- W2573536706 abstract "CuO/ZnO nanocomposites with 4 at. % CuO were annealed in air at various temperatures between 100 and 1200 °C to produce Cu-doped ZnO nanocrystals. X-ray diffraction shows that a CuO phase can be observed in the CuO/ZnO nanocomposites annealed at different temperatures, and the Cu-doped ZnO nanocrystals are identified to be of wurtzite structure. The main peak (101) appears at slightly lower diffraction angles with increasing annealing temperature from 400 up to 1200 °C, which confirms the successful doping of Cu into the ZnO lattice above 400 °C. Scanning electron microscopy indicates that most particles in the CuO/ZnO nanocomposites are isolated when annealing at 100–400 °C, but these particles have a tendency to form clusters or aggregates as the annealing temperature increases from 700 to 1000 °C. Positron annihilation measurements reveal a large number of vacancy defects in the interface region of the nanocomposites, and they are gradually recovered with increasing annealing temperature up to 1000 °C. Room-temperature ferromagnetism can be observed in the CuO/ZnO nanocomposites, and the magnetization decreases continuously with increasing annealing temperature. However, there may be several different origins of ferromagnetism in the CuO/ZnO nanocomposites. At low annealing temperatures, the ferromagnetism originates from the CuO nanograins, and the ferromagnetism of CuO nanograins decreases with an increase in the grain size after subsequent higher temperature annealing, which leads to the weakening of ferromagnetism in the CuO/ZnO nanocomposites. After annealing from 400 to 1000 °C, the ferromagnetism gradually vanishes. The ferromagnetism is probably induced by Cu substitution but is mediated by vacancy defects in the CuO/ZnO nanocomposites. The disappearance of ferromagnetism coincides well with the recovery of vacancy defects. It can be inferred that the ferromagnetism is mediated by vacancy defects that are distributed in the interface region." @default.
- W2573536706 created "2017-01-26" @default.
- W2573536706 creator A5009965853 @default.
- W2573536706 creator A5010772151 @default.
- W2573536706 creator A5034607443 @default.
- W2573536706 creator A5056764566 @default.
- W2573536706 creator A5067666102 @default.
- W2573536706 creator A5074754590 @default.
- W2573536706 creator A5081153716 @default.
- W2573536706 creator A5041105110 @default.
- W2573536706 date "2017-01-12" @default.
- W2573536706 modified "2023-10-18" @default.
- W2573536706 title "Defect evolution and its impact on the ferromagnetism of Cu-doped ZnO nanocrystals upon thermal treatment: A positron annihilation study" @default.
- W2573536706 cites W1549548166 @default.
- W2573536706 cites W1652302089 @default.
- W2573536706 cites W1969200114 @default.
- W2573536706 cites W1970609092 @default.
- W2573536706 cites W1971613182 @default.
- W2573536706 cites W1973703973 @default.
- W2573536706 cites W1975055033 @default.
- W2573536706 cites W1979955306 @default.
- W2573536706 cites W1983917857 @default.
- W2573536706 cites W1985889637 @default.
- W2573536706 cites W1993974592 @default.
- W2573536706 cites W1994821152 @default.
- W2573536706 cites W1998587619 @default.
- W2573536706 cites W2001819024 @default.
- W2573536706 cites W2003148904 @default.
- W2573536706 cites W2004040475 @default.
- W2573536706 cites W2005024190 @default.
- W2573536706 cites W2007461175 @default.
- W2573536706 cites W2009202784 @default.
- W2573536706 cites W2013285380 @default.
- W2573536706 cites W2015544346 @default.
- W2573536706 cites W2021143539 @default.
- W2573536706 cites W2028515748 @default.
- W2573536706 cites W2036184053 @default.
- W2573536706 cites W2040850509 @default.
- W2573536706 cites W2048184654 @default.
- W2573536706 cites W2053251031 @default.
- W2573536706 cites W2059312061 @default.
- W2573536706 cites W2066678422 @default.
- W2573536706 cites W2067214999 @default.
- W2573536706 cites W2069618075 @default.
- W2573536706 cites W2069754809 @default.
- W2573536706 cites W2070413347 @default.
- W2573536706 cites W2070949091 @default.
- W2573536706 cites W2086595590 @default.
- W2573536706 cites W2088526887 @default.
- W2573536706 cites W2093907939 @default.
- W2573536706 cites W2108983307 @default.
- W2573536706 cites W2110231396 @default.
- W2573536706 cites W2110872931 @default.
- W2573536706 cites W2115719017 @default.
- W2573536706 cites W2146941399 @default.
- W2573536706 cites W2147632075 @default.
- W2573536706 cites W2207520130 @default.
- W2573536706 cites W2218312957 @default.
- W2573536706 doi "https://doi.org/10.1063/1.4973960" @default.
- W2573536706 hasPublicationYear "2017" @default.
- W2573536706 type Work @default.
- W2573536706 sameAs 2573536706 @default.
- W2573536706 citedByCount "2" @default.
- W2573536706 countsByYear W25735367062017 @default.
- W2573536706 countsByYear W25735367062018 @default.
- W2573536706 crossrefType "journal-article" @default.
- W2573536706 hasAuthorship W2573536706A5009965853 @default.
- W2573536706 hasAuthorship W2573536706A5010772151 @default.
- W2573536706 hasAuthorship W2573536706A5034607443 @default.
- W2573536706 hasAuthorship W2573536706A5041105110 @default.
- W2573536706 hasAuthorship W2573536706A5056764566 @default.
- W2573536706 hasAuthorship W2573536706A5067666102 @default.
- W2573536706 hasAuthorship W2573536706A5074754590 @default.
- W2573536706 hasAuthorship W2573536706A5081153716 @default.
- W2573536706 hasConcept C115260700 @default.
- W2573536706 hasConcept C121332964 @default.
- W2573536706 hasConcept C171250308 @default.
- W2573536706 hasConcept C191897082 @default.
- W2573536706 hasConcept C192562407 @default.
- W2573536706 hasConcept C26873012 @default.
- W2573536706 hasConcept C2777855556 @default.
- W2573536706 hasConcept C3045981 @default.
- W2573536706 hasConcept C32546565 @default.
- W2573536706 hasConcept C49040817 @default.
- W2573536706 hasConcept C535196362 @default.
- W2573536706 hasConcept C57863236 @default.
- W2573536706 hasConcept C62520636 @default.
- W2573536706 hasConcept C82217956 @default.
- W2573536706 hasConcept C92880739 @default.
- W2573536706 hasConceptScore W2573536706C115260700 @default.
- W2573536706 hasConceptScore W2573536706C121332964 @default.
- W2573536706 hasConceptScore W2573536706C171250308 @default.
- W2573536706 hasConceptScore W2573536706C191897082 @default.
- W2573536706 hasConceptScore W2573536706C192562407 @default.
- W2573536706 hasConceptScore W2573536706C26873012 @default.
- W2573536706 hasConceptScore W2573536706C2777855556 @default.
- W2573536706 hasConceptScore W2573536706C3045981 @default.
- W2573536706 hasConceptScore W2573536706C32546565 @default.
- W2573536706 hasConceptScore W2573536706C49040817 @default.
- W2573536706 hasConceptScore W2573536706C535196362 @default.