- W2518565568 abstract "The temper embrittlement occurring in HAZ of 2 1/4Cr-1Mo steel was studied in the tempering temperature-time range of 774 to 900 K and 0.2 to 10000 hours. The transition temperature, TrE was measured on each specimen, and the temper embrittlement was detected as the rise of TrE. The temper embrittlement were classified into four types. The first and second types of embrittlement appear in the earlier stage of tempering, such as 775 K for 1 hour, and 100 hours, respectively. They differ from the low-temperature temper embrittlement which has ever been observed. The secondary hardening occurring during tempering seems to play an important role to induce those types of embrittlement. The third type appears in the tempering in a log time (825 K for 100 to 1000 hours). This type is identical with the high-temperature temper embrittlement (reversible temper embrittlement) . The fourth type arises in the final stage of tempering (825 K for 1000 to 10000 hours). Little work has been made to distinguish this type from the third type, and hence little is known about its characteristics. The temperature-time ranges in which those four types of embrittlement arise were shown in a diagram. The range where no embrittlement arises was also pointed out. Impact test carried out below the temperature of TrE produced an intergranular fracture in the specimen causing the third type of embrittlement, and a transgranular one in those for the first, second and fourth types of embrittlement." @default.
- W2518565568 created "2016-09-16" @default.
- W2518565568 creator A5001845091 @default.
- W2518565568 creator A5061339520 @default.
- W2518565568 creator A5066681119 @default.
- W2518565568 creator A5082485466 @default.
- W2518565568 date "1996-01-01" @default.
- W2518565568 modified "2023-10-16" @default.
- W2518565568 title "Study of Temper Embrittlement in HAZ of Cr-Mo Steels (Report 1). Four Types of Temper Embrittlement observed in HAZ of 21/4Cr-1Mo Steel." @default.
- W2518565568 cites W2002129701 @default.
- W2518565568 doi "https://doi.org/10.2207/qjjws.14.344" @default.
- W2518565568 hasPublicationYear "1996" @default.
- W2518565568 type Work @default.
- W2518565568 sameAs 2518565568 @default.
- W2518565568 citedByCount "5" @default.
- W2518565568 crossrefType "journal-article" @default.
- W2518565568 hasAuthorship W2518565568A5001845091 @default.
- W2518565568 hasAuthorship W2518565568A5061339520 @default.
- W2518565568 hasAuthorship W2518565568A5066681119 @default.
- W2518565568 hasAuthorship W2518565568A5082485466 @default.
- W2518565568 hasBestOaLocation W25185655681 @default.
- W2518565568 hasConcept C142282041 @default.
- W2518565568 hasConcept C184102282 @default.
- W2518565568 hasConcept C191897082 @default.
- W2518565568 hasConcept C192562407 @default.
- W2518565568 hasConcept C207948433 @default.
- W2518565568 hasConcept C2777820655 @default.
- W2518565568 hasConcept C2779930716 @default.
- W2518565568 hasConcept C87976508 @default.
- W2518565568 hasConceptScore W2518565568C142282041 @default.
- W2518565568 hasConceptScore W2518565568C184102282 @default.
- W2518565568 hasConceptScore W2518565568C191897082 @default.
- W2518565568 hasConceptScore W2518565568C192562407 @default.
- W2518565568 hasConceptScore W2518565568C207948433 @default.
- W2518565568 hasConceptScore W2518565568C2777820655 @default.
- W2518565568 hasConceptScore W2518565568C2779930716 @default.
- W2518565568 hasConceptScore W2518565568C87976508 @default.
- W2518565568 hasIssue "2" @default.
- W2518565568 hasLocation W25185655681 @default.
- W2518565568 hasOpenAccess W2518565568 @default.
- W2518565568 hasPrimaryLocation W25185655681 @default.
- W2518565568 hasRelatedWork W1992377420 @default.
- W2518565568 hasRelatedWork W2001433311 @default.
- W2518565568 hasRelatedWork W2016368579 @default.
- W2518565568 hasRelatedWork W2030530812 @default.
- W2518565568 hasRelatedWork W2030602022 @default.
- W2518565568 hasRelatedWork W2046499048 @default.
- W2518565568 hasRelatedWork W2322072850 @default.
- W2518565568 hasRelatedWork W2348668830 @default.
- W2518565568 hasRelatedWork W2518565568 @default.
- W2518565568 hasRelatedWork W2797460705 @default.
- W2518565568 hasVolume "14" @default.
- W2518565568 isParatext "false" @default.
- W2518565568 isRetracted "false" @default.
- W2518565568 magId "2518565568" @default.
- W2518565568 workType "article" @default.