- W2593376098 abstract "In order to protect parts against wear, the carbon steel used are commonly coated by cermet coatings to increase the wear resistance. In this paper, the coatings consist of tungsten carbide 17wt% cobalt (WC-17Co), tungsten carbide 9wt% nickel (WC-9Ni), electrodeposited nickel (electro Ni) and electrodeposited nickel-silicon carbide (electro Ni-SiC) coatings. All coatings are deposited onto AISI 1018 carbon steel by using two different methods which are high velocity oxygen fuel (HVOF) and co-electrodeposition method. Abrasive wear test were observed under two‑body dry abrasion conditions with pin-on-disc test arrangement. Based on the volume loss after the wear test, the wear rates were calculated by using Archard’s law. The wear tracks of the coatings were investigated by using scanning electron microscope (SEM) and atomic force microscopy (AFM). The hardness of each coating was measured by using Vickers microhardness. The results showed that HVOF coatings have lower wear rate compared to the electrodeposited coatings. WC-9Ni has the lowest wear rate which is 4.06×10 -3 mm 3 /Nm much lower compared to electro Ni-SiC of 16.36×10 -3 mm 3 /Nm. This result was expected as the hardness of WC-9Ni is 1625.37 HV higher than electrodeposited coatings which approximately 380.51 HV. In conclusion, the methods of coating deposited affect the wear resistance as well as the hardness of the coatings." @default.
- W2593376098 created "2017-03-16" @default.
- W2593376098 creator A5026546040 @default.
- W2593376098 creator A5067212084 @default.
- W2593376098 date "2017-03-01" @default.
- W2593376098 modified "2023-09-27" @default.
- W2593376098 title "Two-Body Dry Abrasive Wear Performance of High Velocity Oxygen Fuel Spray Process and Electrodeposited Cermet Coatings" @default.
- W2593376098 cites W1819534215 @default.
- W2593376098 cites W1981723753 @default.
- W2593376098 cites W1995035098 @default.
- W2593376098 cites W2003528973 @default.
- W2593376098 cites W2021712103 @default.
- W2593376098 cites W2023468583 @default.
- W2593376098 cites W2027110149 @default.
- W2593376098 cites W2031189610 @default.
- W2593376098 cites W2033225141 @default.
- W2593376098 cites W2056839304 @default.
- W2593376098 cites W2075060586 @default.
- W2593376098 cites W2076688440 @default.
- W2593376098 cites W2083274338 @default.
- W2593376098 cites W2095507689 @default.
- W2593376098 cites W2122866066 @default.
- W2593376098 cites W2163328551 @default.
- W2593376098 cites W2183606052 @default.
- W2593376098 cites W2498883961 @default.
- W2593376098 cites W2604247092 @default.
- W2593376098 doi "https://doi.org/10.4028/www.scientific.net/msf.888.131" @default.
- W2593376098 hasPublicationYear "2017" @default.
- W2593376098 type Work @default.
- W2593376098 sameAs 2593376098 @default.
- W2593376098 citedByCount "1" @default.
- W2593376098 countsByYear W25933760982019 @default.
- W2593376098 crossrefType "journal-article" @default.
- W2593376098 hasAuthorship W2593376098A5026546040 @default.
- W2593376098 hasAuthorship W2593376098A5067212084 @default.
- W2593376098 hasConcept C118231568 @default.
- W2593376098 hasConcept C134132462 @default.
- W2593376098 hasConcept C134646822 @default.
- W2593376098 hasConcept C149669645 @default.
- W2593376098 hasConcept C159985019 @default.
- W2593376098 hasConcept C165720898 @default.
- W2593376098 hasConcept C191897082 @default.
- W2593376098 hasConcept C192562407 @default.
- W2593376098 hasConcept C26771246 @default.
- W2593376098 hasConcept C2780957350 @default.
- W2593376098 hasConcept C2781422231 @default.
- W2593376098 hasConcept C2781448156 @default.
- W2593376098 hasConcept C515602321 @default.
- W2593376098 hasConcept C542268612 @default.
- W2593376098 hasConcept C87976508 @default.
- W2593376098 hasConceptScore W2593376098C118231568 @default.
- W2593376098 hasConceptScore W2593376098C134132462 @default.
- W2593376098 hasConceptScore W2593376098C134646822 @default.
- W2593376098 hasConceptScore W2593376098C149669645 @default.
- W2593376098 hasConceptScore W2593376098C159985019 @default.
- W2593376098 hasConceptScore W2593376098C165720898 @default.
- W2593376098 hasConceptScore W2593376098C191897082 @default.
- W2593376098 hasConceptScore W2593376098C192562407 @default.
- W2593376098 hasConceptScore W2593376098C26771246 @default.
- W2593376098 hasConceptScore W2593376098C2780957350 @default.
- W2593376098 hasConceptScore W2593376098C2781422231 @default.
- W2593376098 hasConceptScore W2593376098C2781448156 @default.
- W2593376098 hasConceptScore W2593376098C515602321 @default.
- W2593376098 hasConceptScore W2593376098C542268612 @default.
- W2593376098 hasConceptScore W2593376098C87976508 @default.
- W2593376098 hasLocation W25933760981 @default.
- W2593376098 hasOpenAccess W2593376098 @default.
- W2593376098 hasPrimaryLocation W25933760981 @default.
- W2593376098 hasRelatedWork W2037367310 @default.
- W2593376098 hasRelatedWork W2054292554 @default.
- W2593376098 hasRelatedWork W2055643292 @default.
- W2593376098 hasRelatedWork W2078653494 @default.
- W2593376098 hasRelatedWork W2091698914 @default.
- W2593376098 hasRelatedWork W2156829121 @default.
- W2593376098 hasRelatedWork W2199648861 @default.
- W2593376098 hasRelatedWork W2360023091 @default.
- W2593376098 hasRelatedWork W2369094935 @default.
- W2593376098 hasRelatedWork W2374755190 @default.
- W2593376098 hasRelatedWork W2376117833 @default.
- W2593376098 hasRelatedWork W2382171187 @default.
- W2593376098 hasRelatedWork W2518343394 @default.
- W2593376098 hasRelatedWork W2756183117 @default.
- W2593376098 hasRelatedWork W2907458932 @default.
- W2593376098 hasRelatedWork W2943178510 @default.
- W2593376098 hasRelatedWork W3082200258 @default.
- W2593376098 hasRelatedWork W2189397422 @default.
- W2593376098 hasRelatedWork W2795869018 @default.
- W2593376098 hasRelatedWork W2802710047 @default.
- W2593376098 isParatext "false" @default.
- W2593376098 isRetracted "false" @default.
- W2593376098 magId "2593376098" @default.
- W2593376098 workType "article" @default.