- W2471805482 abstract "用座滴法研究了Zr55Al10Ni5Cu30合金熔体与不锈钢基片在连续升温和不同温度下保温20min的润湿动力学,用扫描电镜观察了润湿冷凝样品的界面形貌,用能谱分析、X射线衍射等研究了界面反应,分析了Zr55 Al10Ni5Cu30与不锈钢基片之间的扩散和界面问题。结果表明:随着温度的升高,Zr55Al10Ni5Cu30与不锈钢基片之间的润湿角减小,润湿半径增大;1223,1273K时等温润湿动力学分3个阶段:孕育阶段、准稳态减小阶段和趋于平衡阶段,温度高于1323K时润湿只有趋于平衡阶段;Zr55Al10Ni5Cu30合金与不锈钢之间的润湿为反应控制型润湿,界面处有明显的扩散层和界面反应层;合金熔体一侧含熔体与不锈钢反应生成的Cr2Zr,界面处含反应生成的Al5Cr;在制备Zr55Al10Ni5Cu30/不锈钢非晶复合材料时必须合理选择制备工艺,严格'控制界面反应。" @default.
- W2471805482 created "2016-07-22" @default.
- W2471805482 creator A5018649105 @default.
- W2471805482 creator A5053411535 @default.
- W2471805482 creator A5062217966 @default.
- W2471805482 creator A5071142884 @default.
- W2471805482 creator A5085670583 @default.
- W2471805482 creator A5088434519 @default.
- W2471805482 date "2003-10-11" @default.
- W2471805482 modified "2023-10-15" @default.
- W2471805482 title "Zr_(55)Al_(10)Ni_5Cu_(30)合金熔体与不锈钢的润湿行为" @default.
- W2471805482 hasPublicationYear "2003" @default.
- W2471805482 type Work @default.
- W2471805482 sameAs 2471805482 @default.
- W2471805482 citedByCount "0" @default.
- W2471805482 crossrefType "journal-article" @default.
- W2471805482 hasAuthorship W2471805482A5018649105 @default.
- W2471805482 hasAuthorship W2471805482A5053411535 @default.
- W2471805482 hasAuthorship W2471805482A5062217966 @default.
- W2471805482 hasAuthorship W2471805482A5071142884 @default.
- W2471805482 hasAuthorship W2471805482A5085670583 @default.
- W2471805482 hasAuthorship W2471805482A5088434519 @default.
- W2471805482 hasConcept C144133560 @default.
- W2471805482 hasConceptScore W2471805482C144133560 @default.
- W2471805482 hasIssue "10" @default.
- W2471805482 hasLocation W24718054821 @default.
- W2471805482 hasOpenAccess W2471805482 @default.
- W2471805482 hasPrimaryLocation W24718054821 @default.
- W2471805482 isParatext "false" @default.
- W2471805482 isRetracted "false" @default.
- W2471805482 magId "2471805482" @default.
- W2471805482 workType "article" @default.