- W2490298063 abstract "The brazing behavior of 3003 fin assemble with 4343(filler layer)/4A60(transition layer)/08Al(steel layer) brazing sheet (the ratio of filler layer thickness to transition thickness were constant 1:2) were investigated. This study elucidates the brazing results vary with the layer thickness and brazing temperatures. Results showed that keeping the holding time at brazing temperature constant (the holding time of this study was 10 minutes in all brazing progress), under the condition of brazing temperature less than or equal to 580 °C, thinner filler layer led to well formed joint, while thicker filler layer led to defects at brazing joints because of poor mobility. When brazing temperature was up to 600 °C, a thinner transition layer trended to lead to the formation a thick intermetallic compounds layer on the Aluminum-Steel surface. It was inferred that Si diffused from molten filler metal to the interface of transition layer and steel layer and promoted the formation of intermetallic compounds. Furthermore, it was found that in the surface away from brazing joints, with lower Si content, the intermetallic compounds were mainly η (Fe2Al5), while higher Si content region nearby brazing joints trended to form τ5(Al8Fe2Si) and τ6(Al4.5FeSi). Meanwhile, a transition layer with thickness above 134μm could avoid the formation of intermetallic compound. The optimum brazing process was that temperature range was 590 °C to 595 °C with 10-minutes holding time and the transition layer thickness was suggested to be equal or more than 134μm." @default.
- W2490298063 created "2016-08-23" @default.
- W2490298063 creator A5019724950 @default.
- W2490298063 creator A5056465234 @default.
- W2490298063 creator A5075152513 @default.
- W2490298063 creator A5087389582 @default.
- W2490298063 date "2016-01-01" @default.
- W2490298063 modified "2023-09-26" @default.
- W2490298063 title "The Brazing Behavior of Aluminum-Steel Cladding Strip with Pre-Cladded Brazing Layer Used in Air Cooling System of Power Plants" @default.
- W2490298063 cites W1503767974 @default.
- W2490298063 cites W1977574670 @default.
- W2490298063 cites W2055856482 @default.
- W2490298063 cites W2072336820 @default.
- W2490298063 cites W2101014098 @default.
- W2490298063 doi "https://doi.org/10.1051/matecconf/20166705017" @default.
- W2490298063 hasPublicationYear "2016" @default.
- W2490298063 type Work @default.
- W2490298063 sameAs 2490298063 @default.
- W2490298063 citedByCount "0" @default.
- W2490298063 crossrefType "journal-article" @default.
- W2490298063 hasAuthorship W2490298063A5019724950 @default.
- W2490298063 hasAuthorship W2490298063A5056465234 @default.
- W2490298063 hasAuthorship W2490298063A5075152513 @default.
- W2490298063 hasAuthorship W2490298063A5087389582 @default.
- W2490298063 hasBestOaLocation W24902980631 @default.
- W2490298063 hasConcept C120114934 @default.
- W2490298063 hasConcept C159985019 @default.
- W2490298063 hasConcept C191897082 @default.
- W2490298063 hasConcept C192562407 @default.
- W2490298063 hasConcept C19474535 @default.
- W2490298063 hasConcept C20480867 @default.
- W2490298063 hasConcept C27501479 @default.
- W2490298063 hasConcept C2778223994 @default.
- W2490298063 hasConcept C2779227376 @default.
- W2490298063 hasConcept C2780026712 @default.
- W2490298063 hasConcept C36456112 @default.
- W2490298063 hasConcept C513153333 @default.
- W2490298063 hasConcept C86171150 @default.
- W2490298063 hasConceptScore W2490298063C120114934 @default.
- W2490298063 hasConceptScore W2490298063C159985019 @default.
- W2490298063 hasConceptScore W2490298063C191897082 @default.
- W2490298063 hasConceptScore W2490298063C192562407 @default.
- W2490298063 hasConceptScore W2490298063C19474535 @default.
- W2490298063 hasConceptScore W2490298063C20480867 @default.
- W2490298063 hasConceptScore W2490298063C27501479 @default.
- W2490298063 hasConceptScore W2490298063C2778223994 @default.
- W2490298063 hasConceptScore W2490298063C2779227376 @default.
- W2490298063 hasConceptScore W2490298063C2780026712 @default.
- W2490298063 hasConceptScore W2490298063C36456112 @default.
- W2490298063 hasConceptScore W2490298063C513153333 @default.
- W2490298063 hasConceptScore W2490298063C86171150 @default.
- W2490298063 hasLocation W24902980631 @default.
- W2490298063 hasLocation W24902980632 @default.
- W2490298063 hasOpenAccess W2490298063 @default.
- W2490298063 hasPrimaryLocation W24902980631 @default.
- W2490298063 hasRelatedWork W1965148666 @default.
- W2490298063 hasRelatedWork W1970504709 @default.
- W2490298063 hasRelatedWork W2072089000 @default.
- W2490298063 hasRelatedWork W2318589939 @default.
- W2490298063 hasRelatedWork W2378344398 @default.
- W2490298063 hasRelatedWork W2392280097 @default.
- W2490298063 hasRelatedWork W250402765 @default.
- W2490298063 hasRelatedWork W3025175549 @default.
- W2490298063 hasRelatedWork W3119488421 @default.
- W2490298063 hasRelatedWork W3120506015 @default.
- W2490298063 hasVolume "67" @default.
- W2490298063 isParatext "false" @default.
- W2490298063 isRetracted "false" @default.
- W2490298063 magId "2490298063" @default.
- W2490298063 workType "article" @default.