• W2566428844 abstract "The production of tribological nanoscale multilayer CrN/NbN coatings up to 6 µm thick by Sputtering/HIPIMS has been reported in literature. However, high demanding applications, such as internal combustion engine parts, need thicker coatings (>30 µm). The production of such parts by sputtering would be economically restrictive due to low deposition rates. In this work, nanoscale multilayer CrN/NbN coatings were produced in a high-deposition rate, industrial-size, Cathodic Arc Physical Vapor Deposition (ARC-PVD) chamber, containing three cathodes in alternate positions (Cr/Nb/Cr). Four 30 µm thick NbN/CrN multilayer coatings with different periodicities (20, 10, 7.5 and 4 nm) were produced. The coatings were characterized by X-Ray Diffraction (XRD) and Transmission Electron Microscopy (TEM). The multilayer coating system was composed of alternate cubic rock-salt CrN and NbN layers, coherently strained due to lattice mismatch. The film grew with columnar morphology through the entire stratified structure. The periodicities adopted were maintained throughout the entire coating. The 20 nm periodicity coating showed separate NbN and CrN peaks in the XRD patterns, while for the lower periodicity (≤10nm) coatings, just one intermediate lattice (d-spacing) was detected. An almost linear increase of hardness with decreasing bilayer period indicates that interfacial effects can dominate the hardening mechanisms." @default.
• W2566428844 created "2017-01-06" @default.
• W2566428844 creator A5041006883 @default.
• W2566428844 creator A5051890146 @default.
• W2566428844 creator A5067312456 @default.
• W2566428844 creator A5075919718 @default.
• W2566428844 date "2016-12-19" @default.
• W2566428844 modified "2023-10-03" @default.
• W2566428844 title "Thick CrN/NbN Multilayer Coating Deposited by Cathodic Arc Technique" @default.
• W2566428844 cites W1950916373 @default.
• W2566428844 cites W1968477616 @default.
• W2566428844 cites W1978998438 @default.
• W2566428844 cites W1979753997 @default.
• W2566428844 cites W1983487915 @default.
• W2566428844 cites W1984952151 @default.
• W2566428844 cites W1990089805 @default.
• W2566428844 cites W1997293764 @default.
• W2566428844 cites W1998430613 @default.
• W2566428844 cites W2003223265 @default.
• W2566428844 cites W2005956230 @default.
• W2566428844 cites W2008415031 @default.
• W2566428844 cites W2013527877 @default.
• W2566428844 cites W2014135663 @default.
• W2566428844 cites W2017366062 @default.
• W2566428844 cites W2023053552 @default.
• W2566428844 cites W2029232463 @default.
• W2566428844 cites W2029589171 @default.
• W2566428844 cites W2032282007 @default.
• W2566428844 cites W2040619580 @default.
• W2566428844 cites W2041229711 @default.
• W2566428844 cites W2041324807 @default.
• W2566428844 cites W2044964222 @default.
• W2566428844 cites W2047616290 @default.
• W2566428844 cites W2054227393 @default.
• W2566428844 cites W2056368254 @default.
• W2566428844 cites W2078034946 @default.
• W2566428844 cites W2079907889 @default.
• W2566428844 cites W2086688915 @default.
• W2566428844 cites W2087371977 @default.
• W2566428844 cites W2090350459 @default.
• W2566428844 cites W2100331762 @default.
• W2566428844 cites W2107274894 @default.
• W2566428844 cites W2134137766 @default.
• W2566428844 cites W2147934360 @default.
• W2566428844 cites W2154120439 @default.
• W2566428844 cites W2166382057 @default.
• W2566428844 cites W2291357118 @default.
• W2566428844 cites W4255468385 @default.
• W2566428844 doi "https://doi.org/10.1590/1980-5373-mr-2016-0293" @default.
• W2566428844 hasPublicationYear "2016" @default.
• W2566428844 type Work @default.
• W2566428844 sameAs 2566428844 @default.
• W2566428844 citedByCount "11" @default.
• W2566428844 countsByYear W25664288442017 @default.
• W2566428844 countsByYear W25664288442018 @default.
• W2566428844 countsByYear W25664288442019 @default.
• W2566428844 countsByYear W25664288442020 @default.
• W2566428844 countsByYear W25664288442021 @default.
• W2566428844 countsByYear W25664288442023 @default.
• W2566428844 crossrefType "journal-article" @default.
• W2566428844 hasAuthorship W2566428844A5041006883 @default.
• W2566428844 hasAuthorship W2566428844A5051890146 @default.
• W2566428844 hasAuthorship W2566428844A5067312456 @default.
• W2566428844 hasAuthorship W2566428844A5075919718 @default.
• W2566428844 hasBestOaLocation W25664288441 @default.
• W2566428844 hasConcept C146088050 @default.
• W2566428844 hasConcept C159985019 @default.
• W2566428844 hasConcept C171250308 @default.
• W2566428844 hasConcept C19067145 @default.
• W2566428844 hasConcept C191897082 @default.
• W2566428844 hasConcept C192562407 @default.
• W2566428844 hasConcept C22423302 @default.
• W2566428844 hasConcept C2781448156 @default.
• W2566428844 hasConcept C45206210 @default.
• W2566428844 hasConcept C51576277 @default.
• W2566428844 hasConcept C61427134 @default.
• W2566428844 hasConceptScore W2566428844C146088050 @default.
• W2566428844 hasConceptScore W2566428844C159985019 @default.
• W2566428844 hasConceptScore W2566428844C171250308 @default.
• W2566428844 hasConceptScore W2566428844C19067145 @default.
• W2566428844 hasConceptScore W2566428844C191897082 @default.
• W2566428844 hasConceptScore W2566428844C192562407 @default.
• W2566428844 hasConceptScore W2566428844C22423302 @default.
• W2566428844 hasConceptScore W2566428844C2781448156 @default.
• W2566428844 hasConceptScore W2566428844C45206210 @default.
• W2566428844 hasConceptScore W2566428844C51576277 @default.
• W2566428844 hasConceptScore W2566428844C61427134 @default.
• W2566428844 hasIssue "1" @default.
• W2566428844 hasLocation W25664288441 @default.
• W2566428844 hasLocation W25664288442 @default.
• W2566428844 hasLocation W25664288443 @default.
• W2566428844 hasOpenAccess W2566428844 @default.
• W2566428844 hasPrimaryLocation W25664288441 @default.
• W2566428844 hasRelatedWork W1671997990 @default.
• W2566428844 hasRelatedWork W1963504437 @default.
• W2566428844 hasRelatedWork W1968373997 @default.
• W2566428844 hasRelatedWork W1988448510 @default.
• W2566428844 hasRelatedWork W2029355201 @default.

• next