- W2426471182 abstract "To evaluate the effect of different acid etching modes on bond strength between composite resin and non-carious sclerotic dentin, and to provide references for clinical application.Thirty premolars with naturally-occurring non-carious cervical lesions were divided into 2 groups based on self-etch adhesive system AdperTM Easy one (AEO) and total-etch adhesive system AdperTM Single Bond2 (ASB2). Each group was further divided into 3 subgroups (ASB21, ASB22, ASB23, AEO1, AEO2, AEO3) and subjected to the following processing: ASB21 subgroup was etched for 15 s with 35% phosphoric acid and coated with binder for 15 s; ASB22 subgroup was etched for 30 s with 35% phosphoric acid and coated with binder for 15 s; ASB23 subgroup was etched for 15 s with 35% phosphoric acid and coated with binder for 30 s; AEO1 subgroup was only etched with binder for 20 s; AEO2 subgroup was etched with binder for 40 s; AEO3 subgroup was etched for 15 s with 35% phosphoric acid and coated with binder for 20 s. The samples were restored with composite resin; 24 h after saved in distilled water at room temperature, the teeth were cut into dumbbell-shaped specimens with surface areas of approximately 1.0 mm2. The microtensile bond strength (μTBS) was detected and evaluated by one-way ANOVA and SNK-q test using SPSS 17.0 software package.μTBS was given in MPa: AEO3>ASB22>ASB23>ASB21>AEO2>AEO1, AEO3 resulted in statistically highest bond strength and AEO1 had the lowest bond strength (P<0.05), ASB22 acquired bond strength just lower than AEO3 (P<0.05).Use of total-etch adhesive system increasing the etching time of phosphoric time can enhance bond strength. For self-etch adhesive system,both duplicated the time of adhesive treatment and use of phosphoric acid can improve the bond strength. Use of phosphoric acid to etch for 15 s and coated with self-etch adhesive system for 20 s achieved the highest bond strength. In either self-etch or total-etch adhesive system, use of phosphoric acid to etch for 15 s and coated with self-etch adhesive system for 20 s achieved optimal bond strength, there was the lowest bond strength when the self-etch adhesive system used as recommended time." @default.
- W2426471182 created "2016-06-24" @default.
- W2426471182 creator A5052311006 @default.
- W2426471182 creator A5053632548 @default.
- W2426471182 creator A5089773076 @default.
- W2426471182 date "2016-02-01" @default.
- W2426471182 modified "2023-09-23" @default.
- W2426471182 title "[Influence of different acid etching modes on bond strengths to non-carious sclerotic dentin]." @default.
- W2426471182 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/27063306" @default.
- W2426471182 hasPublicationYear "2016" @default.
- W2426471182 type Work @default.
- W2426471182 sameAs 2426471182 @default.
- W2426471182 citedByCount "0" @default.
- W2426471182 crossrefType "journal-article" @default.
- W2426471182 hasAuthorship W2426471182A5052311006 @default.
- W2426471182 hasAuthorship W2426471182A5053632548 @default.
- W2426471182 hasAuthorship W2426471182A5089773076 @default.
- W2426471182 hasConcept C104779481 @default.
- W2426471182 hasConcept C108797602 @default.
- W2426471182 hasConcept C159096172 @default.
- W2426471182 hasConcept C159985019 @default.
- W2426471182 hasConcept C178790620 @default.
- W2426471182 hasConcept C185592680 @default.
- W2426471182 hasConcept C191897082 @default.
- W2426471182 hasConcept C192562407 @default.
- W2426471182 hasConcept C199343813 @default.
- W2426471182 hasConcept C2776622989 @default.
- W2426471182 hasConcept C2778265030 @default.
- W2426471182 hasConcept C2779227376 @default.
- W2426471182 hasConcept C2779263046 @default.
- W2426471182 hasConcept C2779429693 @default.
- W2426471182 hasConcept C2781311116 @default.
- W2426471182 hasConcept C43617362 @default.
- W2426471182 hasConcept C68928338 @default.
- W2426471182 hasConcept C71924100 @default.
- W2426471182 hasConceptScore W2426471182C104779481 @default.
- W2426471182 hasConceptScore W2426471182C108797602 @default.
- W2426471182 hasConceptScore W2426471182C159096172 @default.
- W2426471182 hasConceptScore W2426471182C159985019 @default.
- W2426471182 hasConceptScore W2426471182C178790620 @default.
- W2426471182 hasConceptScore W2426471182C185592680 @default.
- W2426471182 hasConceptScore W2426471182C191897082 @default.
- W2426471182 hasConceptScore W2426471182C192562407 @default.
- W2426471182 hasConceptScore W2426471182C199343813 @default.
- W2426471182 hasConceptScore W2426471182C2776622989 @default.
- W2426471182 hasConceptScore W2426471182C2778265030 @default.
- W2426471182 hasConceptScore W2426471182C2779227376 @default.
- W2426471182 hasConceptScore W2426471182C2779263046 @default.
- W2426471182 hasConceptScore W2426471182C2779429693 @default.
- W2426471182 hasConceptScore W2426471182C2781311116 @default.
- W2426471182 hasConceptScore W2426471182C43617362 @default.
- W2426471182 hasConceptScore W2426471182C68928338 @default.
- W2426471182 hasConceptScore W2426471182C71924100 @default.
- W2426471182 hasIssue "1" @default.
- W2426471182 hasLocation W24264711821 @default.
- W2426471182 hasOpenAccess W2426471182 @default.
- W2426471182 hasPrimaryLocation W24264711821 @default.
- W2426471182 hasRelatedWork W176632087 @default.
- W2426471182 hasRelatedWork W2003796239 @default.
- W2426471182 hasRelatedWork W2011554265 @default.
- W2426471182 hasRelatedWork W2018021436 @default.
- W2426471182 hasRelatedWork W2082575746 @default.
- W2426471182 hasRelatedWork W2116125112 @default.
- W2426471182 hasRelatedWork W2154749455 @default.
- W2426471182 hasRelatedWork W2180424360 @default.
- W2426471182 hasRelatedWork W2288180884 @default.
- W2426471182 hasRelatedWork W2390736332 @default.
- W2426471182 hasRelatedWork W2409772322 @default.
- W2426471182 hasRelatedWork W2423578713 @default.
- W2426471182 hasRelatedWork W2525013943 @default.
- W2426471182 hasRelatedWork W2624698530 @default.
- W2426471182 hasRelatedWork W2762409934 @default.
- W2426471182 hasRelatedWork W2805669196 @default.
- W2426471182 hasRelatedWork W2994492276 @default.
- W2426471182 hasRelatedWork W3013968057 @default.
- W2426471182 hasRelatedWork W3075399205 @default.
- W2426471182 hasRelatedWork W180386450 @default.
- W2426471182 hasVolume "25" @default.
- W2426471182 isParatext "false" @default.
- W2426471182 isRetracted "false" @default.
- W2426471182 magId "2426471182" @default.
- W2426471182 workType "article" @default.