• W2464038215 abstract "A PG 76-22 Polymer Modified Asphalt Cement composition was subjected in the laboratory to accelerated aging using both a standard Thin Film Oven Test and a Pressure Aging Vessel. Conditions simulating wet atmospheres (PAV in saturated water vapors) as well as very long service terms (multiple dry and wet PAV operations) were studied. A Rotating Cylinder Aging Test has been employed as an alternate asphalt aging technique using the same PMAC composition in order to observe the initial phases of the oxidative aging process. The data provided by this technique was correlated with the actual aging in the field of asphalt pavements. The extent of oxidation and changes in the molecular mass of the asphalt cement components of aged samples were estimated using Fourier Transform Infrared Spectroscopy data, Potentiometric Titrations and Gel Permeation Chromatography analyses. FTIR data show that multiple PAV and RCAT aging introduced polar carboxylic acid oxygen species. PT analysis identified the presence of sulfonic acids in commercial PMACs, apparently derived from sulfur used in preparing the blends. GPC data show that even after extensive RCAT aging the polymer did not degrade significantly. In contrast, the polymer is rapidly crosslinked or degraded by PAV or field aging. In order to obtain a better understanding of the role of radicals during oxidative processes both under dry and wet conditions, the chemical impact of aging of PMAC components has been modeled using a cobalt naphthenate/cumene hydroperoxide redox system to generate free radicals. Under these conditions, the polymer served as a sacrificial antioxidant and protected the asphalt components from oxidation. Viscoelastic properties of asphalts were determined from dynamic shear measurements using a high torque instrument. The cross-over temperature at which G equals G' as temperature increases was considered as the critical temperature and chosen as a criterion to asses the advancement of hardening (aging). The oxidative aging in the presence of water promoted an increase in the carbonyl content of aged samples, primarily as acid groups. Aging in the wet atmosphere had also a retarding effect on asphalt hardening." @default.
• W2464038215 created "2016-07-22" @default.
• W2464038215 creator A5037838843 @default.
• W2464038215 date "2022-06-10" @default.
• W2464038215 modified "2023-10-15" @default.
• W2464038215 title "Wet and dry aging of polymer-asphalt blends: chemistry and performance" @default.
• W2464038215 cites W119273545 @default.
• W2464038215 cites W1559487532 @default.
• W2464038215 cites W163612010 @default.
• W2464038215 cites W184522978 @default.
• W2464038215 cites W1973724444 @default.
• W2464038215 cites W1974321764 @default.
• W2464038215 cites W1980572102 @default.
• W2464038215 cites W2038797566 @default.
• W2464038215 cites W2082405910 @default.
• W2464038215 cites W2243120704 @default.
• W2464038215 cites W2246689303 @default.
• W2464038215 cites W2760531820 @default.
• W2464038215 cites W2993478885 @default.
• W2464038215 cites W591246053 @default.
• W2464038215 cites W656775183 @default.
• W2464038215 doi "https://doi.org/10.31390/gradschool_dissertations.2747" @default.
• W2464038215 hasPublicationYear "2022" @default.
• W2464038215 type Work @default.
• W2464038215 sameAs 2464038215 @default.
• W2464038215 citedByCount "10" @default.
• W2464038215 countsByYear W24640382152012 @default.
• W2464038215 countsByYear W24640382152013 @default.
• W2464038215 countsByYear W24640382152014 @default.
• W2464038215 countsByYear W24640382152015 @default.
• W2464038215 countsByYear W24640382152016 @default.
• W2464038215 crossrefType "dissertation" @default.
• W2464038215 hasAuthorship W2464038215A5037838843 @default.
• W2464038215 hasBestOaLocation W24640382151 @default.
• W2464038215 hasConcept C118820876 @default.
• W2464038215 hasConcept C124614425 @default.
• W2464038215 hasConcept C127413603 @default.
• W2464038215 hasConcept C145148216 @default.
• W2464038215 hasConcept C159985019 @default.
• W2464038215 hasConcept C160892712 @default.
• W2464038215 hasConcept C168056786 @default.
• W2464038215 hasConcept C178790620 @default.
• W2464038215 hasConcept C185592680 @default.
• W2464038215 hasConcept C192562407 @default.
• W2464038215 hasConcept C42360764 @default.
• W2464038215 hasConcept C521977710 @default.
• W2464038215 hasConceptScore W2464038215C118820876 @default.
• W2464038215 hasConceptScore W2464038215C124614425 @default.
• W2464038215 hasConceptScore W2464038215C127413603 @default.
• W2464038215 hasConceptScore W2464038215C145148216 @default.
• W2464038215 hasConceptScore W2464038215C159985019 @default.
• W2464038215 hasConceptScore W2464038215C160892712 @default.
• W2464038215 hasConceptScore W2464038215C168056786 @default.
• W2464038215 hasConceptScore W2464038215C178790620 @default.
• W2464038215 hasConceptScore W2464038215C185592680 @default.
• W2464038215 hasConceptScore W2464038215C192562407 @default.
• W2464038215 hasConceptScore W2464038215C42360764 @default.
• W2464038215 hasConceptScore W2464038215C521977710 @default.
• W2464038215 hasLocation W24640382151 @default.
• W2464038215 hasOpenAccess W2464038215 @default.
• W2464038215 hasPrimaryLocation W24640382151 @default.
• W2464038215 hasRelatedWork W1563464303 @default.
• W2464038215 hasRelatedWork W2077423026 @default.
• W2464038215 hasRelatedWork W2405651621 @default.
• W2464038215 hasRelatedWork W2481938601 @default.
• W2464038215 hasRelatedWork W2748952813 @default.
• W2464038215 hasRelatedWork W2899084033 @default.
• W2464038215 hasRelatedWork W2902108287 @default.
• W2464038215 hasRelatedWork W2923710639 @default.
• W2464038215 hasRelatedWork W3199644883 @default.
• W2464038215 hasRelatedWork W2489749078 @default.
• W2464038215 isParatext "false" @default.
• W2464038215 isRetracted "false" @default.
• W2464038215 magId "2464038215" @default.
• W2464038215 workType "dissertation" @default.