- W2605776980 abstract "Electrical resistivity was measured on specimens aged at temperatures between 273 and 423 K for various times after quenching from temperatures Tq between 623 and 823 K. oindent(1) Resistivity increases in two stages during isothermal aging below 403±5 K, which is in good agreement with the solvus temperature of G. P. zones, irrespective of Tq value. The precipitation below 403 K is a competitive reaction of (I) growth of G. P. zones and (II) formation of δ″ particles (short-range ordered Al3Li). The first and second stages of resistivity increase are attributed mainly to the reactions (I) and (II) respectively. (2) With the reaction (II), the resistivity decreases initially and then increases, exhibiting a tendency to show no resistivity-peak. This resistivity increase makes a sharp contrast with the occurrence of resistivity-peak associated with the reaction (I). (3) The reaction (I) is retarded while the reaction (II) is accelerated with increasing Tq. The retardation effect of high Tq on the reaction (I) decreases with decreasing prequench heating time at the Tq. These results suggest that the distributions of both vacancy and solute atom (Li) in the solid solution become non-random with increasing heating time at the Tq. (4) The activation energies for the reactions (I) and (II) were estimated respectively to be 67.5±5 and 110±7 kJ/mol, which may be assigned to migration energies of free vacancy and vacancy-Li pair." @default.
- W2605776980 created "2017-04-28" @default.
- W2605776980 creator A5048782454 @default.
- W2605776980 creator A5071262624 @default.
- W2605776980 creator A5086834179 @default.
- W2605776980 date "1980-01-01" @default.
- W2605776980 modified "2023-10-16" @default.
- W2605776980 title "Early Stage of Low-Temperature Aging in an Al-1.7 mass%Li Alloy" @default.
- W2605776980 cites W2061131554 @default.
- W2605776980 doi "https://doi.org/10.2320/jinstmet1952.44.11_1203" @default.
- W2605776980 hasPublicationYear "1980" @default.
- W2605776980 type Work @default.
- W2605776980 sameAs 2605776980 @default.
- W2605776980 citedByCount "10" @default.
- W2605776980 countsByYear W26057769802012 @default.
- W2605776980 crossrefType "journal-article" @default.
- W2605776980 hasAuthorship W2605776980A5048782454 @default.
- W2605776980 hasAuthorship W2605776980A5071262624 @default.
- W2605776980 hasAuthorship W2605776980A5086834179 @default.
- W2605776980 hasBestOaLocation W26057769801 @default.
- W2605776980 hasConcept C107054158 @default.
- W2605776980 hasConcept C113196181 @default.
- W2605776980 hasConcept C114221277 @default.
- W2605776980 hasConcept C119599485 @default.
- W2605776980 hasConcept C121332964 @default.
- W2605776980 hasConcept C121745418 @default.
- W2605776980 hasConcept C127413603 @default.
- W2605776980 hasConcept C133347239 @default.
- W2605776980 hasConcept C147789679 @default.
- W2605776980 hasConcept C153294291 @default.
- W2605776980 hasConcept C185592680 @default.
- W2605776980 hasConcept C191897082 @default.
- W2605776980 hasConcept C192562407 @default.
- W2605776980 hasConcept C207055975 @default.
- W2605776980 hasConcept C21800796 @default.
- W2605776980 hasConcept C2780026712 @default.
- W2605776980 hasConcept C43617362 @default.
- W2605776980 hasConcept C62520636 @default.
- W2605776980 hasConcept C69990965 @default.
- W2605776980 hasConcept C8010536 @default.
- W2605776980 hasConcept C91881484 @default.
- W2605776980 hasConcept C95121573 @default.
- W2605776980 hasConcept C97355855 @default.
- W2605776980 hasConceptScore W2605776980C107054158 @default.
- W2605776980 hasConceptScore W2605776980C113196181 @default.
- W2605776980 hasConceptScore W2605776980C114221277 @default.
- W2605776980 hasConceptScore W2605776980C119599485 @default.
- W2605776980 hasConceptScore W2605776980C121332964 @default.
- W2605776980 hasConceptScore W2605776980C121745418 @default.
- W2605776980 hasConceptScore W2605776980C127413603 @default.
- W2605776980 hasConceptScore W2605776980C133347239 @default.
- W2605776980 hasConceptScore W2605776980C147789679 @default.
- W2605776980 hasConceptScore W2605776980C153294291 @default.
- W2605776980 hasConceptScore W2605776980C185592680 @default.
- W2605776980 hasConceptScore W2605776980C191897082 @default.
- W2605776980 hasConceptScore W2605776980C192562407 @default.
- W2605776980 hasConceptScore W2605776980C207055975 @default.
- W2605776980 hasConceptScore W2605776980C21800796 @default.
- W2605776980 hasConceptScore W2605776980C2780026712 @default.
- W2605776980 hasConceptScore W2605776980C43617362 @default.
- W2605776980 hasConceptScore W2605776980C62520636 @default.
- W2605776980 hasConceptScore W2605776980C69990965 @default.
- W2605776980 hasConceptScore W2605776980C8010536 @default.
- W2605776980 hasConceptScore W2605776980C91881484 @default.
- W2605776980 hasConceptScore W2605776980C95121573 @default.
- W2605776980 hasConceptScore W2605776980C97355855 @default.
- W2605776980 hasIssue "11" @default.
- W2605776980 hasLocation W26057769801 @default.
- W2605776980 hasOpenAccess W2605776980 @default.
- W2605776980 hasPrimaryLocation W26057769801 @default.
- W2605776980 hasRelatedWork W1521582694 @default.
- W2605776980 hasRelatedWork W1966394797 @default.
- W2605776980 hasRelatedWork W2022186869 @default.
- W2605776980 hasRelatedWork W2071252532 @default.
- W2605776980 hasRelatedWork W2076603131 @default.
- W2605776980 hasRelatedWork W2174510520 @default.
- W2605776980 hasRelatedWork W2605464325 @default.
- W2605776980 hasRelatedWork W2990402655 @default.
- W2605776980 hasRelatedWork W3154131211 @default.
- W2605776980 hasRelatedWork W53750174 @default.
- W2605776980 hasVolume "44" @default.
- W2605776980 isParatext "false" @default.
- W2605776980 isRetracted "false" @default.
- W2605776980 magId "2605776980" @default.
- W2605776980 workType "article" @default.