• W2618109618 abstract "Interaction of the intermetallic compound CeCo3 with hydrogen (pressure of 25 atm) and ammonia (pressure of 6– 8 atm) is investigated at temperatures of 20–450 oC: the composition of products is established, formation conditions of the hydride and nitride phases are determined. Dependence of a direction of intermetallide reaction with the ammonia, passing in presence of NH4Cl (10 wt. % from quantity of intermetallic compound) as activator, from temperature is shown. Formation of hydride phase CeCo3H4 is established at hydrogenation of the intermetallide CeCo3 with both hydrogen and ammonia at heating to 100 oC. The treatment of an initial alloy with ammonia at temperatures to 250 oC also ends by formation of tetrahydride CeCo3H4. Ammonia use as hydrogenating agent in such conditions leads to dispergation of an initial alloy that it is confirmed by increase in a specific surface area of a product with 5.7 to 18.4 m2/g at hydrogenation temperature of 100 and 250 oC accordingly. At that calculated average size of particles makes ~1 and ~0.3 micron accordingly. The value of a specific surface area of the product received after carrying out of 5 cycles sorption-desorption at use of hydrogen made only 0.3 m2/g, that testifies to clear advantages of ammonia application for dispergation. In the conditions of the further temperature treatment (300–350 oC) ammonia causes amorphization of an alloy. It is established, that at intermetallide heating in ammonia atmosphere in temperature area of 400–450 oC the mixture of products (CeHx, CeN, Ce2Co17Hx, Co) is formed according to data of the X-ray analysis. The availability of intermetallide use as working substance in the metal hydride accumulator of hydrogen working at temperatures up to 150 oC is considered. The hydrogen accumulator based on CeCo3 will have the good operating characteristics: relatively low temperature of hydrogen desorption, acceptable hydrogen capacity, easy to charge and relatively low cost. Исследовано взаимодействие интерметаллического соединения CeCo3 с водородом (давление 25 атм) и аммиаком (давление 6–8 атм) при температурах 20–450 oC: установлен состав продуктов, определены условия образования гидридных и нитридных фаз. Показана зависимость направления реакции интерметаллида с аммиаком, проходящая в присутствии NH4Cl (10 мас. % от количества интерметаллида) как активатора, от температуры. Установлено образование гидридной фазы состава CeCo3H4 при гидрировании интерметаллида CeCo3 как водородом, так и аммиаком при нагревании до 100 oC. Обработка исходного сплава аммиаком при температурах до 250 oC также заканчивается образованием тетрагидрида CeCo3H4. Использование аммиака как гидрирующего агента в таких условиях приводит к диспергированию исходного сплава, что подтверждено увеличением удельной поверхности продукта с 5,7 м2/г до 18,4 м2/г при температуре гидрирования 100 oC и 250 oC соответственно. При этом рассчитанный средний размер частиц составляет ~1 мкм и ~0,3 мкм соответственно. Удельная поверхность продукта, полученного после проведения 5 циклов сорбции – десорбции при использовании водорода составляла только 0,3 м2/г, что свидетельствует о явных преимуществах применения аммиака для диспергирования. В условиях дальнейшей температурной обработки (300–350 oC) аммиак вызывает аморфизацию сплава. Установлено, что при нагревании интерметаллида в атмосфере аммиака в температурной области 400–450 oC по данным рентгенофазового анализа образуется смесь продуктов (CeHx, CeN, Ce2Co17Hx, Co). Рассмотрена перспективность использования интерметаллида как рабочего вещества в металлогидридном аккумуляторе водорода, работающем при температурах до 150 oC. Аккумулятор водорода на основе CeCo3 будет обладать хорошими эксплуатационными характеристиками: относительно низкой температурой десорбции водорода, приемлемой емкостью по водороду, легкостью заряда и сравнительно низкой стоимостью." @default.
• W2618109618 created "2017-06-05" @default.
• W2618109618 creator A5014641330 @default.
• W2618109618 creator A5025063097 @default.
• W2618109618 date "2017-05-17" @default.
• W2618109618 modified "2023-09-23" @default.
