- W2492414978 abstract "Inverter surge resistant enameled wire was prepared with an organic/inorganic hybrid nanocomposite, and the effect of ambient temperature on the insulation lifetime of the enameled wire in the form of twisted pair was studied by a withstanding voltage tester. The organic polymer was Polyesterimide-polyamideimide (EI/AI) and the inorganic material was a Nano-sized silica (average particle size : 15 nm). The enamel thickness was 50 μm and the ambient temperature was 100℃, 150℃, 200℃, and 250℃, respectively. Transmission electron microscopy (TEM) observation showed that Nano-sized Silica were evenly dispersed in EI/AI. There were many air gaps in a twisted pair, therefore, when voltage was applied to the twisted pair, enamel erosion took place in the air gap area because of partial discharge accordi, ng to Paschen's law. As ambient temperature increased, insulation lifetime decreased according to Arrhenius relationship, which was explained by the increasing mobility of polymer chains in EI or AI. And insulation breakdown voltage value at 10 kHz was 1,864.5 sec (31.1 min), which is 1.9 times higher than at 20 kHz, 981.6 sec (16.4 min)." @default.
- W2492414978 created "2016-08-23" @default.
- W2492414978 creator A5091322237 @default.
- W2492414978 date "2016-06-25" @default.
- W2492414978 modified "2023-09-23" @default.
- W2492414978 title "Effect of Ambient Temperature on Insulation Lifetime of Inverter Surge Resistant Enameled Wire Prepared with Organic/Inorganic Hybrid Nanocomposite" @default.
- W2492414978 cites W1970649207 @default.
- W2492414978 cites W2006573724 @default.
- W2492414978 cites W2044139759 @default.
- W2492414978 cites W2048608563 @default.
- W2492414978 cites W2074910498 @default.
- W2492414978 cites W2094691358 @default.
- W2492414978 cites W2115586214 @default.
- W2492414978 cites W2128719053 @default.
- W2492414978 cites W2168053533 @default.
- W2492414978 cites W1624442295 @default.
- W2492414978 doi "https://doi.org/10.4313/teem.2016.17.3.163" @default.
- W2492414978 hasPublicationYear "2016" @default.
- W2492414978 type Work @default.
- W2492414978 sameAs 2492414978 @default.
- W2492414978 citedByCount "0" @default.
- W2492414978 crossrefType "journal-article" @default.
- W2492414978 hasAuthorship W2492414978A5091322237 @default.
- W2492414978 hasBestOaLocation W24924149781 @default.
- W2492414978 hasConcept C108990781 @default.
- W2492414978 hasConcept C119599485 @default.
- W2492414978 hasConcept C127413603 @default.
- W2492414978 hasConcept C130143024 @default.
- W2492414978 hasConcept C159985019 @default.
- W2492414978 hasConcept C165801399 @default.
- W2492414978 hasConcept C178790620 @default.
- W2492414978 hasConcept C185592680 @default.
- W2492414978 hasConcept C192562407 @default.
- W2492414978 hasConcept C521977710 @default.
- W2492414978 hasConcept C86183883 @default.
- W2492414978 hasConcept C92880739 @default.
- W2492414978 hasConcept C95121573 @default.
- W2492414978 hasConceptScore W2492414978C108990781 @default.
- W2492414978 hasConceptScore W2492414978C119599485 @default.
- W2492414978 hasConceptScore W2492414978C127413603 @default.
- W2492414978 hasConceptScore W2492414978C130143024 @default.
- W2492414978 hasConceptScore W2492414978C159985019 @default.
- W2492414978 hasConceptScore W2492414978C165801399 @default.
- W2492414978 hasConceptScore W2492414978C178790620 @default.
- W2492414978 hasConceptScore W2492414978C185592680 @default.
- W2492414978 hasConceptScore W2492414978C192562407 @default.
- W2492414978 hasConceptScore W2492414978C521977710 @default.
- W2492414978 hasConceptScore W2492414978C86183883 @default.
- W2492414978 hasConceptScore W2492414978C92880739 @default.
- W2492414978 hasConceptScore W2492414978C95121573 @default.
- W2492414978 hasLocation W24924149781 @default.
- W2492414978 hasOpenAccess W2492414978 @default.
- W2492414978 hasPrimaryLocation W24924149781 @default.
- W2492414978 hasRelatedWork W1832308060 @default.
- W2492414978 hasRelatedWork W1976874617 @default.
- W2492414978 hasRelatedWork W1999677645 @default.
- W2492414978 hasRelatedWork W2014435825 @default.
- W2492414978 hasRelatedWork W2018592953 @default.
- W2492414978 hasRelatedWork W2052998041 @default.
- W2492414978 hasRelatedWork W2109235197 @default.
- W2492414978 hasRelatedWork W2167052269 @default.
- W2492414978 hasRelatedWork W2168053533 @default.
- W2492414978 hasRelatedWork W2331644525 @default.
- W2492414978 hasRelatedWork W2366621169 @default.
- W2492414978 hasRelatedWork W2393101955 @default.
- W2492414978 hasRelatedWork W2530056232 @default.
- W2492414978 hasRelatedWork W2742602237 @default.
- W2492414978 hasRelatedWork W2773466977 @default.
- W2492414978 hasRelatedWork W2810958799 @default.
- W2492414978 hasRelatedWork W2902291206 @default.
- W2492414978 hasRelatedWork W3010325173 @default.
- W2492414978 hasRelatedWork W2932225745 @default.
- W2492414978 hasRelatedWork W2959588691 @default.
- W2492414978 isParatext "false" @default.
- W2492414978 isRetracted "false" @default.
- W2492414978 magId "2492414978" @default.
- W2492414978 workType "article" @default.