• W2489731844 abstract "The effect of isothermal aging on the microstructure and shear strength of Sn3Ag0.5Cu/Cu (SAC305/Cu) solder joints were studied systematically. The single-lap shear samples of SAC305/Cu solder joint were prepared and aged up to 456 h at 150 and 180 °C, respectively. The interfacial intermetallic compound layer of the aged solder joint gradually thickened with increasing both aging time and aging temperature, while, the interfacial intermetallic compound layer morphology transformed from scallop-type to layer-type after the aging treatment. The growth of the interfacial Cu-Sn interfacial intermetallic compounds layer of aged SAC305/Cu solder joints exhibited a linear function of the square root of aging time, indicating that the formation of the interfacial Cu-Sn interfacial intermetallic compounds during aging treatment was mainly controlled by the diffusion mechanism. The diffusion coefficient (D) values of interfacial intermetallic compound layer were 4.64×10−17 and 1.06×10−16 m2 s−1 for aging temperatures of 150 °C and 180 °C, respectively. Single-lap shear tests results revealed that the shear strength of SAC305/Cu solder joints decreased continuously with an increase in interfacial intermetallic compound layer thickness and aging time. The main reason for these characteristics was the excessive increase in the interfacial intermetallic compound thickness of solder joints, causing a change in the stress concentration of the shear load from the protruding region to the inside of the interfacial intermetallic compound layer at the same tested condition. In addition, the shear fractures in as-reflowed and short time aged solder joints were shown to be ductile in nature and confined in the bulk solder rather than through the interfacial intermetallic compound layer. However, the shear fracture locations transferred from the solder bulk to the interfacial Cu-Sn interfacial intermetallic compound layer, and finally to the Cu3Sn/Cu interface with increasing aging time." @default.
• W2489731844 created "2016-08-23" @default.
• W2489731844 creator A5021736459 @default.
• W2489731844 creator A5043111788 @default.
• W2489731844 creator A5050279656 @default.
• W2489731844 creator A5068397352 @default.
• W2489731844 creator A5081502398 @default.
• W2489731844 date "2016-09-01" @default.
• W2489731844 modified "2023-09-30" @default.
• W2489731844 title "Microstructure evolution and shear fracture behavior of aged Sn3Ag0.5Cu/Cu solder joints" @default.
• W2489731844 cites W1772498928 @default.
• W2489731844 cites W1796707144 @default.
• W2489731844 cites W1967225666 @default.
• W2489731844 cites W1971521274 @default.
• W2489731844 cites W1988996139 @default.
• W2489731844 cites W1994178688 @default.
• W2489731844 cites W1996407250 @default.
• W2489731844 cites W1997246835 @default.
• W2489731844 cites W2000661325 @default.
• W2489731844 cites W2002923627 @default.
• W2489731844 cites W2007828539 @default.
• W2489731844 cites W2007885511 @default.
• W2489731844 cites W2009088589 @default.
• W2489731844 cites W2018938304 @default.
• W2489731844 cites W2030652152 @default.
• W2489731844 cites W2040743544 @default.
• W2489731844 cites W2041364026 @default.
• W2489731844 cites W2044358827 @default.
• W2489731844 cites W2052122949 @default.
• W2489731844 cites W2059523013 @default.
• W2489731844 cites W2061687441 @default.
• W2489731844 cites W2062304382 @default.
• W2489731844 cites W2064487125 @default.
• W2489731844 cites W2065273895 @default.
• W2489731844 cites W2090296883 @default.
• W2489731844 cites W2090790436 @default.
• W2489731844 cites W2092043072 @default.
• W2489731844 cites W2093601693 @default.
• W2489731844 cites W2095047873 @default.
• W2489731844 cites W2101086736 @default.
• W2489731844 cites W2122260821 @default.
• W2489731844 cites W2126503149 @default.
• W2489731844 cites W2181171231 @default.
• W2489731844 cites W2251170613 @default.
• W2489731844 cites W2295962751 @default.
• W2489731844 cites W2334959979 @default.
• W2489731844 cites W2337785456 @default.
• W2489731844 doi "https://doi.org/10.1016/j.msea.2016.07.071" @default.
• W2489731844 hasPublicationYear "2016" @default.
• W2489731844 type Work @default.
• W2489731844 sameAs 2489731844 @default.
• W2489731844 citedByCount "95" @default.
• W2489731844 countsByYear W24897318442017 @default.
• W2489731844 countsByYear W24897318442018 @default.
• W2489731844 countsByYear W24897318442019 @default.
• W2489731844 countsByYear W24897318442020 @default.
• W2489731844 countsByYear W24897318442021 @default.
• W2489731844 countsByYear W24897318442022 @default.
• W2489731844 countsByYear W24897318442023 @default.
• W2489731844 crossrefType "journal-article" @default.
• W2489731844 hasAuthorship W2489731844A5021736459 @default.
• W2489731844 hasAuthorship W2489731844A5043111788 @default.
• W2489731844 hasAuthorship W2489731844A5050279656 @default.
• W2489731844 hasAuthorship W2489731844A5068397352 @default.
• W2489731844 hasAuthorship W2489731844A5081502398 @default.
• W2489731844 hasConcept C127413603 @default.
• W2489731844 hasConcept C127893833 @default.
• W2489731844 hasConcept C159390177 @default.
• W2489731844 hasConcept C159750122 @default.
• W2489731844 hasConcept C159985019 @default.
• W2489731844 hasConcept C170154142 @default.
• W2489731844 hasConcept C18555067 @default.
• W2489731844 hasConcept C191897082 @default.
• W2489731844 hasConcept C192562407 @default.
• W2489731844 hasConcept C27501479 @default.
• W2489731844 hasConcept C2779227376 @default.
• W2489731844 hasConcept C2780026712 @default.
• W2489731844 hasConcept C39432304 @default.
• W2489731844 hasConcept C50296614 @default.
• W2489731844 hasConcept C87976508 @default.
• W2489731844 hasConcept C96035792 @default.
• W2489731844 hasConceptScore W2489731844C127413603 @default.
• W2489731844 hasConceptScore W2489731844C127893833 @default.
• W2489731844 hasConceptScore W2489731844C159390177 @default.
• W2489731844 hasConceptScore W2489731844C159750122 @default.
• W2489731844 hasConceptScore W2489731844C159985019 @default.
• W2489731844 hasConceptScore W2489731844C170154142 @default.
• W2489731844 hasConceptScore W2489731844C18555067 @default.
• W2489731844 hasConceptScore W2489731844C191897082 @default.
• W2489731844 hasConceptScore W2489731844C192562407 @default.
• W2489731844 hasConceptScore W2489731844C27501479 @default.
• W2489731844 hasConceptScore W2489731844C2779227376 @default.
• W2489731844 hasConceptScore W2489731844C2780026712 @default.
• W2489731844 hasConceptScore W2489731844C39432304 @default.
• W2489731844 hasConceptScore W2489731844C50296614 @default.
• W2489731844 hasConceptScore W2489731844C87976508 @default.
• W2489731844 hasConceptScore W2489731844C96035792 @default.
• W2489731844 hasFunder F4320321001 @default.

• next