• W2618109618 title "ГИДРИРОВАНИЕ ИНТЕРМЕТАЛЛИЧЕСКОГО СОЕДИНЕНИЯ CeCo3 ВОДОРОДОМ И АММИАКОМ // HYDROGENATION OF INTERMETALLIC COMPOUND CeCo3 WITH HYDROGEN AND AMMONIA" @default.
• W2618109618 hasPublicationYear "2017" @default.
• W2618109618 type Work @default.
• W2618109618 sameAs 2618109618 @default.
• W2618109618 citedByCount "0" @default.
• W2618109618 crossrefType "journal-article" @default.
• W2618109618 hasAuthorship W2618109618A5014641330 @default.
• W2618109618 hasAuthorship W2618109618A5025063097 @default.
• W2618109618 hasConcept C147789679 @default.
• W2618109618 hasConcept C150394285 @default.
• W2618109618 hasConcept C162711632 @default.
• W2618109618 hasConcept C178790620 @default.
• W2618109618 hasConcept C179104552 @default.
• W2618109618 hasConcept C181258405 @default.
• W2618109618 hasConcept C185592680 @default.
• W2618109618 hasConcept C191897082 @default.
• W2618109618 hasConcept C192562407 @default.
• W2618109618 hasConcept C27501479 @default.
• W2618109618 hasConcept C2776382133 @default.
• W2618109618 hasConcept C2777961443 @default.
• W2618109618 hasConcept C2780026712 @default.
• W2618109618 hasConcept C512968161 @default.
• W2618109618 hasConcept C68044625 @default.
• W2618109618 hasConceptScore W2618109618C147789679 @default.
• W2618109618 hasConceptScore W2618109618C150394285 @default.
• W2618109618 hasConceptScore W2618109618C162711632 @default.
• W2618109618 hasConceptScore W2618109618C178790620 @default.
• W2618109618 hasConceptScore W2618109618C179104552 @default.
• W2618109618 hasConceptScore W2618109618C181258405 @default.
• W2618109618 hasConceptScore W2618109618C185592680 @default.
• W2618109618 hasConceptScore W2618109618C191897082 @default.
• W2618109618 hasConceptScore W2618109618C192562407 @default.
• W2618109618 hasConceptScore W2618109618C27501479 @default.
• W2618109618 hasConceptScore W2618109618C2776382133 @default.
• W2618109618 hasConceptScore W2618109618C2777961443 @default.
• W2618109618 hasConceptScore W2618109618C2780026712 @default.
• W2618109618 hasConceptScore W2618109618C512968161 @default.
• W2618109618 hasConceptScore W2618109618C68044625 @default.
• W2618109618 hasIssue "2" @default.
• W2618109618 hasLocation W26181096181 @default.
• W2618109618 hasOpenAccess W2618109618 @default.
• W2618109618 hasPrimaryLocation W26181096181 @default.
• W2618109618 hasRelatedWork W1446935022 @default.
• W2618109618 hasRelatedWork W193662614 @default.
• W2618109618 hasRelatedWork W1979948897 @default.
• W2618109618 hasRelatedWork W1997202313 @default.
• W2618109618 hasRelatedWork W1997886484 @default.
• W2618109618 hasRelatedWork W2005055693 @default.
• W2618109618 hasRelatedWork W2029096501 @default.
• W2618109618 hasRelatedWork W2118744602 @default.
• W2618109618 hasRelatedWork W2205251135 @default.
• W2618109618 hasRelatedWork W2212102268 @default.
• W2618109618 hasRelatedWork W2364476215 @default.
• W2618109618 hasRelatedWork W2395513850 @default.
• W2618109618 hasRelatedWork W2477472981 @default.
• W2618109618 hasRelatedWork W2550861515 @default.
• W2618109618 hasRelatedWork W2789575030 @default.
• W2618109618 hasRelatedWork W2947764122 @default.
• W2618109618 hasRelatedWork W827618940 @default.
• W2618109618 hasRelatedWork W2130994345 @default.
• W2618109618 hasRelatedWork W2484130658 @default.
• W2618109618 hasRelatedWork W2811675538 @default.
• W2618109618 isParatext "false" @default.
• W2618109618 isRetracted "false" @default.
• W2618109618 magId "2618109618" @default.
• W2618109618 workType "article" @default.