- W2392152087 abstract "In-situ neutron diffraction has been employed to examine the effect of strain path on lattice strain evolution during monotonic and cyclic tension in an extruded Mg-8.5wt.%Al alloy. In the cyclic tension test, the maximum applied stress increased with cycle number. Lattice strain data were acquired for three grain orientations, characterized by the plane normal to the stress axis. The lattice strain in the hard {10.0} orientation, which is unfavorably oriented for both basal slip and {10.2} extension twinning, evolved linearly throughout both tests during loading and unloading. The {00.2} orientation exhibited significant relaxation associated with {10.2} extension twinning. Coupled with a linear lattice strain unloading behavior, this relaxation led to increasingly compressive residual strains in the {00.2} orientation with increasing cycle number. The {10.1} orientation is favorably oriented for basal slip, and thus showed a soft grain behavior. Microyielding occurred in the monotonic tension test and in all cycles of the cyclic test at an applied stress of ~50 MPa, indicating that strain hardening in this orientation was not completely stable from one cycle to the next. The lattice strain unloading behavior was linear in the {10.1} orientation, leading to a compressive residual strain after every cycle, which, however, did not increase systematically from one cycle to the next as in the {00.2} orientation." @default.
- W2392152087 created "2016-06-24" @default.
- W2392152087 creator A5037447625 @default.
- W2392152087 creator A5042181210 @default.
- W2392152087 creator A5051750356 @default.
- W2392152087 date "2015-05-01" @default.
- W2392152087 modified "2023-09-30" @default.
- W2392152087 title "Effect of Strain Path on Lattice Strain Evolution during Monotonic and Cyclic Tension of Magnesium Alloy" @default.
- W2392152087 cites W1984412060 @default.
- W2392152087 cites W1993232970 @default.
- W2392152087 cites W1996016885 @default.
- W2392152087 cites W2001771132 @default.
- W2392152087 cites W2019759475 @default.
- W2392152087 cites W2030644878 @default.
- W2392152087 cites W2035891324 @default.
- W2392152087 cites W2052641043 @default.
- W2392152087 cites W2063970767 @default.
- W2392152087 cites W2067374255 @default.
- W2392152087 cites W2069118835 @default.
- W2392152087 cites W2078087162 @default.
- W2392152087 cites W2085080678 @default.
- W2392152087 cites W2092263132 @default.
- W2392152087 cites W2094907091 @default.
- W2392152087 cites W4231016564 @default.
- W2392152087 doi "https://doi.org/10.3740/mrsk.2015.25.5.221" @default.
- W2392152087 hasPublicationYear "2015" @default.
- W2392152087 type Work @default.
- W2392152087 sameAs 2392152087 @default.
- W2392152087 citedByCount "0" @default.
- W2392152087 crossrefType "journal-article" @default.
- W2392152087 hasAuthorship W2392152087A5037447625 @default.
- W2392152087 hasAuthorship W2392152087A5042181210 @default.
- W2392152087 hasAuthorship W2392152087A5051750356 @default.
- W2392152087 hasBestOaLocation W23921520871 @default.
- W2392152087 hasConcept C121332964 @default.
- W2392152087 hasConcept C126322002 @default.
- W2392152087 hasConcept C134306372 @default.
- W2392152087 hasConcept C159985019 @default.
- W2392152087 hasConcept C191897082 @default.
- W2392152087 hasConcept C192562407 @default.
- W2392152087 hasConcept C24890656 @default.
- W2392152087 hasConcept C2776797782 @default.
- W2392152087 hasConcept C2778022156 @default.
- W2392152087 hasConcept C2780026712 @default.
- W2392152087 hasConcept C2781204021 @default.
- W2392152087 hasConcept C33923547 @default.
- W2392152087 hasConcept C543218039 @default.
- W2392152087 hasConcept C71924100 @default.
- W2392152087 hasConcept C72169020 @default.
- W2392152087 hasConceptScore W2392152087C121332964 @default.
- W2392152087 hasConceptScore W2392152087C126322002 @default.
- W2392152087 hasConceptScore W2392152087C134306372 @default.
- W2392152087 hasConceptScore W2392152087C159985019 @default.
- W2392152087 hasConceptScore W2392152087C191897082 @default.
- W2392152087 hasConceptScore W2392152087C192562407 @default.
- W2392152087 hasConceptScore W2392152087C24890656 @default.
- W2392152087 hasConceptScore W2392152087C2776797782 @default.
- W2392152087 hasConceptScore W2392152087C2778022156 @default.
- W2392152087 hasConceptScore W2392152087C2780026712 @default.
- W2392152087 hasConceptScore W2392152087C2781204021 @default.
- W2392152087 hasConceptScore W2392152087C33923547 @default.
- W2392152087 hasConceptScore W2392152087C543218039 @default.
- W2392152087 hasConceptScore W2392152087C71924100 @default.
- W2392152087 hasConceptScore W2392152087C72169020 @default.
- W2392152087 hasFunder F4320321204 @default.
- W2392152087 hasIssue "5" @default.
- W2392152087 hasLocation W23921520871 @default.
- W2392152087 hasOpenAccess W2392152087 @default.
- W2392152087 hasPrimaryLocation W23921520871 @default.
- W2392152087 hasRelatedWork W1974077162 @default.
- W2392152087 hasRelatedWork W1999962534 @default.
- W2392152087 hasRelatedWork W2076761015 @default.
- W2392152087 hasRelatedWork W2079226407 @default.
- W2392152087 hasRelatedWork W2119062422 @default.
- W2392152087 hasRelatedWork W2381903024 @default.
- W2392152087 hasRelatedWork W2387193083 @default.
- W2392152087 hasRelatedWork W3100694364 @default.
- W2392152087 hasRelatedWork W4241038428 @default.
- W2392152087 hasRelatedWork W4320002253 @default.
- W2392152087 hasVolume "25" @default.
- W2392152087 isParatext "false" @default.
- W2392152087 isRetracted "false" @default.
- W2392152087 magId "2392152087" @default.
- W2392152087 workType "article" @default.