- W2587830023 abstract "Abstract Strain controlled fatigue tests have been performed on two types of heavily filled epoxy corrosion protection coating sprayed onto a 6 mm steel substrate. Fatigue cycling was performed at R ratios of 0 and −1. The two coatings differed in their formulation and the major differences in mechanical performance were in their static strain to first crack development and their fracture toughness, where Coating A was significantly tougher than coating B. During strain cycling coating crack development was monitored using optical observations and surface replicas. It was found that in both coatings surface crack development began soon after the onset of cycling and proceeded via growth of surface channelling cracks and multiple initiation of new cracks. Detailed studies were made of crack development morphology and its relation to coating type and to the applied strain range. A definition of coating life as the first appearance of a 2 mm surface crack length was used. This represented the end of the life where the coating protected the substrate. Before this life was achieved, crack growth rates of single cracks were invariant with crack length. After this point further crack growth, multiple cracking and crack to crack interactions took place. Cracking in this region could be characterised with a new total crack length parameter shown to be strongly dependent on applied strain range." @default.
- W2587830023 created "2017-02-24" @default.
- W2587830023 creator A5002561789 @default.
- W2587830023 creator A5025576549 @default.
- W2587830023 creator A5034518449 @default.
- W2587830023 creator A5037061413 @default.
- W2587830023 creator A5081452608 @default.
- W2587830023 date "2017-06-01" @default.
- W2587830023 modified "2023-09-27" @default.
- W2587830023 title "Fatigue cracking behaviour of epoxy-based marine coatings on steel substrate under cyclic tension" @default.
- W2587830023 cites W1549923431 @default.
- W2587830023 cites W1580758131 @default.
- W2587830023 cites W1991381870 @default.
- W2587830023 cites W1991471570 @default.
- W2587830023 cites W1995805074 @default.
- W2587830023 cites W2005742019 @default.
- W2587830023 cites W2008061866 @default.
- W2587830023 cites W2013720906 @default.
- W2587830023 cites W2013981336 @default.
- W2587830023 cites W2015907760 @default.
- W2587830023 cites W2043990260 @default.
- W2587830023 cites W2050471950 @default.
- W2587830023 cites W2052722765 @default.
- W2587830023 cites W2056706911 @default.
- W2587830023 cites W2057992002 @default.
- W2587830023 cites W2062613656 @default.
- W2587830023 cites W2094708596 @default.
- W2587830023 cites W2103147779 @default.
- W2587830023 cites W2114423906 @default.
- W2587830023 cites W2132281155 @default.
- W2587830023 cites W2135720994 @default.
- W2587830023 cites W2143589752 @default.
- W2587830023 cites W2291550768 @default.
- W2587830023 doi "https://doi.org/10.1016/j.ijfatigue.2017.02.010" @default.
- W2587830023 hasPublicationYear "2017" @default.
- W2587830023 type Work @default.
- W2587830023 sameAs 2587830023 @default.
- W2587830023 citedByCount "6" @default.
- W2587830023 countsByYear W25878300232019 @default.
- W2587830023 countsByYear W25878300232021 @default.
- W2587830023 countsByYear W25878300232022 @default.
- W2587830023 countsByYear W25878300232023 @default.
- W2587830023 crossrefType "journal-article" @default.
- W2587830023 hasAuthorship W2587830023A5002561789 @default.
- W2587830023 hasAuthorship W2587830023A5025576549 @default.
- W2587830023 hasAuthorship W2587830023A5034518449 @default.
- W2587830023 hasAuthorship W2587830023A5037061413 @default.
- W2587830023 hasAuthorship W2587830023A5081452608 @default.
- W2587830023 hasBestOaLocation W25878300232 @default.
- W2587830023 hasConcept C111368507 @default.
- W2587830023 hasConcept C112950240 @default.
- W2587830023 hasConcept C127313418 @default.
- W2587830023 hasConcept C159985019 @default.
- W2587830023 hasConcept C166595027 @default.
- W2587830023 hasConcept C186068551 @default.
- W2587830023 hasConcept C191897082 @default.
- W2587830023 hasConcept C192562407 @default.
- W2587830023 hasConcept C2777289219 @default.
- W2587830023 hasConcept C3020080851 @default.
- W2587830023 hasConcept C58396970 @default.
- W2587830023 hasConcept C61039299 @default.
- W2587830023 hasConceptScore W2587830023C111368507 @default.
- W2587830023 hasConceptScore W2587830023C112950240 @default.
- W2587830023 hasConceptScore W2587830023C127313418 @default.
- W2587830023 hasConceptScore W2587830023C159985019 @default.
- W2587830023 hasConceptScore W2587830023C166595027 @default.
- W2587830023 hasConceptScore W2587830023C186068551 @default.
- W2587830023 hasConceptScore W2587830023C191897082 @default.
- W2587830023 hasConceptScore W2587830023C192562407 @default.
- W2587830023 hasConceptScore W2587830023C2777289219 @default.
- W2587830023 hasConceptScore W2587830023C3020080851 @default.
- W2587830023 hasConceptScore W2587830023C58396970 @default.
- W2587830023 hasConceptScore W2587830023C61039299 @default.
- W2587830023 hasFunder F4320321765 @default.
- W2587830023 hasLocation W25878300231 @default.
- W2587830023 hasLocation W25878300232 @default.
- W2587830023 hasOpenAccess W2587830023 @default.
- W2587830023 hasPrimaryLocation W25878300231 @default.
- W2587830023 hasRelatedWork W2003266812 @default.
- W2587830023 hasRelatedWork W2015297691 @default.
- W2587830023 hasRelatedWork W2093762090 @default.
- W2587830023 hasRelatedWork W2098986329 @default.
- W2587830023 hasRelatedWork W2117665458 @default.
- W2587830023 hasRelatedWork W2376820830 @default.
- W2587830023 hasRelatedWork W2587830023 @default.
- W2587830023 hasRelatedWork W2593200884 @default.
- W2587830023 hasRelatedWork W2955807060 @default.
- W2587830023 hasRelatedWork W4323539025 @default.
- W2587830023 hasVolume "99" @default.
- W2587830023 isParatext "false" @default.
- W2587830023 isRetracted "false" @default.
- W2587830023 magId "2587830023" @default.
- W2587830023 workType "article" @default.