• W2613532425 abstract "Two sets of indium oxide thin films (~150 nm) grown on quartz substrates using thermal evaporation technique were processed separately with 25‐keV Co − and N + ions with several fluences ranging from 1.0 × 10 15 to 1.0 × 10 16 ions/cm 2 . The pristine and the ion implanted films were characterized by Rutherford backscattering spectroscopy (RBS), X‐ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and UV–Vis spectrometry. The RBS spectra reveal signature of only cobalt and nitrogen in accordance to their fluences confirming absence of any contamination arising due to ion implantation. An increase in the average crystallite size (from 13.7 to 15.3 nm) of Co − ions implanted films was confirmed by XRD. On the other hand, the films implanted with N + ions showed a decrease in the average crystallite size from 20.1 to 13.7 nm. The XRD results were further verified by SEM micrographs. As seen in AFM images, the RMS surface roughness of the samples processed by both ion beams was found to decrease a bit (29.4 to 22.2 nm in Co − implanted samples and 24.2 to 23.3 nm in N + implanted samples) with increasing fluence. The Tauc's plot deduced from UV–visible spectroscopy showed that the band gap decreases from 3.54 to 3.27 eV in Co − implanted films and increases from 3.38 to 3.58 eV for films implanted with N + ions. The experimental results suggest that the modifications in structural and optical properties of indium oxide films can be controlled by optimizing the implantation conditions. Copyright © 2017 John Wiley & Sons, Ltd." @default.
• W2613532425 created "2017-05-19" @default.
• W2613532425 creator A5030814612 @default.
• W2613532425 creator A5041856695 @default.
• W2613532425 creator A5063833455 @default.
• W2613532425 creator A5066576125 @default.
• W2613532425 creator A5067135648 @default.
• W2613532425 date "2017-05-12" @default.
• W2613532425 modified "2023-10-16" @default.
• W2613532425 title "Ion induced controlled modifications in structural and optical properties of indium oxide thin films - studies with 25-keV Co⁻ and N⁺ beam implantations" @default.
• W2613532425 cites W1966251296 @default.
• W2613532425 cites W1972114719 @default.
• W2613532425 cites W1976921975 @default.
• W2613532425 cites W1981109882 @default.
• W2613532425 cites W1982472414 @default.
• W2613532425 cites W1985035816 @default.
• W2613532425 cites W1986667543 @default.
• W2613532425 cites W1994666753 @default.
• W2613532425 cites W1996155830 @default.
• W2613532425 cites W2000370831 @default.
• W2613532425 cites W2000458254 @default.
• W2613532425 cites W2000719036 @default.
• W2613532425 cites W2006018808 @default.
• W2613532425 cites W2008311058 @default.
• W2613532425 cites W2013986483 @default.
• W2613532425 cites W2015842673 @default.
• W2613532425 cites W2016906589 @default.
• W2613532425 cites W2021768562 @default.
• W2613532425 cites W2026063681 @default.
• W2613532425 cites W2026497079 @default.
• W2613532425 cites W2043599508 @default.
• W2613532425 cites W2046377884 @default.
• W2613532425 cites W2060039019 @default.
• W2613532425 cites W2060090703 @default.
• W2613532425 cites W2061341776 @default.
• W2613532425 cites W2062404953 @default.
• W2613532425 cites W2063329433 @default.
• W2613532425 cites W2079735338 @default.
• W2613532425 cites W2095049549 @default.
• W2613532425 cites W2103732964 @default.
• W2613532425 cites W2149622372 @default.
• W2613532425 cites W2158596216 @default.
• W2613532425 cites W2161492159 @default.
• W2613532425 cites W2164075440 @default.
• W2613532425 cites W2279232892 @default.
• W2613532425 cites W2299158163 @default.
• W2613532425 cites W2467611054 @default.
• W2613532425 cites W2569423419 @default.
• W2613532425 cites W3015586612 @default.
• W2613532425 doi "https://doi.org/10.1002/sia.6242" @default.
• W2613532425 hasPublicationYear "2017" @default.
• W2613532425 type Work @default.
• W2613532425 sameAs 2613532425 @default.
• W2613532425 citedByCount "2" @default.
• W2613532425 countsByYear W26135324252017 @default.
• W2613532425 countsByYear W26135324252021 @default.
• W2613532425 crossrefType "journal-article" @default.
• W2613532425 hasAuthorship W2613532425A5030814612 @default.
• W2613532425 hasAuthorship W2613532425A5041856695 @default.
• W2613532425 hasAuthorship W2613532425A5063833455 @default.
• W2613532425 hasAuthorship W2613532425A5066576125 @default.
• W2613532425 hasAuthorship W2613532425A5067135648 @default.
• W2613532425 hasConcept C113196181 @default.
• W2613532425 hasConcept C121332964 @default.
• W2613532425 hasConcept C137637335 @default.
• W2613532425 hasConcept C145148216 @default.
• W2613532425 hasConcept C159985019 @default.
• W2613532425 hasConcept C171250308 @default.
• W2613532425 hasConcept C178790620 @default.
• W2613532425 hasConcept C185592680 @default.
• W2613532425 hasConcept C19067145 @default.
• W2613532425 hasConcept C191897082 @default.
• W2613532425 hasConcept C192562407 @default.
• W2613532425 hasConcept C22078206 @default.
• W2613532425 hasConcept C26771246 @default.
• W2613532425 hasConcept C2780547777 @default.
• W2613532425 hasConcept C32891209 @default.
• W2613532425 hasConcept C41823505 @default.
• W2613532425 hasConcept C43617362 @default.
• W2613532425 hasConcept C49040817 @default.
• W2613532425 hasConcept C50774322 @default.
• W2613532425 hasConcept C543292547 @default.
• W2613532425 hasConcept C62520636 @default.
• W2613532425 hasConceptScore W2613532425C113196181 @default.
• W2613532425 hasConceptScore W2613532425C121332964 @default.
• W2613532425 hasConceptScore W2613532425C137637335 @default.
• W2613532425 hasConceptScore W2613532425C145148216 @default.
• W2613532425 hasConceptScore W2613532425C159985019 @default.
• W2613532425 hasConceptScore W2613532425C171250308 @default.
• W2613532425 hasConceptScore W2613532425C178790620 @default.
• W2613532425 hasConceptScore W2613532425C185592680 @default.
• W2613532425 hasConceptScore W2613532425C19067145 @default.
• W2613532425 hasConceptScore W2613532425C191897082 @default.
• W2613532425 hasConceptScore W2613532425C192562407 @default.
• W2613532425 hasConceptScore W2613532425C22078206 @default.
• W2613532425 hasConceptScore W2613532425C26771246 @default.
• W2613532425 hasConceptScore W2613532425C2780547777 @default.
• W2613532425 hasConceptScore W2613532425C32891209 @default.

• next