• W2476669976 abstract "Accelerated ageing experiments have been conducted to address durability issues of carbon/epoxy composites to be used for emerging facilities and infrastructure, such as, bridges and buildings, in different climatic zones. The degradation of carbon/epoxy composites under UV, hygrothermal exposure, and applied tensile stress has been investigated. The tests were designed to capture the synergistic effects of field exposure and extreme temperatures, viz., hot/dry, hot/wet, cold/dry, and cold/wet conditions. Short beam shear tests (SBST) were performed for the determination of interlaminar shear strength (ILSS) of conditioned composite specimens. The hot/dry samples showed increased strength, while the hot/wet ones showed a decrease in strength. It is conjectured that conditioning at 90 °C possibly contributed to an increase in the ILSS from post curing. For the hot/wet samples (90 °C, immersed in water) the results indicate that strength degradation due to moisture-induced hydrolysis overshadowed the post-curing effect. The samples subjected to shear stress under hot conditions (90 °C) showed a higher ILSS, possibly due to improved crosslink density arising from post-cure. There is insignificant variation in the ILSS of UV treated and the UV untreated control samples. All the SBST test data reported in this work are from tests performed at room temperature and ambient humidity after environmental ageing. A two-dimensional cohesive layer constitutive model with a prescribed traction-separation law constructed from the basic principles of continuum mechanics, taking into account hygrothermal mechanisms that are likely to occur within a cohesive bi-material interface, such as between adjacent plies in a laminate, was applied to simulate interlaminar failure in the SBST specimens, using Finite Element Analysis (FEA). A phenomenological predictive model was developed using the finite element results." @default.
• W2476669976 created "2016-08-23" @default.
• W2476669976 creator A5000055451 @default.
• W2476669976 creator A5014302388 @default.
• W2476669976 creator A5031595608 @default.
• W2476669976 creator A5034882621 @default.
• W2476669976 creator A5061095436 @default.
• W2476669976 creator A5062065730 @default.
• W2476669976 creator A5065107107 @default.
• W2476669976 creator A5066985878 @default.
• W2476669976 date "2008-03-01" @default.
• W2476669976 modified "2023-09-22" @default.
• W2476669976 title "Characterization and Modeling of the Effect of Environmental Degradation on Interlaminar Shear Strength of Carbon/Epoxy Composites" @default.
• W2476669976 cites W1972121965 @default.
• W2476669976 cites W1980155939 @default.
• W2476669976 cites W1984655262 @default.
• W2476669976 cites W1985110139 @default.
• W2476669976 cites W1991717224 @default.
• W2476669976 cites W2004385958 @default.
• W2476669976 cites W2007946595 @default.
• W2476669976 cites W2013437174 @default.
• W2476669976 cites W2014368988 @default.
• W2476669976 cites W2018081968 @default.
• W2476669976 cites W2033577786 @default.
• W2476669976 cites W2043119783 @default.
• W2476669976 cites W2052708608 @default.
• W2476669976 cites W2068086236 @default.
• W2476669976 cites W2075498950 @default.
• W2476669976 cites W2085160786 @default.
• W2476669976 cites W2086151727 @default.
• W2476669976 cites W2088740127 @default.
• W2476669976 cites W2127052695 @default.
• W2476669976 cites W2130688392 @default.
• W2476669976 cites W2464072380 @default.
• W2476669976 cites W32620874 @default.
• W2476669976 doi "https://doi.org/10.1177/096739110801600301" @default.
• W2476669976 hasPublicationYear "2008" @default.
• W2476669976 type Work @default.
• W2476669976 sameAs 2476669976 @default.
• W2476669976 citedByCount "5" @default.
• W2476669976 countsByYear W24766699762018 @default.
• W2476669976 crossrefType "journal-article" @default.
• W2476669976 hasAuthorship W2476669976A5000055451 @default.
• W2476669976 hasAuthorship W2476669976A5014302388 @default.
• W2476669976 hasAuthorship W2476669976A5031595608 @default.
• W2476669976 hasAuthorship W2476669976A5034882621 @default.
• W2476669976 hasAuthorship W2476669976A5061095436 @default.
• W2476669976 hasAuthorship W2476669976A5062065730 @default.
• W2476669976 hasAuthorship W2476669976A5065107107 @default.
• W2476669976 hasAuthorship W2476669976A5066985878 @default.
• W2476669976 hasConcept C104304963 @default.
• W2476669976 hasConcept C104779481 @default.
• W2476669976 hasConcept C112950240 @default.
• W2476669976 hasConcept C121332964 @default.
• W2476669976 hasConcept C132976073 @default.
• W2476669976 hasConcept C151420433 @default.
• W2476669976 hasConcept C159985019 @default.
• W2476669976 hasConcept C166595027 @default.
• W2476669976 hasConcept C176864760 @default.
• W2476669976 hasConcept C192562407 @default.
• W2476669976 hasConcept C96035792 @default.
• W2476669976 hasConcept C97355855 @default.
• W2476669976 hasConceptScore W2476669976C104304963 @default.
• W2476669976 hasConceptScore W2476669976C104779481 @default.
• W2476669976 hasConceptScore W2476669976C112950240 @default.
• W2476669976 hasConceptScore W2476669976C121332964 @default.
• W2476669976 hasConceptScore W2476669976C132976073 @default.
• W2476669976 hasConceptScore W2476669976C151420433 @default.
• W2476669976 hasConceptScore W2476669976C159985019 @default.
• W2476669976 hasConceptScore W2476669976C166595027 @default.
• W2476669976 hasConceptScore W2476669976C176864760 @default.
• W2476669976 hasConceptScore W2476669976C192562407 @default.
• W2476669976 hasConceptScore W2476669976C96035792 @default.
• W2476669976 hasConceptScore W2476669976C97355855 @default.
• W2476669976 hasIssue "3" @default.
• W2476669976 hasLocation W24766699761 @default.
• W2476669976 hasOpenAccess W2476669976 @default.
• W2476669976 hasPrimaryLocation W24766699761 @default.
• W2476669976 hasRelatedWork W1995958177 @default.
• W2476669976 hasRelatedWork W2029945387 @default.
• W2476669976 hasRelatedWork W2073593360 @default.
• W2476669976 hasRelatedWork W2093279597 @default.
• W2476669976 hasRelatedWork W2117665458 @default.
• W2476669976 hasRelatedWork W2224028747 @default.
• W2476669976 hasRelatedWork W2344923355 @default.
• W2476669976 hasRelatedWork W2376820830 @default.
• W2476669976 hasRelatedWork W2593200884 @default.
• W2476669976 hasRelatedWork W3121051381 @default.
• W2476669976 hasVolume "16" @default.
• W2476669976 isParatext "false" @default.
• W2476669976 isRetracted "false" @default.
• W2476669976 magId "2476669976" @default.
• W2476669976 workType "article" @default.