- W2510176530 abstract "To investigate fatigue fracture resistance and wear behavior of a polymer infiltrated ceramic network (PICN) material (ENAMIC, Vita Zahnfabrik). Anatomically shaped ENAMIC monolithic crowns were milled using a CAD/CAM system. The crowns were cemented on aged dentin-like composite abutments (Z100, 3M ESPE) with resin-based cement (Vita DUO Cement, Vita). The specimens were subjected to 2 types of fatigue and wear tests: (1) accelerated sliding-contact mouth-motion step-stress fatigue test (n = 24) in water; and (2) long-term sliding-contact mouth-motion fatigue/wear test using a clinically relevant load (P = 200 N, n = 8) in water. Failure was designated as chip-off or bulk fracture. Optical and scanning electron microscopes were used to examine the occlusal surface and subsurface damage, as well as to reveal the material’s microstructure. In addition, wear volume and depth were measured by X-ray micro-computed tomography. For accelerated mouth-motion step-stress fatigue testing, 3 out of the 24 ENAMIC crowns fractured following cyclic loading up to 1700 N. Minor occlusal damage and contact-induced cone cracks were observed in all surviving specimens, but no flexural radial cracks were seen. For long-term mouth-motion fatigue/wear testing under a 200 N load in water, a small wear scar without significant cracks was observed in all 8 tested ENAMIC crowns. Monolithic CAD/CAM ENAMIC crowns showed superior resistance to sliding-contact fatigue fracture and wear." @default.
- W2510176530 created "2016-09-16" @default.
- W2510176530 creator A5025838352 @default.
- W2510176530 creator A5030064190 @default.
- W2510176530 creator A5073535453 @default.
- W2510176530 creator A5078726607 @default.
- W2510176530 creator A5089996204 @default.
- W2510176530 date "2016-11-01" @default.
- W2510176530 modified "2023-10-18" @default.
- W2510176530 title "Polymer infiltrated ceramic network structures for resistance to fatigue fracture and wear" @default.
- W2510176530 cites W1554494077 @default.
- W2510176530 cites W168125948 @default.
- W2510176530 cites W1932888361 @default.
- W2510176530 cites W1956350146 @default.
- W2510176530 cites W1972085843 @default.
- W2510176530 cites W1972189925 @default.
- W2510176530 cites W1973139438 @default.
- W2510176530 cites W1981498402 @default.
- W2510176530 cites W1990995532 @default.
- W2510176530 cites W1997947900 @default.
- W2510176530 cites W2001549471 @default.
- W2510176530 cites W2004968110 @default.
- W2510176530 cites W2006449317 @default.
- W2510176530 cites W2008267646 @default.
- W2510176530 cites W2010139259 @default.
- W2510176530 cites W2023816622 @default.
- W2510176530 cites W2027984864 @default.
- W2510176530 cites W2035345491 @default.
- W2510176530 cites W2039728109 @default.
- W2510176530 cites W2048206572 @default.
- W2510176530 cites W2053358628 @default.
- W2510176530 cites W2056209264 @default.
- W2510176530 cites W2065195705 @default.
- W2510176530 cites W2068370373 @default.
- W2510176530 cites W2073448873 @default.
- W2510176530 cites W2082604392 @default.
- W2510176530 cites W2101122039 @default.
- W2510176530 cites W2101614799 @default.
- W2510176530 cites W2102773635 @default.
- W2510176530 cites W2108752214 @default.
- W2510176530 cites W2111498507 @default.
- W2510176530 cites W2116893589 @default.
- W2510176530 cites W2119113863 @default.
- W2510176530 cites W2126490493 @default.
- W2510176530 cites W2138125097 @default.
- W2510176530 cites W2140481289 @default.
- W2510176530 cites W2142622967 @default.
- W2510176530 cites W2143989407 @default.
- W2510176530 cites W2155498659 @default.
- W2510176530 cites W2163271499 @default.
- W2510176530 cites W2165719407 @default.
- W2510176530 cites W2166568087 @default.
- W2510176530 cites W2172191836 @default.
- W2510176530 cites W2207987467 @default.
- W2510176530 cites W2221598089 @default.
- W2510176530 cites W2222476749 @default.
- W2510176530 cites W2239697369 @default.
- W2510176530 cites W2260844539 @default.
- W2510176530 cites W2412310851 @default.
- W2510176530 cites W2418462225 @default.
- W2510176530 cites W2473498713 @default.
- W2510176530 cites W25153508 @default.
- W2510176530 cites W326178968 @default.
- W2510176530 doi "https://doi.org/10.1016/j.dental.2016.08.216" @default.
- W2510176530 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/5075247" @default.
- W2510176530 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/27585486" @default.
- W2510176530 hasPublicationYear "2016" @default.
- W2510176530 type Work @default.
- W2510176530 sameAs 2510176530 @default.
- W2510176530 citedByCount "63" @default.
- W2510176530 countsByYear W25101765302017 @default.
- W2510176530 countsByYear W25101765302018 @default.
- W2510176530 countsByYear W25101765302019 @default.
- W2510176530 countsByYear W25101765302020 @default.
- W2510176530 countsByYear W25101765302021 @default.
- W2510176530 countsByYear W25101765302022 @default.
- W2510176530 countsByYear W25101765302023 @default.
- W2510176530 crossrefType "journal-article" @default.
- W2510176530 hasAuthorship W2510176530A5025838352 @default.
- W2510176530 hasAuthorship W2510176530A5030064190 @default.
- W2510176530 hasAuthorship W2510176530A5073535453 @default.
- W2510176530 hasAuthorship W2510176530A5078726607 @default.
- W2510176530 hasAuthorship W2510176530A5089996204 @default.
- W2510176530 hasBestOaLocation W25101765302 @default.
- W2510176530 hasConcept C134132462 @default.
- W2510176530 hasConcept C159985019 @default.
- W2510176530 hasConcept C178405089 @default.
- W2510176530 hasConcept C192562407 @default.
- W2510176530 hasConcept C26771246 @default.
- W2510176530 hasConcept C43369102 @default.
- W2510176530 hasConcept C61039299 @default.
- W2510176530 hasConceptScore W2510176530C134132462 @default.
- W2510176530 hasConceptScore W2510176530C159985019 @default.
- W2510176530 hasConceptScore W2510176530C178405089 @default.
- W2510176530 hasConceptScore W2510176530C192562407 @default.
- W2510176530 hasConceptScore W2510176530C26771246 @default.
- W2510176530 hasConceptScore W2510176530C43369102 @default.
- W2510176530 hasConceptScore W2510176530C61039299 @default.