- W2606704455 abstract "Tests on sulfide corrosion cracking of weldable high strength structual steels were performed at oil refining plants. The tests were carried out on eight main parts of the oil refining plants, viz., oil storage tank, prefractionator, top and bottom sides of fractionator, stabilizer, stabilizer-receiver, depropanizer-receiver, and vacuum column. The duration of testing was about one year. The results obtained are as follows: (1) Sulfide corrosion cracking was only observed on the test specimens inserted in the stabilizer-reciver, and specimens in other processing units in the plant were found to be unaffected. It was observed that the conditions causing the sulfide corrosion cracking might be attributed to the environment being (a) liquid phase, (b) rich in H2O, (c) rich in active sulfide such as H2S, and (d) subjecting temperature. (2) Types of cracks observed on the test pieces were corrosion cracking on the surfaces, hydrogen blister, and hydrogen crack. (3) The scales removed from the cracked specimen surface were examined and as a result, kansite (Fe9S8) that is closely related to sulfide corrosion cracking was detected by X-ray diffraction. Residual hydrogen in the specimen was rich compared with that in other parts of plants. (4) The corrosion rate of tested materials varied considerably by individual cases, but did not vary to any extent by different heats of steel." @default.
- W2606704455 created "2017-04-28" @default.
- W2606704455 creator A5037205053 @default.
- W2606704455 creator A5048134643 @default.
- W2606704455 creator A5073619026 @default.
- W2606704455 creator A5076401269 @default.
- W2606704455 date "1966-01-01" @default.
- W2606704455 modified "2023-09-26" @default.
- W2606704455 title "Sulfide Corrosion Cracking of Weldable High Strength Steel Plates in Oil Refinining Plants" @default.
- W2606704455 doi "https://doi.org/10.2320/jinstmet1952.30.12_1147" @default.
- W2606704455 hasPublicationYear "1966" @default.
- W2606704455 type Work @default.
- W2606704455 sameAs 2606704455 @default.
- W2606704455 citedByCount "0" @default.
- W2606704455 crossrefType "journal-article" @default.
- W2606704455 hasAuthorship W2606704455A5037205053 @default.
- W2606704455 hasAuthorship W2606704455A5048134643 @default.
- W2606704455 hasAuthorship W2606704455A5073619026 @default.
- W2606704455 hasAuthorship W2606704455A5076401269 @default.
- W2606704455 hasBestOaLocation W26067044551 @default.
- W2606704455 hasConcept C159985019 @default.
- W2606704455 hasConcept C191897082 @default.
- W2606704455 hasConcept C192562407 @default.
- W2606704455 hasConcept C20625102 @default.
- W2606704455 hasConcept C2780564542 @default.
- W2606704455 hasConcept C2780596425 @default.
- W2606704455 hasConcept C518881349 @default.
- W2606704455 hasConcept C58396970 @default.
- W2606704455 hasConceptScore W2606704455C159985019 @default.
- W2606704455 hasConceptScore W2606704455C191897082 @default.
- W2606704455 hasConceptScore W2606704455C192562407 @default.
- W2606704455 hasConceptScore W2606704455C20625102 @default.
- W2606704455 hasConceptScore W2606704455C2780564542 @default.
- W2606704455 hasConceptScore W2606704455C2780596425 @default.
- W2606704455 hasConceptScore W2606704455C518881349 @default.
- W2606704455 hasConceptScore W2606704455C58396970 @default.
- W2606704455 hasIssue "12" @default.
- W2606704455 hasLocation W26067044551 @default.
- W2606704455 hasOpenAccess W2606704455 @default.
- W2606704455 hasPrimaryLocation W26067044551 @default.
- W2606704455 hasRelatedWork W145579800 @default.
- W2606704455 hasRelatedWork W2006221599 @default.
- W2606704455 hasRelatedWork W2335184785 @default.
- W2606704455 hasRelatedWork W2365901306 @default.
- W2606704455 hasRelatedWork W2375670690 @default.
- W2606704455 hasRelatedWork W2383699493 @default.
- W2606704455 hasRelatedWork W2386299628 @default.
- W2606704455 hasRelatedWork W2416044464 @default.
- W2606704455 hasRelatedWork W2762002849 @default.
- W2606704455 hasRelatedWork W3097783663 @default.
- W2606704455 hasVolume "30" @default.
- W2606704455 isParatext "false" @default.
- W2606704455 isRetracted "false" @default.
- W2606704455 magId "2606704455" @default.
- W2606704455 workType "article" @default.