- W2534450888 abstract "Nanocrystalline copper oxide films have been synthesized on glass by dc sputtering method. The effects of oxygen flow rate and deposition temperature on the microstructure of nanocrystalline copper oxide films were investigated. X-ray diffraction analysis shows that a broaden peak of Cu <sub xmlns:mml=http://www.w3.org/1998/Math/MathML xmlns:xlink=http://www.w3.org/1999/xlink>2</sub> O (111) was observed at the deposition condition of DC power 150 W, pressure 3.3 Pa, substrate temperature 200degC, Argon flow rate 10 seem and O <sub xmlns:mml=http://www.w3.org/1998/Math/MathML xmlns:xlink=http://www.w3.org/1999/xlink>2</sub> flow rate 1 sccm. With increasing the oxygen flow rate to 3 - 5 and 7 sccm, CuO (-111) could be obtained at 100 and 200degC, respectively. The increase of oxygen flow rate resulted in the film formation from Cu <sub xmlns:mml=http://www.w3.org/1998/Math/MathML xmlns:xlink=http://www.w3.org/1999/xlink>2</sub> O to CuO. SEM pictures show that copper oxide films exhibit nanosize grains. X-ray diffraction patterns of CuO films deposited at 50-200degC show that only (-111) plane is obtained. The SEM pictures show that the grain size increases with the deposition increases." @default.
- W2534450888 created "2016-10-28" @default.
- W2534450888 creator A5010975996 @default.
- W2534450888 creator A5018414638 @default.
- W2534450888 creator A5077193646 @default.
- W2534450888 date "2007-01-01" @default.
- W2534450888 modified "2023-10-05" @default.
- W2534450888 title "Deposition of nanocrystalline copper oxide films for solar cell application" @default.
- W2534450888 cites W1963485566 @default.
- W2534450888 cites W1988937367 @default.
- W2534450888 cites W1990046987 @default.
- W2534450888 cites W2064428037 @default.
- W2534450888 cites W2079696821 @default.
- W2534450888 cites W2142510977 @default.
- W2534450888 doi "https://doi.org/10.1109/edssc.2007.4450215" @default.
- W2534450888 hasPublicationYear "2007" @default.
- W2534450888 type Work @default.
- W2534450888 sameAs 2534450888 @default.
- W2534450888 citedByCount "1" @default.
- W2534450888 countsByYear W25344508882014 @default.
- W2534450888 crossrefType "proceedings-article" @default.
- W2534450888 hasAuthorship W2534450888A5010975996 @default.
- W2534450888 hasAuthorship W2534450888A5018414638 @default.
- W2534450888 hasAuthorship W2534450888A5077193646 @default.
- W2534450888 hasConcept C111368507 @default.
- W2534450888 hasConcept C113196181 @default.
- W2534450888 hasConcept C121332964 @default.
- W2534450888 hasConcept C127313418 @default.
- W2534450888 hasConcept C127413603 @default.
- W2534450888 hasConcept C140676511 @default.
- W2534450888 hasConcept C151730666 @default.
- W2534450888 hasConcept C171250308 @default.
- W2534450888 hasConcept C172120300 @default.
- W2534450888 hasConcept C178790620 @default.
- W2534450888 hasConcept C185592680 @default.
- W2534450888 hasConcept C191897082 @default.
- W2534450888 hasConcept C192191005 @default.
- W2534450888 hasConcept C192562407 @default.
- W2534450888 hasConcept C2777289219 @default.
- W2534450888 hasConcept C2779851234 @default.
- W2534450888 hasConcept C2781183027 @default.
- W2534450888 hasConcept C2816523 @default.
- W2534450888 hasConcept C42360764 @default.
- W2534450888 hasConcept C540031477 @default.
- W2534450888 hasConcept C544778455 @default.
- W2534450888 hasConcept C62520636 @default.
- W2534450888 hasConcept C64297162 @default.
- W2534450888 hasConcept C86803240 @default.
- W2534450888 hasConceptScore W2534450888C111368507 @default.
- W2534450888 hasConceptScore W2534450888C113196181 @default.
- W2534450888 hasConceptScore W2534450888C121332964 @default.
- W2534450888 hasConceptScore W2534450888C127313418 @default.
- W2534450888 hasConceptScore W2534450888C127413603 @default.
- W2534450888 hasConceptScore W2534450888C140676511 @default.
- W2534450888 hasConceptScore W2534450888C151730666 @default.
- W2534450888 hasConceptScore W2534450888C171250308 @default.
- W2534450888 hasConceptScore W2534450888C172120300 @default.
- W2534450888 hasConceptScore W2534450888C178790620 @default.
- W2534450888 hasConceptScore W2534450888C185592680 @default.
- W2534450888 hasConceptScore W2534450888C191897082 @default.
- W2534450888 hasConceptScore W2534450888C192191005 @default.
- W2534450888 hasConceptScore W2534450888C192562407 @default.
- W2534450888 hasConceptScore W2534450888C2777289219 @default.
- W2534450888 hasConceptScore W2534450888C2779851234 @default.
- W2534450888 hasConceptScore W2534450888C2781183027 @default.
- W2534450888 hasConceptScore W2534450888C2816523 @default.
- W2534450888 hasConceptScore W2534450888C42360764 @default.
- W2534450888 hasConceptScore W2534450888C540031477 @default.
- W2534450888 hasConceptScore W2534450888C544778455 @default.
- W2534450888 hasConceptScore W2534450888C62520636 @default.
- W2534450888 hasConceptScore W2534450888C64297162 @default.
- W2534450888 hasConceptScore W2534450888C86803240 @default.
- W2534450888 hasLocation W25344508881 @default.
- W2534450888 hasOpenAccess W2534450888 @default.
- W2534450888 hasPrimaryLocation W25344508881 @default.
- W2534450888 hasRelatedWork W1969046553 @default.
- W2534450888 hasRelatedWork W1991668545 @default.
- W2534450888 hasRelatedWork W2061214119 @default.
- W2534450888 hasRelatedWork W2317292542 @default.
- W2534450888 hasRelatedWork W2381843244 @default.
- W2534450888 hasRelatedWork W2387663520 @default.
- W2534450888 hasRelatedWork W2768963852 @default.
- W2534450888 hasRelatedWork W3047137656 @default.
- W2534450888 hasRelatedWork W4230069571 @default.
- W2534450888 hasRelatedWork W1980654097 @default.
- W2534450888 isParatext "false" @default.
- W2534450888 isRetracted "false" @default.
- W2534450888 magId "2534450888" @default.
- W2534450888 workType "article" @default.