2381831025 hasRelatedWork W2032158199 @default.
- W2381831025 hasRelatedWork W2050814063 @default.
- W2381831025 hasRelatedWork W2070608307 @default.
- W2381831025 hasRelatedWork W2089843520 @default.
- W2381831025 hasRelatedWork W2167931338 @default.
- W2381831025 hasRelatedWork W2324084133 @default.
- W2381831025 hasRelatedWork W2331920139 @default.
- W2381831025 hasRelatedWork W2573413503 @default.
- W2381831025 hasRelatedWork W2950515858 @default.
- W2381831025 hasRelatedWork W2955382126 @default.
- W2381831025 hasRelatedWork W2979807411 @default.
- W2381831025 hasRelatedWork W3101423089 @default.
- W2381831025 hasRelatedWork W782207543 @default.
- W2381831025 hasRelatedWork W2834092581 @default.
- W2381831025 hasRelatedWork W2848865091 @default.
- W2381831025 hasRelatedWork W3141669619 @default.
- W2381831025 isParatext "false" @default.
- W2381831025 isRetracted "false" @default.
- W2381831025 magId "2381831025" @default.
- W2381831025 workType "article" @default.