• W2557375519 abstract "2D C/C-SiC composites were fabricated using PIP process by repeated impregnations of porous C/C composite preforms with polycarbosilane followed by pyrolysis. Effect of cyclic heating on flexural and shear strength of these composites was studied by exposing the test specimens to oxyacetylene flame for 20 s and cooling by a blast of air. The cyclic heating tests were repeated up to five times. Average flexural and shear strength of the as fabricated composites were about 330 MPa and 14.5 MPa respectively. After five heating and cooling cycles, average flexural and shear strength were reduced to 120 MPa and 5.5 MPa respectively. SEM, XRD, EDAX and XPS studies were also carried out to investigate the causes of strength reduction. Oxidation started preferentially at carbon matrix through the cut ends of the weft fibers. Oxidative damage due to repeatedly heating cooling was found to be much smaller in through-thickness direction due to passive oxidation of SiC matrix while severe damage was observed parallel to the fabric layers." @default.
• W2557375519 created "2016-12-08" @default.
• W2557375519 creator A5005130976 @default.
• W2557375519 creator A5007777774 @default.
• W2557375519 creator A5020358296 @default.
• W2557375519 creator A5061118316 @default.
• W2557375519 creator A5087493160 @default.
• W2557375519 date "2017-02-01" @default.
• W2557375519 modified "2023-10-13" @default.
• W2557375519 title "Fabrication of 2D C/C-SiC composites using PIP based hybrid process and investigation of mechanical properties degradation under cyclic heating" @default.
• W2557375519 cites W1597120060 @default.
• W2557375519 cites W1979268287 @default.
• W2557375519 cites W1983709680 @default.
• W2557375519 cites W1997317896 @default.
• W2557375519 cites W2014711747 @default.
• W2557375519 cites W2018579928 @default.
• W2557375519 cites W2029013507 @default.
• W2557375519 cites W2034723493 @default.
• W2557375519 cites W2036796009 @default.
• W2557375519 cites W2040283543 @default.
• W2557375519 cites W2047156082 @default.
• W2557375519 cites W2054627418 @default.
• W2557375519 cites W2057061339 @default.
• W2557375519 cites W2066792322 @default.
• W2557375519 cites W2071063063 @default.
• W2557375519 cites W2079687759 @default.
• W2557375519 cites W2083929677 @default.
• W2557375519 cites W2084840374 @default.
• W2557375519 cites W2086914791 @default.
• W2557375519 cites W2096782603 @default.
• W2557375519 cites W2110715513 @default.
• W2557375519 cites W2130895652 @default.
• W2557375519 cites W2140150338 @default.
• W2557375519 cites W2144999621 @default.
• W2557375519 cites W2146035791 @default.
• W2557375519 cites W2146763043 @default.
• W2557375519 cites W2164410079 @default.
• W2557375519 cites W2210854452 @default.
• W2557375519 cites W2298932652 @default.
• W2557375519 cites W2301179374 @default.
• W2557375519 cites W2329906535 @default.
• W2557375519 doi "https://doi.org/10.1016/j.ceramint.2016.11.189" @default.
• W2557375519 hasPublicationYear "2017" @default.
• W2557375519 type Work @default.
• W2557375519 sameAs 2557375519 @default.
• W2557375519 citedByCount "24" @default.
• W2557375519 countsByYear W25573755192017 @default.
• W2557375519 countsByYear W25573755192018 @default.
• W2557375519 countsByYear W25573755192019 @default.
• W2557375519 countsByYear W25573755192020 @default.
• W2557375519 countsByYear W25573755192021 @default.
• W2557375519 countsByYear W25573755192022 @default.
• W2557375519 countsByYear W25573755192023 @default.
• W2557375519 crossrefType "journal-article" @default.
• W2557375519 hasAuthorship W2557375519A5005130976 @default.
• W2557375519 hasAuthorship W2557375519A5007777774 @default.
• W2557375519 hasAuthorship W2557375519A5020358296 @default.
• W2557375519 hasAuthorship W2557375519A5061118316 @default.
• W2557375519 hasAuthorship W2557375519A5087493160 @default.
• W2557375519 hasConcept C104779481 @default.
• W2557375519 hasConcept C120024216 @default.
• W2557375519 hasConcept C121332964 @default.
• W2557375519 hasConcept C127413603 @default.
• W2557375519 hasConcept C127893833 @default.
• W2557375519 hasConcept C136525101 @default.
• W2557375519 hasConcept C142724271 @default.
• W2557375519 hasConcept C159390177 @default.
• W2557375519 hasConcept C159750122 @default.
• W2557375519 hasConcept C159985019 @default.
• W2557375519 hasConcept C175708663 @default.
• W2557375519 hasConcept C178405089 @default.
• W2557375519 hasConcept C192562407 @default.
• W2557375519 hasConcept C204787440 @default.
• W2557375519 hasConcept C2779679103 @default.
• W2557375519 hasConcept C36759035 @default.
• W2557375519 hasConcept C39432304 @default.
• W2557375519 hasConcept C41008148 @default.
• W2557375519 hasConcept C46141821 @default.
• W2557375519 hasConcept C548081761 @default.
• W2557375519 hasConcept C6648577 @default.
• W2557375519 hasConcept C71924100 @default.
• W2557375519 hasConcept C76155785 @default.
• W2557375519 hasConceptScore W2557375519C104779481 @default.
• W2557375519 hasConceptScore W2557375519C120024216 @default.
• W2557375519 hasConceptScore W2557375519C121332964 @default.
• W2557375519 hasConceptScore W2557375519C127413603 @default.
• W2557375519 hasConceptScore W2557375519C127893833 @default.
• W2557375519 hasConceptScore W2557375519C136525101 @default.
• W2557375519 hasConceptScore W2557375519C142724271 @default.
• W2557375519 hasConceptScore W2557375519C159390177 @default.
• W2557375519 hasConceptScore W2557375519C159750122 @default.
• W2557375519 hasConceptScore W2557375519C159985019 @default.
• W2557375519 hasConceptScore W2557375519C175708663 @default.
• W2557375519 hasConceptScore W2557375519C178405089 @default.
• W2557375519 hasConceptScore W2557375519C192562407 @default.
• W2557375519 hasConceptScore W2557375519C204787440 @default.
• W2557375519 hasConceptScore W2557375519C2779679103 @default.
• W2557375519 hasConceptScore W2557375519C36759035 @default.

• next