- W2418446670 abstract "Excessive etching of the dentin may decrease bond strength because the adhesive may fail to completely infiltrate to the base of the over-etched demineralized collagen network. The purpose of the present study was to evaluate the influence of increasing etching times on the microtensile bond strength of Single Bond and the leakage of silver ions within the hybrid layer. After etching occlusal dentin for 15, 30, or 60 seconds with 35% phosphoric acid gel, Single Bond was applied and cured for 10 seconds. Z100 was added and cured for 60 seconds. After 24 hours of water immersion, the teeth were sectioned into slices 0.7 mm thick, and hour-glass-shaped specimens were prepared. Alternate slices were either dried for 30 minutes in air, kept wet, or they were coated with fingernail varnish except for 0.5 mm around the bonded area. Only the varnished samples were then stained with 50% AgNO3. Microtensile bond strength was tested using a Vitrodyne V-1000 universal tester. The samples of the stained group were embedded in self-curing PMMA and polished. All samples were observed with an SEM. Nanoleakage of silver ions was measured by exposure to laser ablation with an inductively connected plasma mass spectrometer and by electron dispersive elemental analysis. Increasing etching times seemed to have a negligible effect on bond strength of Single Bond, producing an average value of ca 38 MPa. However, the silver uptake increased upon prolonged etching times. Short-term results suggest that overetching has no detrimental effect on bond strength values of Single Bond. However, increased silver uptake, depending on the etching time, raises concern about the long-term stability of the bond." @default.
- W2418446670 created "2016-06-24" @default.
- W2418446670 creator A5005960925 @default.
- W2418446670 creator A5009262046 @default.
- W2418446670 creator A5036340283 @default.
- W2418446670 creator A5068908664 @default.
- W2418446670 date "1999-10-26" @default.
- W2418446670 modified "2023-09-26" @default.
- W2418446670 title "Nanoleakage at the dentin adhesive interface vs microtensile bond strength." @default.
- W2418446670 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/10530280" @default.
- W2418446670 hasPublicationYear "1999" @default.
- W2418446670 type Work @default.
- W2418446670 sameAs 2418446670 @default.
- W2418446670 citedByCount "44" @default.
- W2418446670 countsByYear W24184466702012 @default.
- W2418446670 countsByYear W24184466702013 @default.
- W2418446670 countsByYear W24184466702015 @default.
- W2418446670 countsByYear W24184466702023 @default.
- W2418446670 crossrefType "journal-article" @default.
- W2418446670 hasAuthorship W2418446670A5005960925 @default.
- W2418446670 hasAuthorship W2418446670A5009262046 @default.
- W2418446670 hasAuthorship W2418446670A5036340283 @default.
- W2418446670 hasAuthorship W2418446670A5068908664 @default.
- W2418446670 hasConcept C108797602 @default.
- W2418446670 hasConcept C112950240 @default.
- W2418446670 hasConcept C159096172 @default.
- W2418446670 hasConcept C159985019 @default.
- W2418446670 hasConcept C178790620 @default.
- W2418446670 hasConcept C185592680 @default.
- W2418446670 hasConcept C191897082 @default.
- W2418446670 hasConcept C192562407 @default.
- W2418446670 hasConcept C26771246 @default.
- W2418446670 hasConcept C2776622989 @default.
- W2418446670 hasConcept C2778265030 @default.
- W2418446670 hasConcept C2778492126 @default.
- W2418446670 hasConcept C2779227376 @default.
- W2418446670 hasConcept C2779263046 @default.
- W2418446670 hasConcept C2780263894 @default.
- W2418446670 hasConcept C2781448156 @default.
- W2418446670 hasConcept C28667232 @default.
- W2418446670 hasConcept C68928338 @default.
- W2418446670 hasConceptScore W2418446670C108797602 @default.
- W2418446670 hasConceptScore W2418446670C112950240 @default.
- W2418446670 hasConceptScore W2418446670C159096172 @default.
- W2418446670 hasConceptScore W2418446670C159985019 @default.
- W2418446670 hasConceptScore W2418446670C178790620 @default.
- W2418446670 hasConceptScore W2418446670C185592680 @default.
- W2418446670 hasConceptScore W2418446670C191897082 @default.
- W2418446670 hasConceptScore W2418446670C192562407 @default.
- W2418446670 hasConceptScore W2418446670C26771246 @default.
- W2418446670 hasConceptScore W2418446670C2776622989 @default.
- W2418446670 hasConceptScore W2418446670C2778265030 @default.
- W2418446670 hasConceptScore W2418446670C2778492126 @default.
- W2418446670 hasConceptScore W2418446670C2779227376 @default.
- W2418446670 hasConceptScore W2418446670C2779263046 @default.
- W2418446670 hasConceptScore W2418446670C2780263894 @default.
- W2418446670 hasConceptScore W2418446670C2781448156 @default.
- W2418446670 hasConceptScore W2418446670C28667232 @default.
- W2418446670 hasConceptScore W2418446670C68928338 @default.
- W2418446670 hasIssue "3" @default.
- W2418446670 hasLocation W24184466701 @default.
- W2418446670 hasOpenAccess W2418446670 @default.
- W2418446670 hasPrimaryLocation W24184466701 @default.
- W2418446670 hasRelatedWork W1567517527 @default.
- W2418446670 hasRelatedWork W189479796 @default.
- W2418446670 hasRelatedWork W2005808179 @default.
- W2418446670 hasRelatedWork W2032899436 @default.
- W2418446670 hasRelatedWork W2065786852 @default.
- W2418446670 hasRelatedWork W2126478894 @default.
- W2418446670 hasRelatedWork W2339122017 @default.
- W2418446670 hasRelatedWork W2400225269 @default.
- W2418446670 hasRelatedWork W2418446670 @default.
- W2418446670 hasRelatedWork W140923395 @default.
- W2418446670 hasVolume "24" @default.
- W2418446670 isParatext "false" @default.
- W2418446670 isRetracted "false" @default.
- W2418446670 magId "2418446670" @default.
- W2418446670 workType "article" @default.