- W2385841348 abstract "The different systems of heat treatment experiments for 2000 grade maraging steel,such as solid solution and aging and so on were carried out.At the same time,the microhardness was tested and the microstructure was analyzed.The results show that:with the solution temperature increasing from 700 ℃ to 850 ℃,the microhardness decreases sharply,as the temperature continues to rise,little change in microhardness.Microstructure fully austenitic after 830 ℃×15 min solid solution.Under the conditions of solution at 830 ℃,with the extends of holding time to 90 min,the microhardness maintains at 320-325 HV.The peak aging temperature is 480 ℃." @default.
- W2385841348 created "2016-06-24" @default.
- W2385841348 creator A5058374613 @default.
- W2385841348 date "2012-01-01" @default.
- W2385841348 modified "2023-09-24" @default.
- W2385841348 title "Effect of Heat Treatment on Structure and Hardness of Spinning States 2000 MPa Grade Maraging Steel" @default.
- W2385841348 hasPublicationYear "2012" @default.
- W2385841348 type Work @default.
- W2385841348 sameAs 2385841348 @default.
- W2385841348 citedByCount "0" @default.
- W2385841348 crossrefType "journal-article" @default.
- W2385841348 hasAuthorship W2385841348A5058374613 @default.
- W2385841348 hasConcept C154815118 @default.
- W2385841348 hasConcept C159985019 @default.
- W2385841348 hasConcept C165720898 @default.
- W2385841348 hasConcept C191897082 @default.
- W2385841348 hasConcept C192562407 @default.
- W2385841348 hasConcept C2779857867 @default.
- W2385841348 hasConcept C87976508 @default.
- W2385841348 hasConcept C96288455 @default.
- W2385841348 hasConceptScore W2385841348C154815118 @default.
- W2385841348 hasConceptScore W2385841348C159985019 @default.
- W2385841348 hasConceptScore W2385841348C165720898 @default.
- W2385841348 hasConceptScore W2385841348C191897082 @default.
- W2385841348 hasConceptScore W2385841348C192562407 @default.
- W2385841348 hasConceptScore W2385841348C2779857867 @default.
- W2385841348 hasConceptScore W2385841348C87976508 @default.
- W2385841348 hasConceptScore W2385841348C96288455 @default.
- W2385841348 hasLocation W23858413481 @default.
- W2385841348 hasOpenAccess W2385841348 @default.
- W2385841348 hasPrimaryLocation W23858413481 @default.
- W2385841348 hasRelatedWork W1849246950 @default.
- W2385841348 hasRelatedWork W2348503372 @default.
- W2385841348 hasRelatedWork W2354021106 @default.
- W2385841348 hasRelatedWork W2355734387 @default.
- W2385841348 hasRelatedWork W2355987569 @default.
- W2385841348 hasRelatedWork W2356263182 @default.
- W2385841348 hasRelatedWork W2364437033 @default.
- W2385841348 hasRelatedWork W2367666683 @default.
- W2385841348 hasRelatedWork W2372341855 @default.
- W2385841348 hasRelatedWork W2372727692 @default.
- W2385841348 hasRelatedWork W2373498506 @default.
- W2385841348 hasRelatedWork W2378047731 @default.
- W2385841348 hasRelatedWork W2378318380 @default.
- W2385841348 hasRelatedWork W2378954681 @default.
- W2385841348 hasRelatedWork W2379155530 @default.
- W2385841348 hasRelatedWork W2379297438 @default.
- W2385841348 hasRelatedWork W2380793621 @default.
- W2385841348 hasRelatedWork W2389111581 @default.
- W2385841348 hasRelatedWork W2597066521 @default.
- W2385841348 hasRelatedWork W2735687111 @default.
- W2385841348 isParatext "false" @default.
- W2385841348 isRetracted "false" @default.
- W2385841348 magId "2385841348" @default.
- W2385841348 workType "article" @default.