- W2381936666 abstract "SiC coatings were prepared on carbon/carbon(C/C) composites by chemical vapor reaction(CVR) method.The structure and morphology of the coating were characterized by XRD,SEM and EDS analysis,and the influence of SiC coating and preparation technology on the fracture behavior of the composites were investigated by three point bending tests.The results show that the flexural strength and maximum fracture displacement of the composites are obvious improved after the coating process.The average flexural strength of carbon/carbon composites is 172.4MPa,while the average flexural strength of the coated composites is 239.8MPa.The improvement of the flexural strength is mainly contributed to the improved interface bonding caused by the vapor diffusion and reaction in the preparation process and the SiC particle reinforcement.Furthermore,the fracture mode of the coated composites is not changed and the coated samples also exhibit pseudo-plastic fracture and ductile frature character." @default.
- W2381936666 created "2016-06-24" @default.
- W2381936666 creator A5058904717 @default.
- W2381936666 date "2011-01-01" @default.
- W2381936666 modified "2023-09-25" @default.
- W2381936666 title "Influence of Chemical Vapor Reaction SiC Coating on Mechanical Properties of C/C Composites" @default.
- W2381936666 hasPublicationYear "2011" @default.
- W2381936666 type Work @default.
- W2381936666 sameAs 2381936666 @default.
- W2381936666 citedByCount "0" @default.
- W2381936666 crossrefType "journal-article" @default.
- W2381936666 hasAuthorship W2381936666A5058904717 @default.
- W2381936666 hasConcept C104779481 @default.
- W2381936666 hasConcept C140205800 @default.
- W2381936666 hasConcept C159985019 @default.
- W2381936666 hasConcept C178405089 @default.
- W2381936666 hasConcept C192562407 @default.
- W2381936666 hasConcept C2781448156 @default.
- W2381936666 hasConcept C43369102 @default.
- W2381936666 hasConcept C86060186 @default.
- W2381936666 hasConceptScore W2381936666C104779481 @default.
- W2381936666 hasConceptScore W2381936666C140205800 @default.
- W2381936666 hasConceptScore W2381936666C159985019 @default.
- W2381936666 hasConceptScore W2381936666C178405089 @default.
- W2381936666 hasConceptScore W2381936666C192562407 @default.
- W2381936666 hasConceptScore W2381936666C2781448156 @default.
- W2381936666 hasConceptScore W2381936666C43369102 @default.
- W2381936666 hasConceptScore W2381936666C86060186 @default.
- W2381936666 hasLocation W23819366661 @default.
- W2381936666 hasOpenAccess W2381936666 @default.
- W2381936666 hasPrimaryLocation W23819366661 @default.
- W2381936666 hasRelatedWork W1984250251 @default.
- W2381936666 hasRelatedWork W2016587109 @default.
- W2381936666 hasRelatedWork W2022000720 @default.
- W2381936666 hasRelatedWork W2028012202 @default.
- W2381936666 hasRelatedWork W2084975826 @default.
- W2381936666 hasRelatedWork W2154200768 @default.
- W2381936666 hasRelatedWork W224051635 @default.
- W2381936666 hasRelatedWork W2351902186 @default.
- W2381936666 hasRelatedWork W2351969958 @default.
- W2381936666 hasRelatedWork W2353125716 @default.
- W2381936666 hasRelatedWork W2360754178 @default.
- W2381936666 hasRelatedWork W2370073508 @default.
- W2381936666 hasRelatedWork W2371766255 @default.
- W2381936666 hasRelatedWork W2474976532 @default.
- W2381936666 hasRelatedWork W2507906931 @default.
- W2381936666 hasRelatedWork W2522398270 @default.
- W2381936666 hasRelatedWork W2561944945 @default.
- W2381936666 hasRelatedWork W2757134013 @default.
- W2381936666 hasRelatedWork W2808448174 @default.
- W2381936666 hasRelatedWork W77280061 @default.
- W2381936666 isParatext "false" @default.
- W2381936666 isRetracted "false" @default.
- W2381936666 magId "2381936666" @default.
- W2381936666 workType "article" @default.