- W2537058166 abstract "Two kinds of new Fe-Cr system alloy brazing filler, Fe-Cr-based and Fe-based, have been developed as a substitute for expensive Ni-based brazing filler in brazing of SUS304 stainless steel. Joint strength of the joints brazed with new filler were investigated and compared with the joint brazed with Ni-based brazing filler. The following results were obtained in the study. P-rich phases were formed because Ni in the new Fe-Cr system alloy diffused from the brazed layer to SUS304 stainless steel when joint clearance was 10 μm. When joint clearance was more than 50 μm, a finally-solidified region appeared in the brazed layer, at the same time, most of P segregated and was enriched in the finally-solidified region. It was proved that the volume fraction of P-rich phases in the finally-solidified region varied with the increase of joint clearance and joint strength decreases with the increase of the volume fraction of P-rich phases. Compared with Ni-based filler, joint strength of the joint brazed with Fe-based filler was almost equal when joint clearance was under 200 μm. On the other hand, joint strength of the joint brazed with Fe-Cr-based filler was slightly inferior regardless of joint clearance. Still, joint strength reached approximately 100 MPa. The result indicated that joint strength of the brazed joint with the Fe-Cr system alloy was strongly affected by the P addition. It is possible that promoting of joint strength can be brought by lower addition of P." @default.
- W2537058166 created "2016-10-28" @default.
- W2537058166 creator A5008096281 @default.
- W2537058166 creator A5016544963 @default.
- W2537058166 creator A5037119704 @default.
- W2537058166 creator A5047453133 @default.
- W2537058166 creator A5067877122 @default.
- W2537058166 creator A5080023007 @default.
- W2537058166 date "2015-01-01" @default.
- W2537058166 modified "2023-10-03" @default.
- W2537058166 title "Joint Strength of SUS304 Stainless Steel Joint Brazed with Fe-Cr System Alloy" @default.
- W2537058166 cites W2050863603 @default.
- W2537058166 doi "https://doi.org/10.7791/jspmee.4.247" @default.
- W2537058166 hasPublicationYear "2015" @default.
- W2537058166 type Work @default.
- W2537058166 sameAs 2537058166 @default.
- W2537058166 citedByCount "2" @default.
- W2537058166 countsByYear W25370581662016 @default.
- W2537058166 countsByYear W25370581662018 @default.
- W2537058166 crossrefType "journal-article" @default.
- W2537058166 hasAuthorship W2537058166A5008096281 @default.
- W2537058166 hasAuthorship W2537058166A5016544963 @default.
- W2537058166 hasAuthorship W2537058166A5037119704 @default.
- W2537058166 hasAuthorship W2537058166A5047453133 @default.
- W2537058166 hasAuthorship W2537058166A5067877122 @default.
- W2537058166 hasAuthorship W2537058166A5080023007 @default.
- W2537058166 hasBestOaLocation W25370581661 @default.
- W2537058166 hasConcept C120114934 @default.
- W2537058166 hasConcept C127413603 @default.
- W2537058166 hasConcept C159985019 @default.
- W2537058166 hasConcept C18555067 @default.
- W2537058166 hasConcept C191897082 @default.
- W2537058166 hasConcept C192562407 @default.
- W2537058166 hasConcept C19474535 @default.
- W2537058166 hasConcept C20480867 @default.
- W2537058166 hasConcept C2778223994 @default.
- W2537058166 hasConcept C2780026712 @default.
- W2537058166 hasConcept C66938386 @default.
- W2537058166 hasConcept C86171150 @default.
- W2537058166 hasConceptScore W2537058166C120114934 @default.
- W2537058166 hasConceptScore W2537058166C127413603 @default.
- W2537058166 hasConceptScore W2537058166C159985019 @default.
- W2537058166 hasConceptScore W2537058166C18555067 @default.
- W2537058166 hasConceptScore W2537058166C191897082 @default.
- W2537058166 hasConceptScore W2537058166C192562407 @default.
- W2537058166 hasConceptScore W2537058166C19474535 @default.
- W2537058166 hasConceptScore W2537058166C20480867 @default.
- W2537058166 hasConceptScore W2537058166C2778223994 @default.
- W2537058166 hasConceptScore W2537058166C2780026712 @default.
- W2537058166 hasConceptScore W2537058166C66938386 @default.
- W2537058166 hasConceptScore W2537058166C86171150 @default.
- W2537058166 hasIssue "5" @default.
- W2537058166 hasLocation W25370581661 @default.
- W2537058166 hasOpenAccess W2537058166 @default.
- W2537058166 hasPrimaryLocation W25370581661 @default.
- W2537058166 hasRelatedWork W1967161507 @default.
- W2537058166 hasRelatedWork W1968477086 @default.
- W2537058166 hasRelatedWork W2072089000 @default.
- W2537058166 hasRelatedWork W2300988900 @default.
- W2537058166 hasRelatedWork W2366833188 @default.
- W2537058166 hasRelatedWork W2382168649 @default.
- W2537058166 hasRelatedWork W2386909569 @default.
- W2537058166 hasRelatedWork W2413254992 @default.
- W2537058166 hasRelatedWork W2771564978 @default.
- W2537058166 hasRelatedWork W622787089 @default.
- W2537058166 hasVolume "4" @default.
- W2537058166 isParatext "false" @default.
- W2537058166 isRetracted "false" @default.
- W2537058166 magId "2537058166" @default.
- W2537058166 workType "article" @default.