- W2582818895 abstract "Friction and wear behavior of Polyoxymethylene/Poly (lactic acid) blends (POM/PLA) was investigated to study effect of PLA content on friction and wear properties. The sliding experiments were carried out by Frictoron EFM-III machine. POM blends sliding against the carbon steel (AISI 1045) counterpart under 200 N of pressure load, 100 mm/s of sliding speed for 60 minutes. The wear weigh loss was measured after wear experiment. Wear profile and worn surface were observed by SEM. It was found that friction coefficient of neat POM is lower than neat PLA. However, the incorporation of PLA into POM led to an increment of friction coefficient of POM blends both of 40% and 60% PLA content that over than neat POM and PLA. While wear weigh loss resulted the increasing with increasing of PLA content, which were supported by wear prolife photographs. The deformation of neat PLA and blends on worn surface originated from adhesive due to the thermal softening and melting behavior, while neat POM reveals the plough action behavior." @default.
- W2582818895 created "2017-02-03" @default.
- W2582818895 creator A5010194351 @default.
- W2582818895 creator A5023321773 @default.
- W2582818895 creator A5026738758 @default.
- W2582818895 creator A5046503970 @default.
- W2582818895 date "2017-01-25" @default.
- W2582818895 modified "2023-09-30" @default.
- W2582818895 title "Investigation of Friction and Wear Behavior of Polyoxymethylene/Poly(Lactic Acid) Blends" @default.
- W2582818895 cites W1572918274 @default.
- W2582818895 cites W1967229430 @default.
- W2582818895 cites W1979432348 @default.
- W2582818895 cites W1996448847 @default.
- W2582818895 cites W2037487780 @default.
- W2582818895 cites W2037604913 @default.
- W2582818895 cites W2052464822 @default.
- W2582818895 cites W2074130198 @default.
- W2582818895 cites W2159814997 @default.
- W2582818895 doi "https://doi.org/10.4028/www.scientific.net/kem.728.229" @default.
- W2582818895 hasPublicationYear "2017" @default.
- W2582818895 type Work @default.
- W2582818895 sameAs 2582818895 @default.
- W2582818895 citedByCount "8" @default.
- W2582818895 countsByYear W25828188952019 @default.
- W2582818895 countsByYear W25828188952020 @default.
- W2582818895 countsByYear W25828188952021 @default.
- W2582818895 countsByYear W25828188952022 @default.
- W2582818895 crossrefType "journal-article" @default.
- W2582818895 hasAuthorship W2582818895A5010194351 @default.
- W2582818895 hasAuthorship W2582818895A5023321773 @default.
- W2582818895 hasAuthorship W2582818895A5026738758 @default.
- W2582818895 hasAuthorship W2582818895A5046503970 @default.
- W2582818895 hasConcept C159985019 @default.
- W2582818895 hasConcept C192562407 @default.
- W2582818895 hasConcept C2776904851 @default.
- W2582818895 hasConcept C2779227376 @default.
- W2582818895 hasConcept C2781098093 @default.
- W2582818895 hasConcept C2989152160 @default.
- W2582818895 hasConcept C521977710 @default.
- W2582818895 hasConcept C68928338 @default.
- W2582818895 hasConceptScore W2582818895C159985019 @default.
- W2582818895 hasConceptScore W2582818895C192562407 @default.
- W2582818895 hasConceptScore W2582818895C2776904851 @default.
- W2582818895 hasConceptScore W2582818895C2779227376 @default.
- W2582818895 hasConceptScore W2582818895C2781098093 @default.
- W2582818895 hasConceptScore W2582818895C2989152160 @default.
- W2582818895 hasConceptScore W2582818895C521977710 @default.
- W2582818895 hasConceptScore W2582818895C68928338 @default.
- W2582818895 hasLocation W25828188951 @default.
- W2582818895 hasOpenAccess W2582818895 @default.
- W2582818895 hasPrimaryLocation W25828188951 @default.
- W2582818895 hasRelatedWork W1974442171 @default.
- W2582818895 hasRelatedWork W2082293200 @default.
- W2582818895 hasRelatedWork W2137307547 @default.
- W2582818895 hasRelatedWork W2380293314 @default.
- W2582818895 hasRelatedWork W2582818895 @default.
- W2582818895 hasRelatedWork W2943188944 @default.
- W2582818895 hasRelatedWork W3008690834 @default.
- W2582818895 hasRelatedWork W3082440218 @default.
- W2582818895 hasRelatedWork W4242480814 @default.
- W2582818895 hasRelatedWork W4285802202 @default.
- W2582818895 hasVolume "728" @default.
- W2582818895 isParatext "false" @default.
- W2582818895 isRetracted "false" @default.
- W2582818895 magId "2582818895" @default.
- W2582818895 workType "article" @default.