• W2409788345 abstract "Ce1–xLaxOy solid solution was simply prepared using mixed rare earth chloride (RECl3·xH2O, RE=Ce, La>99%, containing unseparated Ce and La from rare earth metallurgical industry) as precursor by ultrasonic-assisted co-precipitation method with different ultrasonic frequencies (CLf, f=200, 400, 600, 800, 1000 Hz). A compared Ce1–xLaxOy solid solution (CL*) was also prepared by the same mothod with 10% less precipitant. X-ray diffraction results confirmed the formation of Ce1–xLaxOy solid solution, and the crystal structures of these catalysts were not very sensitive to ultrasonic frequency and precipitant amount. However, both of the factors had obvious effect on morphology and surface area of CL, and precipitant amount seem to play a more crucial role than ultrasonic frequency for Ce1–xLaxOy solid solution preparation. When soot and catalyst were tight contacted, the peak temperature (Tpeak) of soot oxidation and oxygen reducing temperature for CLf catalysts decreased linearly with increasing surface area. Under loose contact condition, the Tpeak had obvious negative correlation with H2 consumption. It was inferred that good reducibility of the Ce1–xLaxOy solid solution favored the soot oxidation reaction. The Ce1–xLaxOy solid solution prepared from unseparated rare earth chloride showed a good soot oxidaiton activity. Controlling the preparation conditions to prepare a CL catalyst would high surface area will enhance its reducibility and activity." @default.
• W2409788345 created "2016-06-24" @default.
• W2409788345 creator A5014211227 @default.
• W2409788345 creator A5027659438 @default.
• W2409788345 creator A5029459478 @default.
• W2409788345 creator A5044957624 @default.
• W2409788345 creator A5045599802 @default.
• W2409788345 creator A5055420452 @default.
• W2409788345 date "2016-06-01" @default.
• W2409788345 modified "2023-10-14" @default.
• W2409788345 title "Ce1–xLaxOy solid solution prepared from mixed rare earth chloride for soot oxidation" @default.
• W2409788345 cites W1966038796 @default.
• W2409788345 cites W1967834823 @default.
• W2409788345 cites W1989824799 @default.
• W2409788345 cites W1999532106 @default.
• W2409788345 cites W2005908262 @default.
• W2409788345 cites W2006017151 @default.
• W2409788345 cites W2022367101 @default.
• W2409788345 cites W2032235714 @default.
• W2409788345 cites W2035477291 @default.
• W2409788345 cites W2043229327 @default.
• W2409788345 cites W2045915970 @default.
• W2409788345 cites W2057391312 @default.
• W2409788345 cites W2058916377 @default.
• W2409788345 cites W2058917222 @default.
• W2409788345 cites W2059102845 @default.
• W2409788345 cites W2064970542 @default.
• W2409788345 cites W2070171202 @default.
• W2409788345 cites W2074159788 @default.
• W2409788345 cites W2075592396 @default.
• W2409788345 cites W2077456755 @default.
• W2409788345 cites W2078656830 @default.
• W2409788345 cites W2091238868 @default.
• W2409788345 cites W2092558010 @default.
• W2409788345 cites W2096872425 @default.
• W2409788345 cites W2118471499 @default.
• W2409788345 cites W2131885341 @default.
• W2409788345 cites W2135888801 @default.
• W2409788345 cites W2162082462 @default.
• W2409788345 cites W2163700499 @default.
• W2409788345 cites W2323835733 @default.
• W2409788345 cites W4254297059 @default.
• W2409788345 doi "https://doi.org/10.1016/s1002-0721(16)60066-2" @default.
• W2409788345 hasPublicationYear "2016" @default.
• W2409788345 type Work @default.
• W2409788345 sameAs 2409788345 @default.
• W2409788345 citedByCount "16" @default.
• W2409788345 countsByYear W24097883452017 @default.
• W2409788345 countsByYear W24097883452018 @default.
• W2409788345 countsByYear W24097883452019 @default.
• W2409788345 countsByYear W24097883452020 @default.
• W2409788345 countsByYear W24097883452021 @default.
• W2409788345 countsByYear W24097883452022 @default.
• W2409788345 crossrefType "journal-article" @default.
• W2409788345 hasAuthorship W2409788345A5014211227 @default.
• W2409788345 hasAuthorship W2409788345A5027659438 @default.
• W2409788345 hasAuthorship W2409788345A5029459478 @default.
• W2409788345 hasAuthorship W2409788345A5044957624 @default.
• W2409788345 hasAuthorship W2409788345A5045599802 @default.
• W2409788345 hasAuthorship W2409788345A5055420452 @default.
• W2409788345 hasConcept C105923489 @default.
• W2409788345 hasConcept C107054158 @default.
• W2409788345 hasConcept C121332964 @default.
• W2409788345 hasConcept C138999460 @default.
• W2409788345 hasConcept C147789679 @default.
• W2409788345 hasConcept C153294291 @default.
• W2409788345 hasConcept C161790260 @default.
• W2409788345 hasConcept C178790620 @default.
• W2409788345 hasConcept C179104552 @default.
• W2409788345 hasConcept C184651966 @default.
• W2409788345 hasConcept C185592680 @default.
• W2409788345 hasConcept C192562407 @default.
• W2409788345 hasConcept C2775925408 @default.
• W2409788345 hasConcept C2778695967 @default.
• W2409788345 hasConceptScore W2409788345C105923489 @default.
• W2409788345 hasConceptScore W2409788345C107054158 @default.
• W2409788345 hasConceptScore W2409788345C121332964 @default.
• W2409788345 hasConceptScore W2409788345C138999460 @default.
• W2409788345 hasConceptScore W2409788345C147789679 @default.
• W2409788345 hasConceptScore W2409788345C153294291 @default.
• W2409788345 hasConceptScore W2409788345C161790260 @default.
• W2409788345 hasConceptScore W2409788345C178790620 @default.
• W2409788345 hasConceptScore W2409788345C179104552 @default.
• W2409788345 hasConceptScore W2409788345C184651966 @default.
• W2409788345 hasConceptScore W2409788345C185592680 @default.
• W2409788345 hasConceptScore W2409788345C192562407 @default.
• W2409788345 hasConceptScore W2409788345C2775925408 @default.
• W2409788345 hasConceptScore W2409788345C2778695967 @default.
• W2409788345 hasIssue "6" @default.
• W2409788345 hasLocation W24097883451 @default.
• W2409788345 hasOpenAccess W2409788345 @default.
• W2409788345 hasPrimaryLocation W24097883451 @default.
• W2409788345 hasRelatedWork W2000224375 @default.
• W2409788345 hasRelatedWork W2007985994 @default.
• W2409788345 hasRelatedWork W2036110988 @default.
• W2409788345 hasRelatedWork W2053430995 @default.
• W2409788345 hasRelatedWork W2083173333 @default.
• W2409788345 hasRelatedWork W2090829759 @default.

• next