- W2590603525 abstract "Adhesive bonded tee joints are being used excessively in civil, military aircraft and ship building industries to join light weight Fiber reinforced Polymeric (FRP) laminates to other metal or composite structures. The mismatch of thermo-mechanical properties between adherend and adhesive bond line induces residual curing stresses even during manufacturing stages resulting in unaccounted failure and fracture behaviour of adhesive joints. The present work investigates the influence of bimodulus behaviour of adhesive and curing stresses on interface delamination fracture behaviour of tee joints by conducting a sequential thermal and geometrically non-linear finite element analysis (FEA) iteratively for evaluating strain energy release rate along the delamination front. The stress dependent elasticity problem of interface fracture has been studied based on the concepts of Modified Crack Closure Integral (MCCI) for different numerical specimens with tension compression modulus ratio R varying from 1 to 5 along the bond line for the respective functionally graded bimodular adhesively bonded tee joint. It is illustrated that the variation of bimodularity index has a strong influence on the interface delamination crack propagation characteristics apart from the other aspects of functionally grading and thermo-elastic anisotropy. The influence of bimodularity in comparison to functionally grading is found to be much more significant on mixed-mode fracture behaviour depicting dissimilar variation of GI, GII and GIII along the interface failure front indicating retardation of the interfacial failure propagation rate over certain zones of adherend." @default.
- W2590603525 created "2017-03-03" @default.
- W2590603525 creator A5052994118 @default.
- W2590603525 creator A5072766032 @default.
- W2590603525 date "2017-06-01" @default.
- W2590603525 modified "2023-09-30" @default.
- W2590603525 title "Bimodularity of interface layer and curing stress coupling effects on mixed mode fracture behaviour of functionally graded tee joint" @default.
- W2590603525 cites W1812635900 @default.
- W2590603525 cites W1963558905 @default.
- W2590603525 cites W1964898194 @default.
- W2590603525 cites W1972237669 @default.
- W2590603525 cites W1976742906 @default.
- W2590603525 cites W1979571099 @default.
- W2590603525 cites W1983567954 @default.
- W2590603525 cites W1984851472 @default.
- W2590603525 cites W1997372248 @default.
- W2590603525 cites W2009556086 @default.
- W2590603525 cites W2013253613 @default.
- W2590603525 cites W2015799030 @default.
- W2590603525 cites W2021014106 @default.
- W2590603525 cites W2028062793 @default.
- W2590603525 cites W2044343352 @default.
- W2590603525 cites W2049669134 @default.
- W2590603525 cites W2061326725 @default.
- W2590603525 cites W2064695005 @default.
- W2590603525 cites W2067012805 @default.
- W2590603525 cites W2068626666 @default.
- W2590603525 cites W2086282310 @default.
- W2590603525 cites W2090869573 @default.
- W2590603525 cites W2091316899 @default.
- W2590603525 cites W2094054810 @default.
- W2590603525 cites W2114974348 @default.
- W2590603525 cites W2138737116 @default.
- W2590603525 cites W2165667665 @default.
- W2590603525 cites W2170449854 @default.
- W2590603525 cites W2226557076 @default.
- W2590603525 cites W2340375578 @default.
- W2590603525 cites W3106768301 @default.
- W2590603525 doi "https://doi.org/10.1016/j.ijadhadh.2017.02.016" @default.
- W2590603525 hasPublicationYear "2017" @default.
- W2590603525 type Work @default.
- W2590603525 sameAs 2590603525 @default.
- W2590603525 citedByCount "9" @default.
- W2590603525 countsByYear W25906035252017 @default.
- W2590603525 countsByYear W25906035252019 @default.
- W2590603525 countsByYear W25906035252020 @default.
- W2590603525 countsByYear W25906035252021 @default.
- W2590603525 countsByYear W25906035252022 @default.
- W2590603525 countsByYear W25906035252023 @default.
- W2590603525 crossrefType "journal-article" @default.
- W2590603525 hasAuthorship W2590603525A5052994118 @default.
- W2590603525 hasAuthorship W2590603525A5072766032 @default.
- W2590603525 hasConcept C127413603 @default.
- W2590603525 hasConcept C132976073 @default.
- W2590603525 hasConcept C135628077 @default.
- W2590603525 hasConcept C159985019 @default.
- W2590603525 hasConcept C18555067 @default.
- W2590603525 hasConcept C192562407 @default.
- W2590603525 hasConcept C2779227376 @default.
- W2590603525 hasConcept C2779278059 @default.
- W2590603525 hasConcept C32860805 @default.
- W2590603525 hasConcept C37292000 @default.
- W2590603525 hasConcept C59085676 @default.
- W2590603525 hasConcept C66938386 @default.
- W2590603525 hasConcept C68928338 @default.
- W2590603525 hasConceptScore W2590603525C127413603 @default.
- W2590603525 hasConceptScore W2590603525C132976073 @default.
- W2590603525 hasConceptScore W2590603525C135628077 @default.
- W2590603525 hasConceptScore W2590603525C159985019 @default.
- W2590603525 hasConceptScore W2590603525C18555067 @default.
- W2590603525 hasConceptScore W2590603525C192562407 @default.
- W2590603525 hasConceptScore W2590603525C2779227376 @default.
- W2590603525 hasConceptScore W2590603525C2779278059 @default.
- W2590603525 hasConceptScore W2590603525C32860805 @default.
- W2590603525 hasConceptScore W2590603525C37292000 @default.
- W2590603525 hasConceptScore W2590603525C59085676 @default.
- W2590603525 hasConceptScore W2590603525C66938386 @default.
- W2590603525 hasConceptScore W2590603525C68928338 @default.
- W2590603525 hasLocation W25906035251 @default.
- W2590603525 hasOpenAccess W2590603525 @default.
- W2590603525 hasPrimaryLocation W25906035251 @default.
- W2590603525 hasRelatedWork W1039848210 @default.
- W2590603525 hasRelatedWork W1971311335 @default.
- W2590603525 hasRelatedWork W2033800547 @default.
- W2590603525 hasRelatedWork W2061261354 @default.
- W2590603525 hasRelatedWork W2064444835 @default.
- W2590603525 hasRelatedWork W2248272060 @default.
- W2590603525 hasRelatedWork W2286282238 @default.
- W2590603525 hasRelatedWork W2793407960 @default.
- W2590603525 hasRelatedWork W2904220176 @default.
- W2590603525 hasRelatedWork W2411832254 @default.
- W2590603525 hasVolume "75" @default.
- W2590603525 isParatext "false" @default.
- W2590603525 isRetracted "false" @default.
- W2590603525 magId "2590603525" @default.
- W2590603525 workType "article" @default.