- W2510150634 abstract "The mechanical properties and formability of AZ31 magnesium alloy strips having different textures were investigated at a high strain rate based on that occuring in mass production by press forming. Forming at a high strain rate on the order of 100 s-1 requires a high temperature of over 473 K. To obtain accurate stress-strain curves, a high-speed testing machine that can maintain a constant true strain rate was used, and the change in gauge length on a test piece in a furnace was measured during the testing time of about 0.5 s. For the specimens, rolled strips consisting of fine grains (about 10 μm) and an extruded strip consisting of coarse grains (about 40 μm) were used. The {0001} textures of the extruded strip and one of the rolled strips were strongly oriented parallel to the rolled surface, but the texture of another rolling strip had two peaks that were inclined at 5∼15 deg in front of and behind the rolling direction. At the high strain rate of 100 s-1, elongation decreased for every specimen. Nevertheless, a limiting drawing ratio (LDR) of 2.1∼2.2 was obtained under uniform heating above 503 K in all the specimens except for the extruded strip. The high LDR of the rolled strip having a two-peak texture was maintained in forming at temperatures down to 473 K, in contrast to the LDR of the strongly oriented rolled strip, which reduced rapidly when formed at temperatures less than 503 K." @default.
- W2510150634 created "2016-09-16" @default.
- W2510150634 creator A5013274929 @default.
- W2510150634 creator A5045258956 @default.
- W2510150634 creator A5047086282 @default.
- W2510150634 creator A5062600901 @default.
- W2510150634 creator A5063222083 @default.
- W2510150634 creator A5067413562 @default.
- W2510150634 creator A5086133075 @default.
- W2510150634 creator A5086763656 @default.
- W2510150634 date "2008-01-01" @default.
- W2510150634 modified "2023-10-04" @default.
- W2510150634 title "Effect of Texture of AZ31 Magnesium Alloy Sheeton Mechanical Properties and Formability at High Strain Rate" @default.
- W2510150634 cites W1993254642 @default.
- W2510150634 cites W2000007156 @default.
- W2510150634 cites W2087638403 @default.
- W2510150634 cites W2128553584 @default.
- W2510150634 cites W2170442425 @default.
- W2510150634 cites W328841391 @default.
- W2510150634 doi "https://doi.org/10.9773/sosei.49.221" @default.
- W2510150634 hasPublicationYear "2008" @default.
- W2510150634 type Work @default.
- W2510150634 sameAs 2510150634 @default.
- W2510150634 citedByCount "0" @default.
- W2510150634 crossrefType "journal-article" @default.
- W2510150634 hasAuthorship W2510150634A5013274929 @default.
- W2510150634 hasAuthorship W2510150634A5045258956 @default.
- W2510150634 hasAuthorship W2510150634A5047086282 @default.
- W2510150634 hasAuthorship W2510150634A5062600901 @default.
- W2510150634 hasAuthorship W2510150634A5063222083 @default.
- W2510150634 hasAuthorship W2510150634A5067413562 @default.
- W2510150634 hasAuthorship W2510150634A5086133075 @default.
- W2510150634 hasAuthorship W2510150634A5086763656 @default.
- W2510150634 hasBestOaLocation W25101506341 @default.
- W2510150634 hasConcept C112950240 @default.
- W2510150634 hasConcept C115961682 @default.
- W2510150634 hasConcept C149342994 @default.
- W2510150634 hasConcept C154945302 @default.
- W2510150634 hasConcept C159985019 @default.
- W2510150634 hasConcept C191897082 @default.
- W2510150634 hasConcept C192562407 @default.
- W2510150634 hasConcept C200925200 @default.
- W2510150634 hasConcept C2776797782 @default.
- W2510150634 hasConcept C2781195486 @default.
- W2510150634 hasConcept C33947775 @default.
- W2510150634 hasConcept C41008148 @default.
- W2510150634 hasConcept C543218039 @default.
- W2510150634 hasConcept C79127381 @default.
- W2510150634 hasConceptScore W2510150634C112950240 @default.
- W2510150634 hasConceptScore W2510150634C115961682 @default.
- W2510150634 hasConceptScore W2510150634C149342994 @default.
- W2510150634 hasConceptScore W2510150634C154945302 @default.
- W2510150634 hasConceptScore W2510150634C159985019 @default.
- W2510150634 hasConceptScore W2510150634C191897082 @default.
- W2510150634 hasConceptScore W2510150634C192562407 @default.
- W2510150634 hasConceptScore W2510150634C200925200 @default.
- W2510150634 hasConceptScore W2510150634C2776797782 @default.
- W2510150634 hasConceptScore W2510150634C2781195486 @default.
- W2510150634 hasConceptScore W2510150634C33947775 @default.
- W2510150634 hasConceptScore W2510150634C41008148 @default.
- W2510150634 hasConceptScore W2510150634C543218039 @default.
- W2510150634 hasConceptScore W2510150634C79127381 @default.
- W2510150634 hasIssue "566" @default.
- W2510150634 hasLocation W25101506341 @default.
- W2510150634 hasOpenAccess W2510150634 @default.
- W2510150634 hasPrimaryLocation W25101506341 @default.
- W2510150634 hasRelatedWork W1545333684 @default.
- W2510150634 hasRelatedWork W1962549392 @default.
- W2510150634 hasRelatedWork W1974077162 @default.
- W2510150634 hasRelatedWork W1986350347 @default.
- W2510150634 hasRelatedWork W1989710912 @default.
- W2510150634 hasRelatedWork W2087638403 @default.
- W2510150634 hasRelatedWork W2133581575 @default.
- W2510150634 hasRelatedWork W2363002399 @default.
- W2510150634 hasRelatedWork W2913950566 @default.
- W2510150634 hasRelatedWork W4210515284 @default.
- W2510150634 hasVolume "49" @default.
- W2510150634 isParatext "false" @default.
- W2510150634 isRetracted "false" @default.
- W2510150634 magId "2510150634" @default.
- W2510150634 workType "article" @default.